US20090230409A1 - Underfill process for flip-chip leds - Google Patents
Underfill process for flip-chip leds Download PDFInfo
- Publication number
- US20090230409A1 US20090230409A1 US12/050,082 US5008208A US2009230409A1 US 20090230409 A1 US20090230409 A1 US 20090230409A1 US 5008208 A US5008208 A US 5008208A US 2009230409 A1 US2009230409 A1 US 2009230409A1
- Authority
- US
- United States
- Prior art keywords
- underfill material
- led
- led die
- submount
- underfill
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This invention relates to flip-chip light emitting diodes (LEDs) and, in particular, to a process for supplying a dielectric underfill material in the gap between the LED chip and its submount.
- Prior art
FIG. 1 illustrates aconventional LED 10 flip chip mounted on a portion of asubmount wafer 22. In a flip-chip, both the n and p contacts are formed on the same side of the LED die opposite to thegrowth substrate 12 side. - In
FIG. 1 , theLED 10 is formed of semiconductor epitaxial layers, including an n-layer, an active layer, and a p-layer, grown on agrowth substrate 12, such as a sapphire substrate. In one example, the epitaxial layers are GaN based, and the active layer emits blue light. Any other type of flip chip LED is applicable to the present invention. -
Metal electrodes 14 are formed on theLED 10 that electrically contact the p-layer, andmetal electrodes 16 are formed on theLED 10 that electrically contact the n-layer. In one example, the electrodes are gold bumps that are ultrasonically welded to anode andcathode metal pads submount wafer 22. Thesubmount wafer 22 hasconductive vias 24 leading tobottom metal pads submount wafer 22 and will be later singulated to form individual LEDs/submounts. - Further details of LEDs can be found in the assignee's U.S. Pat. Nos. 6,649,440 and 6,274,399, and U.S. Patent Publications US 2006/0281203 A1 and 2005/0269582 A1, all incorporated herein by reference.
- An
underfill material 30 is then injected under and around theLED 10 to fill in air gaps between theLED 10 andsubmount wafer 22. Theunderfill material 30 is typically liquid epoxy that is then cured to harden. The hardened underfill provides structural support and protects the chip from contaminants. Theunderfill material 30 is injected by anozzle 32 that is moved around theLED 10 while injecting theunderfill material 30 at a relatively high pressure to fill the narrow gap between theLED 10 andsubmount wafer 22. The underfill may extend further laterally than shown in the figures in actual devices. - Any excess underfill material 30 (e.g., epoxy) on top of and around the
LED 10/substrate 12 may be removed by microbead blasting. - After the
underfill material 30 is cured and microbead blasted, thegrowth substrate 12 is then removed using a laser lift-off process (not shown). The photon energy of the laser (e.g., an excimer laser) is selected to be above the band gap of the LED material and below the absorption edge of the sapphire substrate (e.g., between 3.44 eV and 6 eV). Pulses from the laser through the sapphire are converted to thermal energy within the first 100 nm of the LED material. The generated temperature is in excess of 1000° C. and dissociates the gallium and nitrogen. The resulting high gas pressure pushes the substrate away from the epitaxial layers to release the substrate from the layers, and the loose substrate is then simply removed from the LED structure. The underfill helps prevent the thin LED layers from cracking under the high pressure. - The
growth substrate 12 may instead be removed by etching, such as reactive ion etching (RIE), or grinding. Other techniques may be used depending on the type of LED and substrate. In one example, the substrate is Si-based and an insulating material between the substrate and the LED layers is etched away by a wet etch technique to remove the substrate. - After any other wafer-level processes, the
submount wafer 22 is then sawed or scribed and broken to singulate the LEDs/submounts. The submounts may then be soldered to a printed circuit board. - Problems with the prior art underfill technique include the following.
- Providing a precise amount of underfill material to only fill under and around the thin LED layers is difficult and time-consuming. The underfill process is sequentially performed on an array of LEDs mounted on a submount wafer, prior to the LEDs being singulated. There may be 500-4000 LEDs mounted on a single submount wafer, depending on the size of each LED and the density. Injecting the underfill material under each LED in the array using a single moving nozzle may take 10-40 minutes, depending on the number of LEDs.
- Another problem is that the properties of the underfill material must be carefully selected for proper viscosity, thermal expansion, reliability over the long lifetime of the LED, dielectric properties, thermal conductivity, contaminant protection, and other factors. If the viscosity is too high, the pressure needed to inject the underfill under the LED to fill all voids may damage the LED. Voids must be eliminated since any air will expand when the LED/submount becomes hot and push the LED off the submount. Further, since a void area does not support the LED during the laser lift-off process, the downward stress on the LED during the laser lift-off process may crack the LED.
- Thermal expansion of the underfill is extremely important since the LEDs undergo a solder reflow process when soldering a singulated LED/submount to a printed circuit board. Such temperatures may be 265° C. The solder reflow temperature is above the typical 185° C. glass transition temperature for epoxy, which is the typical underfill material. As it relates to an epoxy, the glass transition temperature (Tg) is the temperature at which epoxy becomes soft. Above the glass transition temperature, the epoxy thermal expansion rises significantly, causing upward pressure on the LED, resulting in cracking or lifting off of the LED.
- What is needed is an improved technique for underfilling an LED that avoids the above-mentioned problems and material limitations.
- An underfill technique for LEDs is described where compression molding is used. The process is performed prior to any substrate lift-off process. The LEDs, mounted on a submount wafer, are placed in a mold. The mold is sealed at least around the perimeter of the submount wafer, and a vacuum is created within the mold. The mold may be aluminum with separate cavities aligned with each LED on the submount wafer. In one embodiment, there are flow channels interconnecting each cavity to a vacuum source and to at least one liquid material inlet.
- Any suitable underfill material, such as a liquid polyimide, is then applied to the inlet of the mold under pressure, and the combination of the vacuum and the liquid material pressure causes the material to completely fill the cavities in the mold where the LEDs are located. There are no voids once the material has filled the mold.
- The dimensions of each mold cavity cause the liquid material to completely encapsulate each LED, along with its growth substrate.
- The liquid material is then cured by heat or UV light to harden the underfill material, and the mold is released from the submount wafer. A higher temperature post cure may be performed after the mold is released.
- In another embodiment, the liquid underfill material may first fill the mold, having a peripheral raised seal, and then the submount wafer is placed over the mold so that the LEDs are immersed in the underfill material. Under compression, the liquid material fills all voids under each LED. Air is pushed out through the seals along with a certain amount of the underfill material. The material is then cured, and the mold released from the submount wafer. Since such a molding process does not rely on the injection of the liquid material under pressure at an inlet of the mold, there is little possibility of damage to the fragile LEDs.
- In another embodiment, the underfill material used to fill the mold is not a liquid but is a powder or small tablets. The solid material is then heated in the mold to melt or soften it so that it can conform to the mold and encapsulate the LEDs. Compression is used to mold the softened material and cause it to flow into the voids under each LED. Handling the underfill material as a solid has various benefits. Such compression molding using an initially solid underfill material greatly increases the number of possible underfill materials. One of the materials which can be used for this process is the powder of an epoxy molding compound.
- After the submount wafer is removed from the mold, the entire submount wafer is subjected to a microbead blasting process to etch away the underfill material until all of the growth substrate is exposed. The substrate is then removed using a laser lift-off process, or other suitable process. The underfill supports the thin LED during this process.
- After the growth substrate has been removed, the LED may be thinned to improve light extraction. The surface of the LED may then be roughened to further improve light extraction by reducing the number of internal reflections.
- Lenses may then be molded over the LEDs and/or other wafer-level processing techniques may be performed.
- The LEDs/submounts are then singulated using sawing, scribe and break, or any other technique.
- By using the above method, a much wider variety of materials may be used for the underfill since a much wider range of viscosities are tolerable. When using the prior art jet nozzle, the material could only have a narrow range of viscosities. A preferred underfill material that can be used with the present process is a polyimide, which has a glass transition temperature near or above the solder reflow temperature, so that there is very little thermal expansion of the polyimide under worst case conditions.
- Further, since all the LEDs on the submount wafer (e.g., 500-4000 LEDs) are underfilled at the same time, the underfill processing time can be reduced to only a few minutes.
-
FIG. 1 is a cross-sectional view of a prior art flip-chip LED, mounted on a submount, where the LED underfill material is dispensed under pressure by a small nozzle at the base of the LED. -
FIG. 2 illustrates a simplified portion of a submount wafer populated by an array of LEDs, such as 500-4000 LEDs. -
FIG. 3A illustrates a wafer-level injection molding process used to encapsulate all LEDs on the submount wafer with an underfill material. -
FIG. 3B illustrates an alternative type of wafer-level molding process, not using injection, used to encapsulate all LEDs on the submount wafer with an underfill material. -
FIG. 4 illustrates the LEDs on the wafer after being removed from the mold ofFIG. 3A orFIG. 3B . -
FIG. 5 illustrates the upper portion of the underfill material ofFIG. 4 being removed by microbead blasting. -
FIG. 6 illustrates a laser lift-off technique for removing the growth substrates from the LEDs. -
FIG. 7 is a cross-sectional view of a single LED mounted on a submount after the LED has been thinned and after the LEDs/submounts have been singulated. The submount is shown soldered to a printed circuit board. - Elements that are the same or equivalent are labeled with the same numeral.
- As a preliminary matter, a conventional LED is formed on a growth substrate. In the example used, the LED is a GaN-based LED, such as an AlInGaN or InGaN LED, for producing blue light. Typically, a relatively thick n-type GaN layer is grown on a sapphire growth substrate using conventional techniques. The relatively thick GaN layer typically includes a low temperature nucleation layer and one or more additional layers so as to provide a low-defect lattice structure for the n-type cladding layer and active layer. One or more n-type cladding layers are then formed over the thick n-type layer, followed by an active layer, one or more p-type cladding layers, and a p-type contact layer (for metallization).
- For a flip-chip, portions of the p-layers and active layer are etched away to expose an n-layer for metallization. In this way, the p contact and n contact are on the same side of the chip and can be directly electrically attached to the submount contact pads. Current from the n-metal contact initially flows laterally through the n-layer.
- Other types of LEDs that can be used in the present invention include AlInGaP LEDs, which can produce light in the red to yellow range.
- The flip-chip LED used as an example in the present invention is the LED structure of
FIG. 1 comprising asemiconductor LED 10, itsgrowth substrate 12, and itselectrodes 14/16, where the LED is mounted on asubmount wafer 22. -
FIG. 2 is a simplified illustration of asubmount wafer 22 on which is mounted an array of LEDs. There may be 500-4000 LEDs on asingle submount wafer 22. An LED is also referred to herein as an LED die. - Instead of positioning a nozzle at the based of each LED for injecting an underfill material under each LED in the array, a wafer-level molding process is performed.
-
FIG. 3A illustrates one type of suitable injection molding process for creating the underfill for each LED. Amold 36 hascavities 38 that define the shape of the hardened underfill material after the molding process. Themold 36 may be formed of aluminum. Themold 36 has aperimeter seal 37 that seals against thesubmount wafer 22 when themold 36 is aligned with thewafer 22 and pressed against thewafer 22. - The
mold 36 has at least oneinlet 40, for injecting the liquid underfill material 41 (e.g., a polyimide), and at least oneoutlet 42 connected to a vacuum source. Once themold 36 is sealed against thewafer 22, a vacuum is created within themold 36, and theunderfill material 41 is injected throughinlet 40. Theunderfill material 41 flows into all thecavities 38 viachannels 44 between the cavities, assisted by the vacuum and the injection pressure of thematerial 41. The vacuum removes almost all the air in themold 36. Ultimately, theentire mold 36 will be filled with theunderfill material 41, including all voids under the LEDs. - The
mold 36 is then heated to cure the liquid underfill material. The temperature of themold 36 during curing is about 150° C. Alternatively, a transparent mold may be used and the underfill material may be cured with UV light. -
FIG. 3B illustrates an alternative wafer-level molding process that does not use pressure injection of the underfill material. InFIG. 3B , themold 48 hascavities 50 that are first filled with theliquid underfill material 41 at atmospheric pressure. Thesubmount wafer 22 is brought against themold 48 so that the LEDs are immersed in the underfill material in eachcavity 50. Thewafer 22 andmold 48 are pressed together to force the underfill material to fill all voids. Aperimeter seal 53 allows the pressure to be high while allowing all air to escape as the underfill material fills the voids. A vacuum may also be pulled between thewafer 22 and themold 48 using a vacuum source around theseal 53. - The
mold 48 is then heated to cure the liquid underfill material. Alternatively, a transparent mold may be used and the underfill material may be cured with UV light. - The mold of
FIG. 3A or 3B is then removed from thewafer 22, resulting in the structure ofFIG. 4 , having excess hardenedunderfill material 54 encapsulating each LED. There may also be a thin layer of hardened underfill material on thewafer 22 surface between each LED depending on the mold. - The
wafer 22 may then be subject to a post-cure temperature of about 250° C. to additionally harden the underfill material. For an epoxy molding compound or a polyimide underfill, its glass transition temperature (Tg) is between 260-300° C., so a post cure temperature less than the Tg is preferred to limit any thermal expansion of the underfill. - In another embodiment, the underfill material used to fill the mold is not a liquid but is a powder or small tablets. The solid material is then heated in the mold of
FIG. 3A orFIG. 3B to melt or soften it. Compression is used to cause the softened material to take the form of the mold and to fill the voids under the LEDs while encapsulating the LEDs. The melted or softened material is then cured or cooled, if necessary, to make it solid again. Certain materials hardened automatically after the heating and compression process. Handling the underfill material as a solid has various benefits. Further, some suitable materials that can be used for an underfill are not a liquid at room temperatures prior to curing, so heating up a solid material in the mold followed by compression greatly increases the number of possible materials that can be used as an underfill. One suitable solid polymer that can be used is an epoxy molding compound in powder form. - To perform a laser lift-off process to remove the
growth substrates 12, theunderfill material 54 over thegrowth substrate 12 must be first removed. If thegrowth substrate 12 will be removed by grinding or another mechanical etch process, such grinding may be used to simultaneously remove theexcess underfill material 54. -
FIG. 5 illustrates the removal of theexcess underfill material 54 by blasting the entire surface of thewafer 22 with high-velocity microbeads 58. In one embodiment, themicrobeads 58 have diameters between 1-20 microns and are formed of NaHCO3. Themicrobeads 58 are accelerated through a nozzle by air at a pressure of about 100 psi or less. The nozzle may be large to etch theunderfill material 54 from all or a large portion of thewafer 22 without the nozzle moving, or a smaller nozzle may be used to etch theunderfill material 54 off only a few LEDs at a time followed by the nozzle moving to a next position over thewafer 22. Removing excess material of any kind using microbeads is a known process. Theunderfill material 54 is etch so that its top surface intersects an edge of the LED semiconductor layers to ensure that the entire LED is supported by the underfill during the substrate laser lift-off process. -
FIG. 6 illustrates the laser lift-off process, previously described. The laser pulses are shown byarrows 60. During the laser lift, the surface of the GaN absorbs heat, causing the surface layer to decompose into the Ga and N2. The N2 pressure pushes the sapphire substrate away from the LED. After thegrowth substrates 12 become detached from the semiconductor LED layers during the lift-off process, they are removed by, for example, an adhesive sheet or some other suitable process. - The exposed LED layers are then thinned by, for example, RIE or a mechanical etch, since the exposed top layer is a relatively thick n-layer, and the surface has been damaged by the laser lift-off process. The resulting top surface may then be roughened to increase the light extraction efficiency.
- Other wafer-level processes may also be performed on the LED array while mounted on the
submount wafer 22. One such process may be to overmold a lens on each LED in a single mold process similar to that shown inFIG. 3A or 3B. Details of a wafer-level lens molding process are described in Patent Publication US 2006/0105485, entitled Overmolded Lens Over LED Die, by Grigoriy Basin et al., assigned to the present assignee and incorporated herein by reference. - The
submount wafer 22 is then singulated to form individual LEDs/submounts.FIG. 7 illustrates a single LED/submount soldered to pads on a printedcircuit board 64. - Since there is a wide range of viscosities of the liquid underfill material that are suitable when using the underfill molding process described herein, the underfill material may be selected substantially independently of its viscosity. The dielectric underfill material may be primarily chosen based on its coefficient of thermal expansion, ease of use, and reliability under all temperatures to which the LED is subjected. A polyimide is the preferred underfill, possessing much better qualities than epoxy.
- While particular embodiments of the present invention have been shown and described, it will be obvious to those skilled in the art that changes and modifications may be made without departing from this invention in its broader aspects and, therefore, the appended claims are to encompass within their scope all such changes and modifications as fall within the true spirit and scope of this invention.
Claims (16)