WO2011048138A1 - A medical implant device - Google Patents
A medical implant device Download PDFInfo
- Publication number
- WO2011048138A1 WO2011048138A1 PCT/EP2010/065786 EP2010065786W WO2011048138A1 WO 2011048138 A1 WO2011048138 A1 WO 2011048138A1 EP 2010065786 W EP2010065786 W EP 2010065786W WO 2011048138 A1 WO2011048138 A1 WO 2011048138A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- particles
- peaks
- substrate
- bonded
- recesses
- Prior art date
Abstract
Description
Claims