WO2006052726A1 - Amphiphilic block copolymer-modified epoxy resins and adhesives made therefrom - Google Patents
Amphiphilic block copolymer-modified epoxy resins and adhesives made therefrom Download PDFInfo
- Publication number
- WO2006052726A1 WO2006052726A1 PCT/US2005/039962 US2005039962W WO2006052726A1 WO 2006052726 A1 WO2006052726 A1 WO 2006052726A1 US 2005039962 W US2005039962 W US 2005039962W WO 2006052726 A1 WO2006052726 A1 WO 2006052726A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- block
- epoxy resin
- block copolymer
- epoxy
- Prior art date
Abstract
Description
Claims