US20090216065A1

US20090216065A1 - Radiation Containing Seeds and Method for High Visibility Magnetic Imaging

Info

Publication number: US20090216065A1
Application number: US12/371,004
Authority: US
Inventors: Christopher D Drobnik; Michael W Drobnik
Original assignee: CR Bard Inc
Current assignee: CR Bard Inc
Priority date: 2008-02-22
Filing date: 2009-02-13
Publication date: 2009-08-27
Also published as: US20150005617A1; US20120253177A1; US8834340B2; US9604076B2

Abstract

A radioactive seed and method for making a radioactive seed with selective magnetic imaging characteristics are provided. The seed comprises a housing which may include a metal shell for at least partially enclosing a radioactive material. The shell encloses a rod having a nickel layer with a phosphorous content, wherein the phosphorous content comprises a level of phosphorous sufficient, when the seed is implanted in tissue, to provide a defined magnetic resonance signature of the seed while substantially eliminating gross artifacts in the magnetic resonance image.

Description

The present application claims benefit of priority to U S. Provisional Application No. 61/030,735, filed Feb. 22, 2008, titled “Radiation Containing Seeds and Methods for High Visibility Magnetic Imaging, the disclosure of which is incorporated herein by reference in its entirety.

TECHNICAL FIELD

The invention relates generally to radioactive seeds and more particularly to radioactive seeds formulated for improved utility in magnetic resonance imaging.

BACKGROUND

Bodily cancers are commonly treated using radiation therapy. Radiation therapy employs radiation to kill cancer cells. One type of radiation therapy is brachytherapy, in which a source of radiation is in direct contact with an afflicted tissue. A common brachytherapy treatment, transperineal seed implantation, involves placing radioactive seeds in the prostate gland to kill prostate gland cancer cells. A physician employs tools, for example, ultrasound, computed axial tomography (“CAT” or “CT”) scans, magnetic resonance “MR”) imaging scans and X-ray images in concert with dose-planning computer software programs to evaluate the medical condition of a patient. The physician constructs an optimal treatment plan to evenly distribute radiation throughout the afflicted tissue. Radioactive seeds of discrete radioactive strengths are inserted into the afflicted tissue through multiple implantation needles at positions corresponding to the treatment plan.
During prostate brachytherapy, the position of the radioactive seeds in relation to the prostate gland and to adjacent structures in the body must be known to a relatively high degree of precision to accurately determine if the dose of radiation delivered from the seeds is adequate to eradicate the prostate cancer. Currently, seeds are guided into the prostate using transrectal ultrasound guidance which is good for imaging the soft tissue of the prostate and the surrounding structures. Occasionally fluoroscopy is used in conjunction with the ultrasound to provide improved images of the seeds. Following the implant, the seed position is typically determined using CT imaging. Using the determined seed positions, the dosimetry of the implant is calculated based on the obtained CT images. The CT images alone, however, have been shown to be deficient in imaging soft tissue structures, so fusing ultrasound or MR images with the CT images is often performed.
Many of the current modalities have shortcomings that need to be overcome before an accurate determination of implant location can be made. For example, ultrasound can determine the structure of the gland and surrounding anatomy to a high degree of accuracy. However, ultrasound is not very accurate at imaging the seeds. Various attempts have been made to design the seeds to be more echogenic (ie. more accurately imaged by ultrasound). The OncoSeed™ by Oncura uses ribs on an outer titanium hull of the seed to increase its ultrasonic reflection. Other attempts have been made to incorporate gas bubbles into the walls of the seeds or into stranding material holding the seeds together to enhance the ultrasound reflection. In the presence of sufficient echogenic artifacts, the location of the contained seeds may be unintelligible in the MR image.
Other methods for locating and imaging the seeds also have shortcomings. Fluoroscopy is very good at identifying the seeds due to the heavy metal X-ray markers in the seeds. Unfortunately, fluoroscopy is poor at imaging the soft tissue in and around the prostate gland. CT imaging is acceptable at imaging both the seeds and the soft tissues, but it is far from ideal. CT imaging is typically not refined enough to image critical structures around the gland and therefore, generally used for gross position analysis only. CT imaging is most often used to do post implant dosimetry. Studies have shown that there is a great deal of operator-to-operator variability, however, in contouring the prostate shape and size for a given image. This variability leads to subsequent variations in the determination of the adequacy of the dose delivered.
MR imaging is the preferred method for imaging the prostate anatomy. Identification of critical structures located around the prostate gland can be performed using MR imaging MR imaging is however rather poor at imaging the seed positions following an implant. Uncontrolled artifacts for the seed can also distort the gland image and make accurate dosimetry assessment difficult. In the presence of sufficiently large artifacts, the seeds and anatomical structures may be unintelligible on an MR image. Additionally, the degree of artifact, or visibility, for a given seed type varies from vendor to vendor and, possibly, even from lot to lot from the same vendor.
Medical professionals therefore are required to compensate for deficits in one or more of the available imaging technologies by employing multiple imaging techniques and fusing the resulting images to determine an accurate location of the implant.
It could be desirable to control the size of an artifact a radioactive seed produces on an MR image of interest, while substantially eliminating gross artifacts that seeds can create on an image. For example, a seed having zero magnetic character can appear as a tiny hole on an MR image, and it cannot be distinguished from blood vessels or other artifacts in a prostate image. If the seed has too much magnetic character, the artifacts may overlap to such a degree then the position of the seeds cannot be accurately determined. However, if the seed is constructed to have a defined, but minimal magnetic character, the image hole for each seed will be big enough to define the seed position but not so large as to irreparably distort the prostate image.
Thus, a need exists for a radioactive seed conducive to providing high fidelity during a magnetic resonance imaging procedure while controlling artifacts produced by the seed.

SUMMARY

The invention in one implementation encompasses a radioactive seed manufactured to have desired magnetic characteristics. The seed may comprise a metal shell for at least partially enclosing a radioactive material. A rod traverses the shell and contains a nickel layer. The nickel layer has a phosphorus content which is sufficient, when the seed is implanted in tissue, to provide a defined magnetic resonance signature.
Another implementation of the invention encompasses a method for making a radioactive seed to have desired magnetic characteristics the method may comprise providing a rod for insertion in a shell of a radioactive seed. The method may comprise the steps of: coating the rod with a nickel layer; providing incorporation of phosphorus into the nickel layer; and adjusting the concentration of the phosphorous such that when the seed is placed in tissue and a magnetic resonance image is taken thereof, a level of phosphorous in the nickel layer is sufficient to substantially eliminate gross artifacts in the magnetic resonance image while providing visibility of the seed on the magnetic resonance image.

DESCRIPTION OF THE DRAWING

Features of exemplary implementations of the invention will become apparent from the description, the claims, and the accompanying drawing in which:

FIG. 1 is a representation of an exemplary implementation of an apparatus that comprises a radioactive seed.

DETAILED DESCRIPTION

While this invention is susceptible of embodiment in many different forms, there is shown in the drawing and will herein be described in detail preferred embodiments of the invention with the understanding that the present disclosure is to be considered as an exemplification of the principles of the invention and is not intended to limit the broad aspect of the invention to the embodiments illustrated.
Turning to FIG. 1, an apparatus 100 comprising a radioactive seed 110 for inserting into a prostate organ for treating, for example, prostate cancer is shown. The radioactive seed 110 in accordance with an embodiment of the invention is manufactured to have desired magnetic characteristics. In accordance with the present disclosure, “desired magnetic characteristics” refers to a magnetic character that is strong enough to provide an MR signature that can be used to define the seed position in an MR image, but not so strong as to irreparably distort the image of e.g., a prostate gland. The seed 110 comprises a metal shell 120 that encloses, at least partially, a radioactive material 130. The radioactive material 130 is used to irradiate cancers in a well known manner. The metal shell 120 may be comprised of any appropriate material, such as titanium. The radioactive seed 110 further comprises a rod 140 traversing the shell 120. The metal shell 120 and the rod 140 may comprise a housing for at least partially enclosing the radioactive material. The rod 140 may be made of a number of layers. For example, the rod 140 may comprise a gold core 150 surrounded by a layer of aluminum 160. The layer of aluminum 160 may be surrounded by consecutive layers of nickel 170, copper 180 and the radioactive material 130, such as radioactive iodine I¹²⁵. C. R. Bard of Murray Hill, N.J. manufactures a similar radioactive seed as the STM 1251 ¹²⁵I seed. An air gap 190 may be filled with an inert gas, such as argon.
The rod 140 traversing the shell 120 can have a nickel layer with a phosphorous content wherein the phosphorous content comprises a level of phosphorous sufficient, when the seed 110 is implanted in tissue, to provide a defined magnetic resonance signature of the seed 110 while substantially eliminating gross artifacts in the MR image. For example, the layers of nickel 170 and copper 180 are commonly plated to the layer of aluminum 160. The electroplating method used to deposit the layer of nickel 170 influences the magnetic characteristics of the rod 140 and therefore affects the visibility of the rod 140 under magnetic resonance imaging (MRI). If the rod 140 is plated using a phosphorous-free bath, the layer of nickel 170 exhibits magnetic characteristics which may cause a relatively large, undesirable artifact on a MR image of the seed 110. Having such artifacts makes an accurate dosimetry assessment difficult. Undesirable artifacts may further complicate assessments in that they may also distort the gland image.
If the rod 140 is plated using a phosphorous bath, the layer of nickel 170 becomes increasingly non-magnetic as the phosphorous content increases. If the phosphorous content of the layer of nickel 170 becomes great enough, the layer of nickel 170 becomes essentially non-magnetic. The relationship between the level of phosphorous and the magnetic characteristics of nickel are discussed in the Standard Specification of Autocatalytic (Electroless) Nickel-Phosphorous Coatings on Metal, published by ASTM International as designation B 733-04, published August 2004, the disclosure of which is hereby incorporated in its entirety by reference. In accordance with an aspect of this invention, the phosphorous content of the layer of nickel 170, and more generally the rod 140, is adjusted to provide enough magnetic character to the seed 110 to allow for imaging and localization, but not enough magnetic character to cause gross artifacts which would interfere with detailed imaging of the prostate gland. Therefore, the electroplating process is used to adjust the phosphorous content of the rod 140 to provide a desired magnetic resonance signature of the seed.
A method for making the radioactive seed 110 to have desired magnetic characteristics is also provided. The rod 140 is inserted in the shell 120 of the radioactive seed 110. In general, the rod 140 may be exposed to, or submersed in, a nickel-containing bath. The phosphorous present in the bath is incorporated into the nickel layer as it is formed on the rod 120 as it is submersed. As previously explained, the level of phosphorous contained in the nickel layer 170 of rod 140 effects the magnetic characteristics of the rod 140. Therefore, the phosphorus content is adjusted by standard means such that when the seed 110 is placed in tissue and an MR image is taken thereof, the level of phosphorous contained in nickel layer 170 of rod 140 is sufficient to substantially eliminate gross artifacts in the MR image while providing visibility of the seed 110 on the MR image. Adjustment of the phosphorous level in the nickel layer 170 of rod 140 may be made by increasing or decreasing the percentage of phosphorous in the bath or the time the rod 140 is submersed. The level of phosphorous may be adjusted so that visibility of the seed 110 in tissue on an MR image is optimized. Determining the proper level of phosphorous may be advantageously determined by any appropriate method. For example, seeds 110 may be manufactured using rods 140 having varying degrees of phosphorus content. The seeds 110 may be inserted into tissue and MR images of the seeds 110 may be generated. Based on one or more characteristics of the MR images, such as the size of artifacts, visibility of the seed 110 and the like, the optimal level of phosphorous in the rods 140 may be determined and optimized seeds produced via the methods disclosed above.
The steps or operations described herein are just exemplary. There may be many variations to these steps or operations without departing from the spirit of the invention. For instance, the steps may be performed in a differing order, or steps may be added, deleted, or modified. The MRI signature of a seed may be varied according to the amount of contained activity (e.g. very radioactive seeds may be made to have larger artifacts than less radioactive seeds, so seeds having different degrees of activity may be identified during a MRI scan.) Seeds of different MRI visibility may be used in different areas of the prostate, such as having very visible seeds in the interior of the gland and less visible seeds in the periphery of the prostate to minimize interference from the peripheral seeds when imaging the interior of the gland. If the seed positions were easily determined on a MRI scan, it may be possible to do the implant without fluoroscopy or CT. In such a case, the seeds would not need a heavy metal gold marker, which would reduce the amount of activity needed in the seeds and therefore reduce cost. By varying the magnetic character of the seeds, it may be possible to move the seeds through an application of an external magnetic field which would permit repositioning after implantation.
In accordance with one embodiment, a method for making a radioactive seed may comprise providing a housing which substantially encloses the radioactive material. The magnetic character of the housing is controlled to obtain a desired magnetic character. A number of methods may be employed to improve, or modify, the magnetic characteristics of the radioactive seed 110. The magnetic character of the radioactive seed may be controlled by varying the metallic composition of the housing, or seed. For example, an amount of iron incorporated into the housing may be varied to provide a defined magnetic resonance signature. Types of materials incorporated into the housing may be selected to provide the desired magnetic character to the radioactive seed. For example, one or more types of stainless steel may be selected for incorporation into the housing to provide the desired magnetic character. The magnetic character of the radioactive seed may be controlled via other processes. For example, an iron-containing seed may be subjected to a magnetic field at a predetermined strength for a predetermined time period in order to obtain the desired magnetic character.
By maximizing the visibility of the seed 110 on an MR image while minimizing gross artifacts on the image, the MRI may be able to provide both anatomic details and accurate seed position. Accurate mapping of both structure and seed position would possibly allow for definitive post-implant quality control, as well as provide a potential for real-time imaging of the quality of the implant using MRI to the ensure the radiation dose delivered to critical structures around the prostate is minimized. These critical structures, including the penile bulb and neurovascular bundles, are difficult to locate using conventional ultrasound imaging but may be easily viewed using magnetic resonance imaging. Accurate dosimetry can be calculated without the need for (and the inherent error in) fusing two images together. There would therefore likely be no need for a second scan or fusion software. Such accurate imaging further saves time for the patient and the physician and would reduce patient radiation exposure if a post-implant CT is not needed or if fluoroscopy during the procedure is reduced.
Although exemplary implementations of the invention have been depicted and described in detail herein, it will be apparent to those skilled in the relevant art that various modifications, additions, substitutions, and the like can be made without departing from the spirit of the invention and these are therefore considered to be within the scope of the invention as defined in the following claims.

Claims

1. A radioactive seed for at least partially enclosing a radioactive material wherein the seed is configured such that the seed has desired magnetic characteristics.

2. The radioactive seed of claim 1 wherein the seed is configured by providing the seed with a metallic composition having the desired magnetic characteristics.

3. The radioactive seed of claim 2 wherein the metallic composition comprises providing the seed with an iron content such that the seed has the desired magnetic characteristics.

4. The radioactive seed of claim 2 wherein the seed is configured by providing a housing with a selected type of stainless steel such that the housing has the desired magnetic characteristics.

5. The radioactive seed of claim 1 wherein the seed is configured by providing the seed with a predetermined metal content and subjecting the seed to a magnetic field such that the housing has the desired magnetic characteristics.

6. The radioactive seed of claim 1 wherein the seed comprises:

a metal shell for at least partially enclosing a radioactive material; and

a rod traversing the shell comprised of a phosphorus-containing nickel layer, wherein the phosphorous content comprises a level of phosphorous sufficient, when the seed is implanted in tissue, to provide a defined magnetic resonance signature of the seed while substantially eliminating gross artifacts in the magnetic resonance image.

7. The radioactive seed of claim 6 wherein the metal shell is comprised of titanium.

8. The radioactive seed of claim 6 wherein the phosphorous content is applied to the rod through an electroplating process.

9. The radioactive seed of claim 6 wherein the phosphorous content is applied to the rod through a deposition process.

10. A method for making a radioactive seed comprising the steps of:

providing a housing for at least partially enclosing a radioactive material; and

configuring the housing such that the radioactive seed has desired magnetic characteristics.

11. The method of claim 10 wherein the housing is configured by providing the housing with a metallic composition having the desired magnetic characteristics.

12. The method of claim 10 wherein the housing is provided with an iron content such that the housing has the desired magnetic characteristics.

13. The method of claim 10 wherein the housing is configured by providing the housing with a selected type of stainless steel such that the housing has the desired magnetic characteristics.

14. The method of claim 10 wherein the housing is configured by providing the housing with a predetermined metal content and subjecting the housing to a magnetic field such that the housing has the desired magnetic characteristics.

15. The method of claim 10 wherein the housing comprises a rod for insertion in a shell of a radioactive seed and further comprising the steps of:

exposing the rod to a phosphorous-containing nickel material;

providing absorption of phosphorous and nickel into the rod; and

adjusting the concentration of the phosphorous such that the radioactive seed has the desired magnetic characteristics.

16. The method of claim 15 wherein the desired magnetic characteristics are determined such that when the radioactive seed is placed in tissue and a magnetic resonance image is taken thereof, a level of phosphorous absorbed in the nickel layer of the rod is sufficient to substantially eliminate gross artifacts in the magnetic resonance image while providing visibility of the seed on the magnetic resonance image.

17. The method of claim 16 further comprising the step of selecting the level of phosphorous contained in the nickel layer of the rod such that visibility of the seed in the magnetic resonance image is optimized.

18. The method of claim 15 further comprising the steps of:

removing the rod from exposure to the nickel-phosphorous material;

inserting the rod in the seed;

inserting the seed in tissue;

generating a magnetic resonance image of the seed in the tissue; and

changing the concentration of phosphorous in the nickel layer of the rod based on a characteristic of the magnetic resonance image.

19. The method of claim 18 wherein the step of exposing comprises the steps of:

selecting a percentage of phosphorous in a bath; and

selecting a percentage of nickel in the bath; and

submerging the rod in the bath for a predetermined time period.

20. A method of making a radioactive seed comprising the steps of:

providing a shell; and

inserting a rod in the shell, the rod having a nickel layer with a phosphorous content wherein the phosphorous content comprises a level of phosphorous sufficient, when the seed is implanted in tissue, to provide a defined magnetic resonance signature of the seed while substantially eliminating gross artifacts in the magnetic resonance image.