WO2002060636A1 - Ultraviolet laser ablative patterning of microstructures in semiconductors - Google Patents
Ultraviolet laser ablative patterning of microstructures in semiconductors Download PDFInfo
- Publication number
- WO2002060636A1 WO2002060636A1 PCT/US2002/000867 US0200867W WO02060636A1 WO 2002060636 A1 WO2002060636 A1 WO 2002060636A1 US 0200867 W US0200867 W US 0200867W WO 02060636 A1 WO02060636 A1 WO 02060636A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- laser
- laser system
- substrate
- chuck
- silicon
- Prior art date
Abstract
Description
Claims