WO2005093513A2 - Positive-working photoimageable bottom antireflective coating - Google Patents
Positive-working photoimageable bottom antireflective coating Download PDFInfo
- Publication number
- WO2005093513A2 WO2005093513A2 PCT/IB2005/000773 IB2005000773W WO2005093513A2 WO 2005093513 A2 WO2005093513 A2 WO 2005093513A2 IB 2005000773 W IB2005000773 W IB 2005000773W WO 2005093513 A2 WO2005093513 A2 WO 2005093513A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- antireflective coating
- photoresist
- acid
- coating
- composition
- Prior art date
Abstract
Description
Claims