WO2005051080A1 - Tube - Google Patents

Tube Download PDF

Info

Publication number
WO2005051080A1
WO2005051080A1 PCT/EP2004/010865 EP2004010865W WO2005051080A1 WO 2005051080 A1 WO2005051080 A1 WO 2005051080A1 EP 2004010865 W EP2004010865 W EP 2004010865W WO 2005051080 A1 WO2005051080 A1 WO 2005051080A1
Authority
WO
WIPO (PCT)
Prior art keywords
tube
pipe according
total mass
pipe
amount
Prior art date
Application number
PCT/EP2004/010865
Other languages
German (de)
French (fr)
Inventor
Andreas Helmreich
Manfred Petsch
Original Assignee
Rehau Ag + Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rehau Ag + Co filed Critical Rehau Ag + Co
Priority to EP04787043A priority Critical patent/EP1677596A1/en
Publication of WO2005051080A1 publication Critical patent/WO2005051080A1/en

Abstract

The invention relates to a tube for conducting liquid and/or gaseous media, comprising at least one wall that surrounds a lumen. Said tube is characterized in that the material of the tube contains at least one oligodynamically active, embedded material at a quantity of 0.01 to 20 percent relative to the total weight. The invention further relates to the use of a tube for conducting liquid and/or gaseous media, comprising at least one wall that surrounds a lumen, said tube being characterized in that the material of the tube contains at least one oligodynamically active, embedded material at a quantity of 0.01 to 20 percent relative to the total weight.

Description

Rohr pipe
Die Erfindung betrifft ein Rohr zum Transport von flüssigen und / oder gasförmigen Medien, mit mindestens einer ein Lumen umgebenden Wand.The invention relates to a tube for transporting liquid and / or gaseous media, with at least one wall surrounding a lumen.
Stand der Technik sind derartige Rohre für den Transport von flüssigen und / oder gasförmigen Medien bekannt.Such tubes for the transport of liquid and / or gaseous media are known in the prior art.
Diese Rohre dienen beispielsweise dem Transport von Trinkwasser aus Trinkwasserreservoiren bis hin zum Endverbraucher, aber auch dem Rücktransport von Abwasser vom Endverbraucher zu Abwasserentsorgungsunternehmungen. Bei diesen Rohren nach dem bekannten Stand der Technik kommt es zu Ablagerungen an der Rohrinnenwand, welche zum einen den Durchflussquerschnitt dieser Rohre reduzieren, zum anderen aber auch die Qualität, insbesondere des zu transportierenden Trinkwassers, negativ beeinflussen. Diese Ablagerungen sind bei Rohren aus metallischen Werkstoffen beispielsweise durch Korrosion entstehender Rost aber auch durch in den wassertransportierten Bestandteilen erfolgt eine Ablagerung von Mikro- Organismen. Diese Mikroorganismen, welche auch bei Rohren aus polymeren Werkstoffen sich ablagern, können bei längerem Transport von Flüssigkeiten noch weiter in das Rohrinnere hinein wachsen und führen somit zu einem reduzierten Durchflussquerschnitt im Rohr aber auch zu einer negativen Auswirkung auf beispielsweise das Trinkwasser. Um den Anforderungen an den Transport von Trinkwasser gerecht zu werden, ist es erforderlich, bei diesen Rohren nach den bekannten Stand der Technik eine Reinigung der inneren Rohroberflächen vorzunehmen, um der Ablagerung und dem Transport derartiger Mikroorganismen Einhalt zu gebieten. Die Reinigung derartiger Rohre ist in den schwer zugänglichen Kanalsystemen zum einen sehr aufwändig und zum anderen bei der Vielzahl der verlegten Rohrsysteme eine kontinuierliche und damit auch kostenaufwändige Maßnahme für die entsprechenden beispielsweise Wasserversorgungsuntemehmen. Durch die Ablagerung von Mikroorganismen bzw. anderen Schadstoffen an der Rohrinnenoberfläche kann es ebenfalls zu einer Schädigung des Materials des Rohres an sich kommen. Die Mikroorganismen bzw. die Schadstoffe lagern sich an der Rohrinnenwand an, welche an sich nicht homogen glatt ist, sondern eine gewisse fertigungsbedingte Rauhigkeit aufweist. In diese rauen Oberflächen gelangen nun beim Einsatz der Rohre nach dem Stand der Technik die Mikroorganismen bzw. die aggressiven Stoffe von beispielsweise Abwassern, welche somit erheblich die Materialeigenschaften des Rohres beeinflussen. Als nachteilig hat sich herausgestellt, dass beispielsweise bei Rohren aus polymeren Werkstoffen Additive ausdiffundieren können, was zu einer Versprödung bzw. Alterung des polymeren Werkstoffes des Roh res führt. Weiterhin nachteilig konnte festgestellt werden, dass sich die Mikroorganismen bzw. die Feststoffe fest an der Rohrinnenwand anlagern und Verkrustungen aufbauen, die teilweise den Durchflussquerschnitt der Rohre nach dem Stand der Technik erheblich reduzieren. Diese Verkrustungen werden außerdem noch durch die Auskristallisation von in beispielweise Abwasser gelösten Stoffen negativ gefördert.These pipes are used, for example, to transport drinking water from drinking water reservoirs to the end user, but also to transport wastewater back from the end user to wastewater disposal companies. With these pipes according to the known prior art, deposits occur on the inner wall of the pipe, which on the one hand reduce the flow cross-section of these pipes and on the other hand also negatively influence the quality, in particular of the drinking water to be transported. In the case of pipes made of metallic materials, these deposits are caused, for example, by corrosion which arises, but also by microorganisms being deposited in the water-transported components. These microorganisms, which are also deposited in pipes made of polymeric materials, can grow even further into the inside of the pipe when liquids are transported for a longer period of time and thus lead to a reduced flow cross-section in the pipe but also to a negative impact on drinking water, for example. In order to meet the requirements for the transport of drinking water, it is necessary to clean the inner pipe surfaces of these pipes according to the known prior art in order to stop the deposition and transport of such microorganisms. The cleaning of such pipes in the difficult-to-access sewer systems is, on the one hand, very complex and, on the other hand, with the large number of pipe systems installed, it is a continuous and therefore also costly measure for the corresponding water supply companies, for example. The deposition of microorganisms or other pollutants on the inner surface of the pipe can also damage the material of the pipe itself. The microorganisms or the pollutants accumulate on the inner wall of the tube, which is not homogeneously smooth in itself, but has a certain roughness due to production. When using the pipes according to the prior art, the microorganisms or the aggressive substances of, for example, waste water now enter these rough surfaces, which thus have a considerable influence on the material properties of the pipe. It has been found to be disadvantageous that additives, for example in pipes made of polymer materials, can diffuse out, which leads to embrittlement or aging of the polymer material of the pipe res. It was also found to be disadvantageous that the microorganisms or the solids adhere firmly to the inner wall of the pipe and build up incrustations, which in some cases significantly reduce the flow cross-section of the pipes according to the prior art. These incrustations are also negatively promoted by the crystallization of substances dissolved in wastewater, for example.
Aus der WO 97 30798 ist ein gattungsgemäßes Rohr bekannt. Dieses Rohr ist aus einem polymeren Werkstoff hergestellt und dient dem Transport von flüssigen und / oder gasförmigen Medien, mit mindestens einer ein Lumen umgebenen Wand. Mit diesem Rohr soll die bekannte Verkrustungsneigung vermindert und die ursprünglichen Materiaieigenschaften weitgehend erhalten bleiben. Dies soll dadurch gelöst werden, dass die innere Oberfläche der Rohrinnenwand mit einer Schutzschicht versehen ist. Diese Schutzschicht wird in einem komplizierten und aufwändigen Verfahren nach der Herstellung des Rohres aufgesprüht.A generic tube is known from WO 97 30798. This tube is made of a polymeric material and is used to transport liquid and / or gaseous media, with at least one wall surrounding a lumen. With this pipe, the known tendency to incrustation is reduced and the original material properties are largely retained. This is to be solved by providing the inner surface of the inner tube wall with a protective layer. This protective layer is sprayed on in a complicated and elaborate process after the pipe has been produced.
Nachteilig bei diesem Rohr und der darin aufgebrachten Beschichtung wird gese en, dass gerade das Aufbringen einer derartigen Schutzschicht sehr zeit- und kostenintensiv ist, wobei nicht sichergestellt ist, dass diese Beschichtung den Beanspruchungen durch die im Trinkwasser bzw. auch in Abwassern enthaltenen Mikroorganismen bzw. Feststoffen dauerhaft standhält. Neben den hohen Kosten derart beschichteter Rohre nach dem Stand der Technik, der schlechten Haftung der Schutzschicht an der Rohrinnenwand spricht somit die mangelnde Langzeitbeständigkeit gegen den Einsatz derartig beschichteter Rohre. Ein weiterer Nachteil wird darin gesehen, dass die in Trinkwasser bzw. in Abwasser enthaltenen Mikroorganismen bzw. Schadstoffe diese Schutzschicht schädigen, so- dass diese sich ablöst und das zu transportierende Trinkwasser bzw. Abwasser zusätzlich einer Schadstoffbelastung unterzieht und andererseits aber trotzdem zu ei- ner Versprödung des Werkstoffes des Rohres an diesen Stellen führt. Somit können die Rohre nach dem bekannten Stand der Technik keinen aktiven Beitrag zur Optimierung der Qualität von beispielsweise von Trinkwasser auf dem Weg vom Versorgungsunternehmen bis hin zum Endverbraucher leisten.A disadvantage of this pipe and the coating applied therein is that the application of such a protective layer is very time-consuming and cost-intensive, but it cannot be ensured that this coating will withstand the stresses caused by the microorganisms or waste water contained in the drinking water or waste water. Resists solids permanently. In addition to the high costs of pipes coated in accordance with the prior art, the poor adhesion of the protective layer to the inner wall of the pipe, the lack of long-term resistance speaks against the use of pipes coated in this way. Another disadvantage is seen in the fact that the microorganisms or pollutants contained in drinking water or in wastewater damage this protective layer, so that it is detached and the drinking water or wastewater to be transported is additionally subjected to a pollutant load and on the other hand to one Embrittlement of the pipe material leads at these points. Thus, the pipes according to the known state of the art cannot make an active contribution to optimizing the quality of, for example, drinking water on the way from the supply company to the end user.
Hier setzt die Erfindung ein, die sich die Aufgabe gestellt hat, die Nachteile des bekannten Standes der Technik zu überwinden, und ein Rohr aufzuzeigen, welches wirtschaftlich und kostengünstig herstellbar ist, welches einer Ablagerung von Schadstoffen bzw. Mikroorganismen an der inneren Oberfläche deutlich verringert bzw. gar nicht erst zulässt und bei dem die Materialeigenschaften über die Nut- zungsdauer an sich erhalten bleiben.This is where the invention comes in, which has set itself the task of overcoming the disadvantages of the known prior art, and of showing a tube which can be produced economically and cost-effectively, which significantly reduces or deposits contaminants or microorganisms on the inner surface . does not even allow and in which the material properties are retained over the period of use.
Erfindungsgemäß wird diese Aufgabe durch die kennzeichnenden Merkmale desAccording to the invention, this object is achieved by the characterizing features of
Anspruches 1 gelöst. Weitere die Erfindung detailliert beschreibende, vorteilhafteClaim 1 solved. Further advantageous description of the invention in detail
Ausgestaltungen sind in den Unteransprüchen ausgeführt.Refinements are set out in the subclaims.
Das erfindungsgemäße Rohr zeichnet sich dadurch aus, dass der Werkstoff desThe tube according to the invention is characterized in that the material of the
Rohres wenigstens ein oligodynamisch wirkendes Material in einer Menge von O,01 bis zu 20 %, bezogen auf die Gesamtmasse, eingelagert enthält.Tube contains at least one oligodynamically acting material in an amount of 0.01 to 20%, based on the total mass.
Das erfindungsgemäße Rohr zeichnet sich weiter dadurch aus, dass der Werkstoff des Rohres über seinen gesamten Querschnitt in räumlich gleichmäßiger Verteilung wenigstens ein oligodynamisch wirkendes Material in einer Menge von 0,01 bis zu 20The tube according to the invention is further characterized in that the material of the tube has at least one oligodynamically active material in an amount of 0.01 to 20 over its entire cross section in spatially uniform distribution
%, bezogen auf die Gesamtmasse, eingelagert enthält.%, based on the total mass, contains.
In einer weiteren vorteilhaften Ausführungsform ist das erfindungsgemäße Ro r so ausgeführt, dass der Werkstoff des Rohres wenigstens ein oligodynamisch wirken- des Material in einer Menge von 0,01 bis zu 20 %, bezogen auf die Gesamtmasse, eingelagert enthält, welches vorzugsweise in dem dem Lumen zugewandten Bereich konzentriert ist. Somit kann auf vorteilhafte Weise erreicht werden, dass die dem zu transportierenden flüssigen und / oder gasförmigen Medien zugewandte innere Oberfläche des Rohres so ausgebildet ist, dass keine chemisch bzΛ/v. biologisch bedingten Verkrustungen bzw. Bewuchse sich anlagern und ausbilden können. Das oligodynamisch wirkende Material des erfindungsgemäßen Rohres ist in einer weiteren Ausführungsform eine bakterizid und / oder mikrobizid bzw. fungizid wirkende Metallkomponente. Das erfindungsgemäße Rohr weist eine bakterizides bzw. bakteriostatische Wirkung gegenüber Pseudomonas aeruginosa, Staphylococcus aureus, Alcaligenes faecalis, Escherichia coli und Enterococcus faecalis auf. Es konnte weiterhin vorteilhaft festgestellt werden, dass das erfindungsgemäße Rohr eine fungizide Wirkung gegenüber Candida aibicans aufweist.In a further advantageous embodiment, the tube according to the invention is designed in such a way that the material of the tube contains at least one oligodynamically acting material in an amount of 0.01 to 20%, based on the total mass, which preferably in that Lumen-facing area is concentrated. It can thus be achieved in an advantageous manner that the inner surface of the tube facing the liquid and / or gaseous media to be transported is designed in such a way that no chemical or v. biological incrustations or growths can accumulate and develop. In another embodiment, the oligodynamically acting material of the tube according to the invention is a bactericidal and / or microbicidal or fungicidal metal component. The tube according to the invention has a bactericidal or bacteriostatic effect on Pseudomonas aeruginosa, Staphylococcus aureus, Alcaligenes faecalis, Escherichia coli and Enterococcus faecalis. It was also found to be advantageous that the tube according to the invention has a fungicidal action against Candida aibicans.
In einem weiteren Ausführungsbeispiel ist das erfindungsgemäße Rohr so ausgebil- det, dass nur eine die Innen- und / oder Außenschl icht bildende Rohrwand wenigstens ein oligodynamisch wirkendes Material enthält. Dieses Ausführungsbeispiel wird im an sich bekannten Verfahren der Coextrusion h&rgestellt, wobei nur die den Mikroorganismen bzw. Schadstoffen zugewandte Seite des erfindungsgemäßen Rohres das oligodynamisch wirkende Material enthält. Somit können vorteilhafterweise die an sich bekannten guten Eigenschaften der Standardrohre erhalten bleiben und diese sind insbesondere durch die erfindungsgemäße Ausführung zum Transport von insbesondere Wasser wie Trinkwasser prädestiniert, ohne das die an sich bekannten Standardeigenschaften erneut überprüft und nachge-wiesen werden müssen. Bei dem erfindungsgemäßen Rohr ist die Metallkomponente einer metallionenabge- bende Substanz, die durch den Kontakt mit der Flü ssigkeit oder dem Gas Metallionen freisetzt, welche aber nur auf die Oberfläche des Rohres wirksam sind. Es konnte überraschend gefunden werden, dass die metallionenabgebende Substanz ein Salz, Oxid, Carbid, eine metallorganische Verbindung ist, die aus Gruppe Silber, Gold, Kupfer, Zink, Blei, Arsen, Cadmium ausgewählt ist. Entgegen der Lehre des Stand der Technik, derartige Rohre mit zusätzlichen aufwändigen Schutzschichten zu versehen, konnte gefunden werden, dass die metallabgebende Substanz aus der Gruppe der Zeolithe ausgewählt ist, wobei diese sowohl natürlich vorkommende als auch industriell herg estellte Zeolithe sind. Das Rohr zeichnet sich außerdem erfindungsgemäß dadurch aus, dass ein Teil der im Zeolith enthaltenen Metalle durch wenigstens eine Art von Ionen austauschbaren Metallen ersetzt ist, die aus der Gruppe Silber, Gold, Kupfer, Zink, Blei, Arsen, Cad- mium ausgewählt sind. Die Metallionen werden vorteilhafterweise durch lonenaus- tauschprozesse ersetzt durch ein- und / oder zweiwertige Ionen der Alkali- oder Erdalkaligruppe. Hier haben sich beispielsweise Wirkstoffe auf Basis von Sodium Alu- mosilicaten ausgezeichnet.In a further exemplary embodiment, the tube according to the invention is designed such that only one tube wall forming the inner and / or outer layer contains at least one oligodynamically active material. This exemplary embodiment is produced in the coextrusion process known per se, only the side of the tube according to the invention facing the microorganisms or pollutants containing the oligodynamically active material. Thus, the good properties of the standard pipes known per se can advantageously be retained and these are predestined, in particular, by the design according to the invention for the transport of water and drinking water in particular, without the standard properties known per se having to be checked again and verified. In the tube according to the invention, the metal component is a metal ion-releasing substance which releases metal ions through contact with the liquid or the gas, but which are only effective on the surface of the tube. It was surprisingly found that the metal ion donating substance is a salt, oxide, carbide, an organometallic compound which is selected from the group consisting of silver, gold, copper, zinc, lead, arsenic and cadmium. Contrary to the teaching of the prior art to provide such pipes with additional complex protective layers, it was found that the metal-donating substance is selected from the group of zeolites, which are both naturally occurring and industrially produced zeolites. The tube is also distinguished according to the invention in that some of the metals contained in the zeolite are replaced by at least one type of ion-exchangeable metal which is selected from the group consisting of silver, gold, copper, zinc, lead, arsenic and cadmium. The metal ions are advantageously replaced by ion exchange processes by mono- and / or divalent ions of the alkali or alkaline earth group. Active ingredients based on sodium aluminum silicates, for example, have distinguished themselves here.
Ein weiterer Vorteil des erfindungsgemäßen Rohres wird dadurch gesehen, dass eine langfristige Sicherstellung des Transportes von flüssigen und / oder gasförmigen Medien sichergestellt ist, da die metallionenabgebende Substanz in einer mittleren Korngröße von etwa 6 μm in den Werkstoff des Rohres eingearbeitet werden kann, da sowohl eine Verteilung über den gesamten Querschnitt in räumlich gleichmäßiger Verteilung als auch eine Verteilung vorzugsweise in dem dem Lumen zuge- wandten Bereich des Rohres realisierbar ist.Another advantage of the tube according to the invention is seen in that a long-term guarantee of the transport of liquid and / or gaseous media is ensured, since the metal ion-releasing substance can be incorporated into the material of the tube in an average grain size of about 6 μm, since both Distribution over the entire cross-section in a spatially uniform distribution, as well as a distribution preferably in the region of the tube facing the lumen, can be achieved.
Es hat sich als vorteilhaft herausgestellt, dass das erfindungsgemäße Rohr thermoplastische Eigenschaften bzw. duroplastische Eigenschaften aufweist. In einer weiteren Ausführungsform ist der Werkstoff des erfindungsgemäßen Rohres wenigstens teilweise vernetzt ausgeführt. Durch den Einsatz der erfindungsgemäßen Rohre können sowohl die Reinigungs-, Wartungs- und Instandsetzungskosten beim Einsatz in Wasserversorgungsnetzen stark reduziert werden, ohne dass der Durchflussquerschnitt bzw. die Qualität beein- flusst wird. Das erfindungsgemäße Rohr kann sowohl kreisförmig, eckig aber auch mehrschichtig ausgeführt sein. Bei der Verwendung eines Werkstoffes des Rohres mit wenigstens ein oligodynamisch wirkenden Material in einer Menge von 0,01 bis zu 20 %, bezogen auf die Gesamtmasse, in einem Rohr zum Transport von flüssigen und / oder gasförmigen Medien, mit mindestens einer ein Lumen umgebenden Wand, kann eine signifikante Verlängerung der Systemstandzeit in den Wasserversorgungsnetzen durch eine gleichbleibende Qualität der zu transportierenden Flüssigkeiten und / oder Gase aber auch einer gleichbleibenden Materialstabilität des Rohres realisiert werden. Weiterhin vorteilhaft wird gesehen, dass auch bei Rohren, welche mit den Nachteilen des bekannten Standes der Technik behaftet sind, eine kostengünstige Sanierung durch die erfindungsgemäßen Rohre realisiert werden können, die zu den gleichen Vorteilen wie ursprünglich montierte erfindungsgemäße Rohre führt.It has proven to be advantageous that the tube according to the invention has thermoplastic properties or thermosetting properties. In a further embodiment, the material of the tube according to the invention is at least partially cross-linked. By using the pipes according to the invention, the cleaning, maintenance and repair costs when used in water supply networks can be greatly reduced without the flow cross-section or the quality being influenced. The tube according to the invention can be circular, angular or multilayered. When using a material of the tube with at least one oligodynamically acting material in an amount of 0.01 to 20%, based on the total mass, in a tube for the transport of liquid and / or gaseous media, with at least one wall surrounding a lumen , a significant extension of the system service life in the water supply networks can be realized by a constant quality of the liquids and / or gases to be transported but also a constant material stability of the pipe. It is also seen with advantage that even in pipes which have the disadvantages of the known prior art, inexpensive refurbishment can be realized by the pipes according to the invention, which leads to the same advantages as originally installed pipes according to the invention.
Es liegt weiterhin im Rahmen der Erfindung, dass der Werkstoff des Rohres in einer Menge von 0,01 bis zu 20 %, bezogen auf die Gesamtmasse, Fungizide wie beispielsweise DCOIT (4,5-Dichlor-2-N-octyl-4-isothiazolin-3-on Dichloroctylisothia_zoli- non), OIT (2-N-octyl-4-isothiazolin-3-on), Bethoxazin (3-Benzo[b]thien -2-yl-5,6- dihydro-1 ,4,2-oxathiazin,4-oxid), Fluorfolpet (2-(Dichlorfluormethylthio)-isoindol- ,3- dion N-Fluordichlormethylthiophthalimid Fluorcaptan Fluorphaltan), OBPA (10, 10'- Oxybispenoxyarsin) beziehungsweise BCM (Methyl-N-(2-benzimidazolyl) -carba mat Benzimidazolylcarbaminsäuremethylester Carbendazim) aufweist. Die erfindungsgemäßen Rohre, welche nach dem an sich bekannten Coextrusions- verfahren hergestellt sind, weisen eine Innenschicht von etwa 0,1 bis 5,0 mm auf, in denen wenigsten ein oligodynamisches wirkendes Material in einer Menge von 0,01 bis zu 20 %, bezogen auf die Gesamtmasse des Rohres, eingelagert ist. Bei den erfindungsgemäßen Rohren hat sich überraschend herausgestellt, dass bei einem Verhältnis von Gesamtwandstärke zur Innenschicht von wenigstens 2 die Ab- Iagerung von Mikroorganismen bzw. Schadstoffen dauerhaft reduziert werden kann, da das oligodynamisch wirkende Material nicht in das beispielsweise zu transportierende Trinkwasser migriert, sondern über die gesamte Produktlebensdauer an der Rohrinnenwand vorgehalten und oberflächenwirksam ist.It is also within the scope of the invention that the material of the tube in an amount of 0.01 to 20%, based on the total mass, of fungicides such as DCOIT (4,5-dichloro-2-N-octyl-4-isothiazoline -3-one dichloroctylisothia_zolinone), OIT (2-N-octyl-4-isothiazolin-3-one), bethoxazine (3-benzo [b] thien -2-yl-5,6-dihydro-1,4. 2-oxathiazine, 4-oxide), fluorofolpet (2- (dichlorofluoromethylthio) isoindole, 3-dione N-fluorodichloromethylthiophthalimide fluorocaptan fluoropaltane), OBPA (10, 10'-oxybispenoxyarsine) or BCM (methyl-N- (2-benzimidazolyl ) -carbamate benzimidazolylcarbamic acid methyl ester carbendazim). The tubes according to the invention, which are produced by the coextrusion method known per se, have an inner layer of approximately 0.1 to 5.0 mm, in which at least an oligodynamic material in an amount of 0.01 to 20%, based on the total mass of the pipe. In the case of the pipes according to the invention, it has surprisingly been found that with a ratio of the total wall thickness to the inner layer of at least 2, the deposition of microorganisms or pollutants can be reduced permanently, since the oligodynamically acting material does not migrate into the drinking water to be transported, for example, but via the entire product life is kept on the inside of the pipe and is effective on the surface.
Beispiel 1 :Example 1 :
Das erfindungsgemäße Rohr besteht aus: 95 bis 98 % Polyethylen 2 bis 5 % Silber-Sodium-Hydrogen-Zirkonium-PhosphatThe tube according to the invention consists of: 95 to 98% polyethylene 2 to 5% silver sodium hydrogen zirconium phosphate
Beispiel 2:Example 2:
Die erfindungsgemäße Rohr bestehend aus: 95 % Polyvinylchlorid VMQ 0,1 bis 5 % Silbersalz X2nO- Na2O- AI2O3- 2SiO2 X= Ag+ 0,5 bis 5 % OBPA (10,10'-Oxybispenoxyarsin) Beispiel 3:The tube according to the invention consists of: 95% polyvinyl chloride VMQ 0.1 to 5% silver salt X 2n O-Na 2 O-Al 2 O 3 - 2SiO 2 X = Ag + 0.5 to 5% OBPA (10,10'-oxybispenoxyarsine ) Example 3:
Das erfindungsgemäße Rohr besteht aus 2 coextrudierten Schichten, mit: 90 % Polyethylen, vernetzt, für die stabile Außenschicht 5 % Polyethylen für die Innenschicht 0, 1 bis 5 % Silbersalz X2nO- Na2O- AI2O3- 2SiO2 X= Ag+ The tube according to the invention consists of 2 coextruded layers, with: 90% polyethylene, crosslinked, for the stable outer layer 5% polyethylene for the inner layer 0.1 to 5% silver salt X 2n O-Na 2 O-AI 2 O 3 - 2SiO 2 X = Ag +

Claims

Patentansprüche claims
1. Rohr zum Transport von flüssigen und oder gasförmigen Medien, mit mindestens einer ein Lumen umgebenden Wand, dadurch gekennzeichnet, dass der Werkstoff des Rohres wenigstens ein oligodynamisch wirkendes Material in einer Menge von 0,01 bis zu 20 %, bezogen auf die Gesamtmasse, eingelagert enthält.1. Pipe for the transport of liquid and or gaseous media, with at least one wall surrounding a lumen, characterized in that the material of the pipe is at least one oligodynamically active material in an amount of 0.01 to 20%, based on the total mass, contains stored.
2. Rohr nach Anspruch 1 , dadurch gekennzeichnet, dass der Werkstoff des Rohres über seinen gesamten Querschnitt in räumlich gleichmäßiger Verteilung wenigstens ein oligodynamisch wirkendes Material in einer Menge von 0,01 bis zu 20 %, bezogen auf die Gesamtmasse, eingelagert enthält.2. Pipe according to claim 1, characterized in that the material of the tube contains at least one oligodynamically acting material in an amount of 0.01 to 20%, based on the total mass, in a spatially uniform distribution over its entire cross section.
3. Rohr nach Anspruch 1 , dadurch gekennzeichnet, dass der Werkstoff des Rohres wenigstens ein oligodynamisch wirkendes Material in einer Menge von 0,01 bis zu 20 %, bezogen auf die Gesamtmasse, eingelagert enthält, welches vorzugsweise in dem dem Lumen zugewandten Bereich konzentriert ist.3. Pipe according to claim 1, characterized in that the material of the tube contains at least one oligodynamically acting material in an amount of 0.01 to 20%, based on the total mass, which is preferably concentrated in the region facing the lumen ,
4. Rohr nach Anspruch 1 , dadurch gekennzeichnet, dass der Werkstoff des Rohres wenigstens ein oligodynamisch wirkendes Material in einer Menge von 0,01 bis zu 20 %, bezogen auf die Gesamtmasse, eingelagert enthält, welches vorzugsweise in dem vom Lumen abgewandten Bereich konzentriert ist.4. Pipe according to claim 1, characterized in that the material of the tube contains at least one oligodynamically acting material in an amount of 0.01 to 20%, based on the total mass, which is preferably concentrated in the area facing away from the lumen ,
5. Rohr nach Anspruch 1 bis 4, dadurch gekennzeichnet, dass das oligodynamisch wirkende Material eine bakterizide und / oder bakteriostatische und / oder micro- bizide Metallkomponente ist. 5. Pipe according to claim 1 to 4, characterized in that the oligodynamically acting material is a bactericidal and / or bacteriostatic and / or microbicidal metal component.
6. Rohr nach Anspruch 1 bis 5, dadurch gekennzeichnet, dass das oligodynamisch wirkende Material eine Wirkung gegenüber Pseudomonas aeruginosa, Staphy- lococcus aureus, Alcaligenes faecalis, Escherich ia coli und Enterococcus faecalis aufweist.6. Pipe according to claim 1 to 5, characterized in that the oligodynamically acting material has an action against Pseudomonas aeruginosa, Staphylococcus aureus, Alcaligenes faecalis, Escherich ia coli and Enterococcus faecalis.
7. Rohr nach Anspruch 1 bis 6, dadurch gekennzeichnet, dass die Metallkomponente eine Metallionen abgebende Substanz ist.7. Pipe according to claim 1 to 6, characterized in that the metal component is a substance which emits metal ions.
8. Rohr nach Anspruch 1 bis 7, dadurch gekennzeichnet, dass die Metallkompo- nente durch den Kontakt mit der Flüssigkeit oder dem Gas die Metallionen freisetzt.8. Pipe according to claim 1 to 7, characterized in that the metal component releases the metal ions through contact with the liquid or the gas.
9. Rohr nach Anspruch 1 bis 8, dadurch gekennzeichnet, dass die Metallionen abgebende Substanz ein Salz, Oxid, Carbid, eine metallorganische Verbindung ist, die aus der Gruppe Silber, Gold, Kupfer, Zink ausgewählt ist.9. Pipe according to claim 1 to 8, characterized in that the metal ion donating substance is a salt, oxide, carbide, an organometallic compound which is selected from the group silver, gold, copper, zinc.
10. Rohr nach Anspruch 1 bis 9, dadurch gekennzeichnet, dass die Metallionen abgebende Substanz aus der Gruppe der Zeolithe ausgewählt ist.10. Pipe according to claim 1 to 9, characterized in that the metal ion-releasing substance is selected from the group of zeolites.
11. Rohr nach Anspruch 1 bis 10, dadurch gekennzeichnet, dass ein Teil der im Ze- olith enthaltenen Metalle durch wenigstens eine Art von Ionen austauschbaren Metallen ersetzt ist, die aus der Gruppe Silber, Gold, Kupfer, Zink ausgewählt sind.11. Pipe according to claim 1 to 10, characterized in that a part of the metals contained in the zeolite is replaced by at least one type of ion-exchangeable metals, which are selected from the group silver, gold, copper, zinc.
12. Rohr nach Anspruch 1 bis 11 , dadurch gekennzeichnet, dass die Metallionen abgebende Substanz eine mittlere Korngröße von etwa 6 μm aufweist.12. Pipe according to claim 1 to 11, characterized in that the metal ion-releasing substance has an average grain size of about 6 microns.
13. Rohr nach Anspruch 1 bis 12, dadurch gekennzeichnet, dass der Werkstoff des Rohres thermoplastische Eigenschaften aufweist.13. Pipe according to claim 1 to 12, characterized in that the material of the tube has thermoplastic properties.
14. Rohr nach Anspruch 1 bis 13, dadurch gekennzeichnet, dass der Werkstoff des Rohres duroplastische Eigenschaften aufweist.14. Pipe according to claim 1 to 13, characterized in that the material of the tube has thermosetting properties.
15. Rohr nach Anspruch 1 bis 14, dadurch gekennzeichnet, dass der Werkstoff des Rohres wenigstens teilweise vernetzt ist. 15. Pipe according to claim 1 to 14, characterized in that the material of the tube is at least partially cross-linked.
16. Rohr nach Anspruch 1 bis 15, dadurch gekennzeichnet, dass das Rohr kreisförmig ausgeführt ist.16. Pipe according to claim 1 to 15, characterized in that the tube is circular.
17. Rohr nach Anspruch 1 bis 16, dadurch gekennzeichnet, dass das Rohr mehr- eckig ausgeführt ist.17. Pipe according to claim 1 to 16, characterized in that the tube is polygonal.
18. Rohr nach Anspruch 1 bis 17, dadurch gekennzeichnet, dass das Rohr mehrschichtig ausgeführt ist.18. Pipe according to claim 1 to 17, characterized in that the tube is multi-layered.
19. Verwendung eines Rohres zum Transport von flüssigen und oder gasförmigen Medien, mit mindestens einer ein Lumen umgebenden Wand, dadurch gekennzeichnet, dass der Werkstoff des Rohres wenigstens ein oligodynamisch wirkendes Material in einer Menge von 0,01 - 20 %, bezogen auf die Gesamtmasse, eingelagert enthält.19. Use of a tube for the transport of liquid and or gaseous media, with at least one wall surrounding a lumen, characterized in that the material of the tube is at least one oligodynamically active material in an amount of 0.01-20%, based on the total mass , stored contains.
20. Verwendung eines Rohres nach Anspruch 18, dadurch gekennzeichnet, dass der Werkstoff des Rohres über seinen gesamten Querschnitt in räumlich gleichmäßiger Verteilung wenigstens ein oligodynamisch wirkendes Material in einer Menge von 0,01 - 20 %, bezogen auf die Gesamtmasse, eingelagert ent- hält.20. Use of a pipe according to claim 18, characterized in that the material of the pipe contains at least one oligodynamically acting material in an amount of 0.01-20%, based on the total mass, in a spatially uniform distribution over its entire cross-section ,
21. Verwendung eines Rohres nach Anspruch 18, dadurch gekennzeichnet, dass der Werkstoff des Rohres wenigstens ein oligodynamisch wirkendes Materia! in einer Menge von 0,01 - 20 %, bezogen auf die Gesamtmasse, eingelagert ent- hält, welches vorzugsweise in dem dem Lumen zugewandten Bereich konzentriert ist.21. Use of a tube according to claim 18, characterized in that the material of the tube has at least one oligodynamically acting material! contained in an amount of 0.01-20%, based on the total mass, which is preferably concentrated in the area facing the lumen.
22. Verwendung eines Rohres nach Anspruch 19, dadurch gekennzeichnet, dass der Werkstoff des Rohres wenigstens ein oligodynamisch wirkendes Material in einer Menge von 0,01 - 20 %, bezogen auf die Gesamtmasse, eingelagert enthält, welches vorzugsweise in dem vom Lumen abgewandten Bereich konzentriert ist.22. Use of a tube according to claim 19, characterized in that the material of the tube contains at least one oligodynamically acting material in an amount of 0.01-20%, based on the total mass, which is preferably concentrated in the area facing away from the lumen is.
Rehau, den 28.10.2003 dr.schi-zrk Rehau, October 28, 2003 dr.schi-zrk
PCT/EP2004/010865 2003-10-30 2004-09-29 Tube WO2005051080A1 (en)