WO1995024054A1 - Improved compositions and methods for polishing - Google Patents
Improved compositions and methods for polishing Download PDFInfo
- Publication number
- WO1995024054A1 WO1995024054A1 PCT/US1995/002793 US9502793W WO9524054A1 WO 1995024054 A1 WO1995024054 A1 WO 1995024054A1 US 9502793 W US9502793 W US 9502793W WO 9524054 A1 WO9524054 A1 WO 9524054A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polishing
- metal
- composition according
- polishing composition
- iodate
- Prior art date
Abstract
A composition is provided for polishing dielectric/metal composites, semiconductors and integrated circuits which contains an iodate compound. The iodate oxidizer may be used along with a compound or compounds which suppress the removal of the dielectric silica in the composite to provide an excellent selectivity of metal versus silica removal.
Description
IMPROVED COMPOSITIONS AND METHODS FOR POLISHING
BACKGROUND OF THE INVENTION
Field of the Invention
The invention relates to the polishing of metals, dielectric/metal composites, semiconductors and integrated circuits. More particularly, this invention relates to improvements in the surface preparation of composite materials where improved polishing rates of metallic components is desired.
Description of the Related Art Conventional polishing compositions or slurries generally consist of a solution which contains abrasive particles. The part, or substrate, is bathed or rinsed in the slurry while an elastomeric pad is pressed against the substrate and the pad and substrate are moved relative to each other. Thus the abrasive particles are pressed against the substrate under load and the lateral motion of the pad causes the abrasive particles to move across the substrate surface, resulting in wear, volumetric removal of the substrate surface.
In many cases the rate of surface removal is determined solely by the degree of applied pressure, the velocity of pad rotation and the chemical activity of the slurry particle. Enhancement of the chemical activity of the
polishing particle has been the basis of numerous patents, for example U.S.Patent No. 4959113 and U.S.Patent No. 5382272 both assigned to Rodel, Inc., Newark, Delaware.
An alternative means of increasing polishing rates is to add components to the slurries which by themselves are corrosive to the substrate. When used together with abrasive particles, substantially higher polishing rates may be achieved. This process, often termed chemical-mechanical polishing (CMP) is a preferred technique for polishing of semiconductors and semiconductor devices, particularly integrated circuits. Often they teach the introduction of additives which accelerate dissolution of the metal component in the polishing of dielectric/metal composite structures such as interconnect vias in integrated circuit structures. The purpose of this and other related techniques is to preferentially remove the metal portion of the circuit so that the resulting surface becomes coplanar. This process is ordinarily termed planarization.
It is highly desirable to improve the selectivity of metal planarization as much as possible. Carr et al. (U.S.Patent No. 4,954,142) teach improvements in CMP planarization of dielectric/metal composite structures by addition of a chelating agent to the slurry which is selective for the metal component of interest. This results in a further increase of the corrosion rate of the metal phase and increased selectivity of metal
versus dielectric phase removal, making the planarization process much more efficient.
Several other patents show chemical-mechanical polishing of a metal or metal containing layers on semiconductor substrates using slurries which contain oxidizing agents along with other solubilizing chemicals. These are U.S.Patent No. 4,956,313, U.S.Patent No. 4,992,135 and U.S.Patent No. 5,209,816. In all of these hydrogen peroxide is the oxidizing agent described as being useful for converting the metal to an oxide which is then subject to the chemical and mechanical action of the polishing slurry.
Hydrogen peroxide is again mentioned as a metal oxidizer in polishing slurries which also contain a compound or compounds that limit the rate of removal of silica and silicates from the surface being planarized. This is disclosed in U.S.Patent No. 5391258 assigned to Rodel, Inc., Newark, Delaware which is made- part of this specification by reference.
There are disadvantages to using hydrogen peroxide, thus, alternative oxidizers are actively being sought. Hydrogen peroxide decomposes with time resulting in a slurry whose activity is decreasing. Chlorine containing compounds are also not satisfactory because they are corrosive to the materials in the semiconductor surface. Any chlorine containing compounds must be carefully removed from the surface of the semiconductor wafer before further use. It is therefore an object of this invention to provide an
oxidizer for metals and metal containing compounds which will perform satisfactorily in polishing slurries for planarization.
SUMMARY OF THE INVENTION
The object of this invention has been achieved by providing a composition for polishing dielectric/metal composites, semiconductors and integrated circuits which contains an iodate compound. The iodate oxidizer may be used along with a compound or compounds which suppress the removal of the dielectric silica in the composite to provide an excellent selectivity of metal versus silica removal.
DESCRIPTION OF THE INVENTION
We have unexpectedly found that iodates such as potassium iodate and sodium iodate perform well as oxidizing agents in polishing slurries without showing the disadvantages of oxidizing agents previously known in the polishing art. We have particularly found that an aqueous slurry composed of abrasive particles, an iodate oxidizing agent and a compound which contains at least two acid groups and, where the pKa of the first dissociable acid is not substantially larger than the pH of the polishing slurry, performs well in the planarization of metal/dielectric composites such as integrated circuits.
One would expect that the oxidation of a metal surface and its subsequent removal rate when polished using a slurry containing a given oxidant would be dependent on the reduction potential of the oxidant. Table 1 shows
the assumed half-cell reduction reactions and the standard reduction potentials (E°) of some oxidants which have been used in compositions for tungsten polishing.
Table 1.
Reaction E°,Volts
NO3" + 3H+ + 2e~ <====> HNO2 + H20 0.934
103" + 6H+ + 6e~ <====> I- + 3H20 ' 1.085 CIO4- + 2H+ + 2e~ <====> C103 ~ + H20 1.189
H2θ2 + 2H+ + 2e~ <====> 2H20 1.776
S208 2_ + 2H+ + 2e_ <====> 2HSO4- 2.123
EXAMPLE 1 Polishing compositions were prepared using a submicron alumina suspension to which were added water and reagent grade chemicals to make up formulations as shown in Table 2 below. Hydrochloric acid was added to each formulation to adjust the pH. These formulations were used to polish samples of sputter-coated tungsten metal film on Si substrates using identical conditions on a Strasbough 6DS planarizer.
Polishing conditions were: Polishing pad: Rodel IC1000
Pressure: 9psi
Platen Speed: 50rpm
Carrier Speed: 40rpm
Slurry Flow Rate: 200ml/min Platen Temperature: Ambient
The removal rate of tungsten was determined by weight loss of the tungsten sheet wafer.
Table 2. Formulation pH Tungsten Removal
Rate Angstroms/min 7%solids,2%Al(C104)3 3.4 141
7%solids,l%K2 (S208) 4.1 218
7%solids,2%KI03 3.4 ' 576
It is obvious from the data in Tables 1 and 2 that the removal rate of tungsten is not related to the reduction potentials of the oxidants used in the formulations and that it is indeed surprising that an iodate compound performs exceptionally well in formulations used for the polishing of tungsten.
EXAMPLE 2
A polishing composition was prepared as in Example 1 using a submicron alumina suspension. Added to the suspension were water, reagent grade potassium iodate and reagent grade potassium hydrogen phthalate to make a composition containing 7% solids, 3.2% potassium iodate and 4.4% potassium hydrogen phthalate. The pH of the polishing slurry in use is 4.1. This composition was used to polish samples of sputter- coated tungsten metal film on Si substrates and samples of thermally grown Si02 on Si substrates using identical conditions on a Strasbough 6DS planarizer. Polishing conditions were the same as those shown in Example 1.
The removal rate of tungsten was determined by weight loss of the tungsten sheet wafer. Removal rate for the oxide sheet wafers was determined using a Prometrix SM200/e film thickness measuring tool. The polishing rate of the tungsten metal was 1829 Angstroms/min while the polishing rate of Si02 was 84 Angstroms/min giving a selectivity of 22. This result compares very favorably with results obtained using fresh 50% hydrogen peroxide as the oxidizing agent in the slurry.
The preceding Examples show the efficacy of using slurries containing the formulations as shown and are not meant in any way to restrict the breadth of the invention as defined in the claims recited below.
Claims
1. A polishing composition for substrates containing a metal and silicon dioxide comprising: an aqueous medium, abrasive particles ,an iodate compound and one or more compounds which suppress the rate of removal of said silicon dioxide wherein each of said compounds or compounds contains at least two acid groups and where the pKa of the first dissociable acid is not substantially larger than the pH of the polishing composition.
2. A polishing composition according to claim 1 in which said compound containing at least two acid groups is potassium hydrogen phthalate.
3. A polishing composition according to claim 1 in which said iodate is potassium iodate.
4. A polishing composition according to claim 1 in which said iodate compound is sodium iodate.
5. A polishing composition according to claim 3 in which said compound containing at least two acid groups is potassium hydrogen phthalate.
6. A polishing composition according to claim 4 in which said compound containing at least two acid groups is potassium hydrogen phthalate.
7. A method for polishing a substrate comprised of a metal and silicon dioxide in which a polishing composition according to claim 1 is used as the polishing slurry.
8. A method for polishing a substrate comprised of a metal and silicon dioxide in which a polishing composition according to claim 2 is used as the polishing slurry.
9. A method for polishing a substrate comprised of a metal and silicon dioxide in which a polishing composition according to claim 3 is used as the polishing slurry.
10. A method for polishing a substrate comprised of a metal and silicon dioxide in which a polishing composition according to claim 4 is used as the polishing slurry.
11. A method for polishing a substrate comprised of a metal and silicon dioxide in which a polishing composition according to claim 5 is used as the polishing slurry.
12. A method for polishing a substrate comprised of a metal and silicon dioxide in which a polishing composition according to claim 6 is used as the polishing slurry.