US20070066086A1 - Method of forming silicon-containing insulation film having low dielectric constant and low film stress - Google Patents
Method of forming silicon-containing insulation film having low dielectric constant and low film stress Download PDFInfo
- Publication number
- US20070066086A1 US20070066086A1 US11/550,917 US55091706A US2007066086A1 US 20070066086 A1 US20070066086 A1 US 20070066086A1 US 55091706 A US55091706 A US 55091706A US 2007066086 A1 US2007066086 A1 US 2007066086A1
- Authority
- US
- United States
- Prior art keywords
- compound
- gas
- group
- silicon
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for forming a silicon-containing insulation film on a substrate by plasma polymerization includes: introducing a reaction gas comprising (i) a source gas consisting of a silicon-containing hydrocarbon linear compound containing at least one vinyl group (Si-vinyl compound), and (ii) an additive gas, into a reaction chamber where a substrate is placed; and applying radio-frequency power to the gas to cause plasma polymerization, thereby depositing an insulation film on the substrate.
Description
- This is a divisional application of U.S. patent application Ser. No. 10/644,195, filed Aug. 20, 2003, the disclosure of which is herein incorporated by reference in its entirety.
- 1. Field of the Invention
- This invention relates generally to a semiconductor technique and more particularly to a method for forming on a semiconductor substrate a silicon-containing insulation film having low film stress by using a plasma CVD (chemical vapor deposition) apparatus.
- 2. Description of the Related Art
- As semiconductors have progressed to accommodate a demand for high speed and high density in recent years, a reduction of capacitance between lines is required to avoid signal delays in the multi-layer wiring technology field. Because a reduction in the dielectric constant of a multi-layer wiring insulation film is required in order to reduce the capacitance between lines, insulation films having low dielectric constants have been developed.
- Conventionally, a silicon oxide (SiOx) film is formed by adding oxygen (O2), nitric oxide (NO) or nitrous oxide (N2O) as an oxidizing agent to a silicon source gas such as SiH4 and Si(OC2H5)4 and applying heat or plasma energy to the source gas. A dielectric constant (ε) of this film was approximately 4.0.
- If a source gas having two alkoxy groups is used, the dielectric constant of a resulting film can be lowered. For example, by using (CH3)2Si(OCH3)2 as a source gas, a siloxan polymer film having a dielectric constant of 3.0 or lower can be formed by plasma polymerization.
- However, films having a dielectric constant of 3.0 or lower have high film stress such as 70 MPa. Because a semiconductor device has multiple layers, if insulation films have high film stress, the adverse effect becomes significant. As a result, such a semiconductor device may not function as is designed. Thus, a reduction of film stress is required.
- Conventionally, for plasma polymerization, high-frequency power (e.g., 13.56 MHz) is applied to generate a plasma. By overlaying low-frequency power (e.g., 400 kHz) and high-frequency power, it is possible to lower film stress. However, when a ratio of low-frequency power to high-frequency power is increased, the dielectric constant of the film increases. Thus, it is difficult to form a film having a low dielectric constant and low film stress.
- One aspect of the present invention is characterizable in that a silicon-containing hydrocarbon compound having at least one vinyl group is used as a source gas for plasma polymerization, thereby forming a film having low film stress without increasing a dielectric constant.
- In an embodiment, the present invention provides a method for forming a silicon-containing insulation film on a substrate by plasma polymerization, comprising the steps of: (a) introducing a reaction gas comprising (i) a source gas comprising a silicon-containing hydrocarbon compound containing at least one vinyl group (Si-vinyl compound), and (ii) an additive gas, into a reaction chamber where a substrate is placed; and (b) applying radio-frequency power to the gas to cause plasma polymerization, thereby depositing an insulation film on the substrate.
- In the above, in an embodiment, the Si-vinyl compound includes, but is not limited to, a compound or compounds selected from the group consisting of linear silicon-containing hydrocarbon compounds having the formula SiαOα−1R2α−β+2(OR)β wherein α is an integer of 1-3, β is 0, 1, or 2, R is C1-6 saturated or unsaturated hydrocarbon, and at least one R attached to Si contains a vinyl group; cyclic compounds having the formula SinOnR2n, wherein n is an integer of 3-6, R is C1-6 saturated or unsaturated hydrocarbon, and at least one R attached to Si contains a vinyl group; and cyclic compounds having the formula Sip(C2H2)pR2p wherein p is an integer of 3-6, and R is C1-6 saturated or unsaturated hydrocarbon. For example, R may be —CzH2(z-w)+1 wherein z is an integer of 2-4, and w represents the number of unsaturated carbon bonds and is an integer of 1-3. Further, the Si-vinyl compound may be a liner compound wherein α is 1 and β is 0. For example, the compound is (CH3)2Si(C2H3)2. In another embodiment, the Si-vinyl compound is a cyclic compound wherein n is 3. The compounds described above can be used singly or in any combination of two or more compounds.
- In an embodiment, radio-frequency (RF) power is high-frequency power without low-frequency power. In the embodiment, the use of the Si-vinyl compound effectively reduce film stress, and thus, there is no need to overlay high-frequency RF power and low-frequency RF power. For example, high-frequency power has 2 MHz or higher frequencies (including (including 5, 10, 15, 20, 25, 30, 40, 50, 60, 70 MHz, and ranges including any of the forgoing). However, in an embodiment, a combination of high-frequency RF power having 2 MHz or higher frequencies and low-frequency RF power having less than 2 MHz frequencies can be used (the ratio of low-frequency power to high-frequency power may be less than 50% including 40%, 30%, 20%, 10%, 5%, and ranges including any of the forgoing (preferably, 3%-30%). High-frequency RF power may be applied at a high power level such as 1.5 W/cm2 or higher (including 2.0, 2.25, 2.5, 2.75, 3.0, 3.25, 3.5 W/cm2, and ranges including any of the foregoing). Such a high power level can increase the mechanical strength and deposition rate of a resultant insulation film.
- According to the above embodiments, the film having low stress can be formed without sacrificing dielectric property. In an embodiment, the dielectric constant can further be reduced. However, in some cases, when using solely the Si-vinyl compound, the mechanical strength of the film may decrease. In order to compensate for a reduction of mechanical strength, the addition of a silicon-containing hydrocarbon compound (Si compound) having no vinyl group to the source gas may be effective.
- In the above, in an embodiment, the Si compound includes, but is not limited to, a compound or compounds selected from the group consisting of linear compounds having the formula SiαOα−1R2α−β+2(OR)β wherein α is an integer of 1-3, β is 0, 1, or 2, R is C1-6 saturated hydrocarbon; and cyclic compounds having the formula SinOnR2n, wherein n is an integer of 3-6, R is C1-6 saturated hydrocarbon. In an embodiment, the flow ratio of the Si-vinyl compound to the Si compound may be in the range of 1% to 100% (including 5%, 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, and ranges including any of the forgoing).
- Further, the additive gas may be selected from the group consisting of a carrier gas, an oxidizing gas, and a plasma stabilizing gas. In an embodiment, the plasma stabilizing gas includes, but is not limited to, a gas selected from the group consisting of H2, CnH2n+2, CnH2n, and CnH2n+1OH wherein n is an integer of 1-5. In an embodiment, the oxidizing gas includes, but is not limited to, a gas selected from the group consisting of O2, CO2, H2O, O3, and NO2. In an embodiment, the carrier gas includes, but is not limited to, an inert gas selected from the group consisting of He, Ar, and N2.
- In an embodiment, the ratio of the Si-vinyl compound to the Si compound may be controlled to obtain a siloxan polymer having a film stress of 60 MPa or lower (including 50 MPa, 40 MPa, 30 MPa, 20 MPa, 10 MPa, and ranges including any of the forgoing) and a dielectric constant of 3.0 or lower (including 2.9, 2.8, 2.7, 2.6, 2.5, 2.4, 2.3, and ranges including any of the forgoing). If the Si-vinyl compound and the Si compound do not contain Si—O bonds and additional oxygen is not supplied, a hard film composed of a silicon carbide material can be formed which may have a dielectric constant of 4.5 or lower (including 4.0, 3.5, 3.0, and ranges including any of the forgoing).
- In another aspect, the present invention provides a method for forming a silicon-containing insulation film on a substrate by plasma polymerization, comprising the steps of: (a) introducing a reaction gas comprising (i) a source gas comprising a silicon-containing hydrocarbon compound containing at least one vinyl group (Si-vinyl compound);
- (ii) a silicon-containing hydrocarbon compound (Si compound) having no vinyl group; and (iii) an additive gas, into a reaction chamber where a substrate is placed; (b) controlling the ratio of the Si-vinyl compound to the Si compound in the range of 10% to 100%; and (c) applying radio-frequency power to the gas to cause plasma polymerization, thereby depositing an insulation film on the substrate. The compounds described above can be used in this embodiment. Further, the conditions described above can also be applied in this embodiment.
- Additionally, after forming an insulation film on a substrate, the substrate can be subjected to any suitable curing treatment such as electron beam irradiation treatment, plasma treatment (e.g., hydrogen plasma treatment), and other annealing processes in order to reinforce mechanical strength of the resulting film.
- In the present invention, an “insulation film” includes any dielectric film regardless of its intended use such as cap layers, hard films, laminated insulation layers, etc.
- For purposes of summarizing the invention and the advantages achieved over the prior art, certain objects and advantages of the invention have been described above. Of course, it is to be understood that not necessarily all such objects or advantages may be achieved in accordance with any particular embodiment of the invention. Thus, for example, those skilled in the art will recognize that the invention may be embodied or carried out in a manner that achieves or optimizes one advantage or group of advantages as taught herein without necessarily achieving other objects or advantages as may be taught or suggested herein.
- Further aspects, features and advantages of this invention will become apparent from the detailed description of the preferred embodiments which follow.
- These and other features of this invention will now be described with reference to the drawings of preferred embodiments which are intended to illustrate and not to limit the invention.
-
FIG. 1 is a graph illustrating the relationship between the ratio of divinyldimethylsilan (DVDMS)/(divinyldimethylsilan (DVDMS)+dimethyldimethoxysilane (DMDMOS)) and film stress and dielectric constant. -
FIG. 2 is a graph illustrating the relationship between the ratio of divinyldimethylsilan (DVDMS)/(divinyldimethylsilan (DVDMS)+1,1,3,3-tetramethyldimethoxydisiloxane (TMDMOS)) and film stress and dielectric constant. - The present invention will be described in detail below with reference to preferred embodiments. However, the present invention simply includes these embodiments and should not be limited thereto.
- In an embodiment of the present invention, a reaction gas comprising (i) a source gas comprising a silicon-containing hydrocarbon compound containing at least one vinyl group (Si-vinyl compound), and (ii) an additive gas. Any suitable Si-vinyl compounds can be used. For example, a usable compound or compounds may be selected from the group consisting of linear silicon-containing hydrocarbon compounds having the formula SiαOα−1R2α−β+2(OR)β wherein α is an integer of 1-3, β is 0, 1, or 2, R is C1-6 saturated or unsaturated hydrocarbon, and at least one R attached to Si contains a vinyl group; cyclic compounds having the formula SinOnR2n, wherein n is an integer of 3-6, R is C1-6 saturated or unsaturated hydrocarbon, and at least one R attached to Si contains a vinyl group; and cyclic compounds having the formula Sip(C2H2)pR2p wherein p is an integer of 3-6, and R is C1-6 saturated or unsaturated hydrocarbon. R may be —CzH2(z−w)+1 wherein z is an integer of 2-4, and w represents the number of unsaturated carbon bonds and is an integer of 1-3. The above compounds can be used singly or in any combination of two or more compounds.
-
- wherein R1, R2, R3, and R4 are each independently C1-6 saturated or unsaturated hydrocarbon such as CH3, C2H3, C2H5, C3H7, C6H5, C2H3, C3H5, C4H7, and C4H5, and at least one of R1, R2, R3, and R4 contains a vinyl group. An oxidizing gas may be added to supply oxygen to form a siloxan polymer. When using the Si-vinyl compound of the above formula without supplying additional oxygen, a silicon carbide film can be formed. As this type of compound, (CH3)3Si(C2H3), (CH3)2Si(C2H3)2, and (C6H5)Si(C2H3)3 can be used, for example.
-
-
-
- wherein R1, R2, R3, R4, R5, and R6 are each independently C1-6 saturated or unsaturated hydrocarbon such as CH3, C2H3, C2H5, C3H7, C6H5, C2H3, C3H5, C4H7, and C4H5, and at least one of R1, R3, R4, and R6 contains a vinyl group. An oxidizing gas may be added to supply oxygen to form a siloxan polymer. As this type of compound, 1,3-divinyl tetramethylsilane (DVTMS, [CH2═CH2Si(CH3)2]2O) can be used, for example.
-
- wherein R1, R2, R3, R4, R5, and R6 are each independently C1-6 saturated or unsaturated hydrocarbon such as CH3, C2H3, C2H5, C3H7, C6H5, C2H3, C3H5, C4H7, and C4H5, and at least one of R1, R2, R3, R4, R5, and R6 contains a vinyl group.
-
-
- wherein R1, R2, R3, R4, R5, and R6, are each independently C1-6 saturated or unsaturated hydrocarbon such as CH3, C2H3, C2H5, C3H7, C6H5, C2H3, C3H5, C4H7, and C4H5. An oxidizing gas may be added to supply oxygen to form a siloxan polymer. When using the Si-vinyl compound of the above formula without supplying additional oxygen, a silicon carbide film can be formed.
- In an embodiment, the source gas may further comprise a silicon-containing hydrocarbon compound (Si compound) having no vinyl group to improve mechanical strength. The Si compound may be a compound or compounds selected from the group consisting of linear compounds having the formula SiαOα−1R2α−β+2(OR)β wherein α is an integer of 1-3, β is 0, 1, or 2, R is C1-6 saturated hydrocarbon; and cyclic compounds having the formula SinOnR2n, wherein n is an integer of 3-6, R is C1-6 saturated hydrocarbon.
- The flow ratio of the Si-vinyl compound to the Si compound may be in the range of 10% to 100% (including 20%, 30%, 40%, 50%, 60%, 70%, 80%, 90%, and ranges including any of the forgoing). The ratio may be controlled so as to obtain a film stress of 60 MPa or lower (including 50 MPa, 40 MPa, 30 MPa, 20 MPa, 10 MPa, and ranges including any of the forgoing) and a dielectric constant of 3.0 or lower (including 2.9, 2.8, 2.7, 2.6, 2.5, 2.4, 2.3, and ranges including any of the forgoing). Further, if the Si-vinyl compound and the Si compound do not contain Si—O bonds and additional oxygen is not supplied, a silicon carbide film can be formed which may have a dielectric constant of 4.5 or lower (including 4.0, 3.5, 3.0, and ranges including any of the forgoing).
- Si compounds which can be mixed include a compound having at least one Si—O bond, two or less O—CnH2n+1 bonds and at least two hydrocarbon radicals bonded with silicon (Si). A preferable silicon-containing hydrocarbon compound has formula:
SiαOα−1R2α−β+2(OCnH2n+1) β - wherein α is an integer of 1-3, β is 0, 1, or 2, n is an integer of 1-3, and R is C1-6 hydrocarbon attached to Si. In an embodiment, α is 1 or 2, and β is 2.
-
-
-
- Further, except for those species indicated above, the silicon-containing hydrocarbon compound can include at least one species of the compound expressed by the chemical formula:
wherein R1, R2, R3, R4, R5 and R6 are each independently C1-6 hydrocarbon such as CH3, C2H5, C3H7, and C6H5, and the additive gases are argon (Ar), Helium (He) and either nitrogen oxide (N2O) or oxygen (O2). - Furthermore, except for those species indicated above, the silicon-containing hydrocarbon compound can include at least one species of the compound expressed by the chemical formula:
wherein R1, R2, R3 and R4 are each independently C1-6 hydrocarbon such as CH3, C2H5, C3H7, and C6H5, and the additive gases are argon (Ar), Helium (He) and either nitrogen oxide (N2O) or oxygen (O2). - These types of source gas is disclosed in U.S. Pat. No. 6,352,945, U.S. Pat. No. 6,383,955, and U.S. Pat. No. 6,432,846, all of which are incorporated herein by reference in their entirety. In embodiments, the source gas may be dimethyl-dimethoxysilane (DM-DMOS), 1,1,3,3-tetramethyldimethoxydisiloxane (TMDMOS), or phenylmethyl dimethoxysilane (PM-DMOS). Different source gases can be mixed or a single source gas can be used alone.
- In an embodiment, the additive gas may be selected from the group consisting of a carrier gas, an oxidizing gas, and a plasma stabilizing gas.
- The carrier gas can be any suitable inert gas including Ar, Ne, He, and N2. The reaction gas may further comprise an oxygen-supplying gas (oxidizing gas). The inert gas may be supplied at a flow rate of 15-300% (50% or more in an embodiment) of that of the source gas. The oxygen-supplying gas can be any suitable gas which can supply oxygen and may include O2, NO, O3, H2O, CO2, and N2O. In an embodiment, the oxygen-supplying gas may be supplied at a flow rate lower than that of the source gas (for the purpose of supplying oxygen, it can be used more). The addition of oxidizing gas is effective to activate a plasma. However, there may be cases where a plasma is overly activated. If an inert gas is added to stabilize a plasma, the dielectric constant tends to increase. Thus, in such cases, a plasma stabilizing gas can be used effectively. That is, in the above, in a case where even if film stress is appropriate, sufficient mechanical strength cannot be accomplished, by further introducing an additive gas selected from the group consisting of an oxidizing gas and a plasma stabilizing gas such as CxHyOz wherein x=0-5, y=2-12, and z=0-3 (such as CnH2n+2 (n=1-5), CnH2n (n=1-5), CnH2n+1H (n=1-5)), into the reaction space when the source gas is introduced, hardness of the hard film can be improved while optimizing film stress of a film.
- The flow rate of additive gas may be 0% to about 500% of the source gas flow (including 10%, 50%, 100%, 200%, 300%, 400%, and ranges including any of the foregoing). In an embodiment, the gas of CxHyOz may be selected from the group consisting of H2, CnH2n+2 (n=1-5) (e.g., CH4, C2H6, C3H8, C2H4, C3H6, C4H8), C1-6 alkanol (e.g., CH3CH(OH)CH2OH, CH3CH(OH)OCH3, CH3CH(OH)CH2OCH3), and C2-6 ether (e.g., CH3CH(OH)CH3). For example, preferably gases include reactive gases such as ethylene glycol, 1,2-propanediol, isopropyl alcohol (IPA), ethylene, or diethyl ether.
- In an embodiment, the reaction gas is excited upstream of the reaction chamber. In this embodiment, the reaction gas can be excited in a remote plasma chamber installed upstream of a reactor, and the film is deposited on a substrate in the reactor. The source gas and the additive gas can be introduced into the remote plasma chamber. In this case, a reaction space is composed of the interior of the remote plasma chamber, the interior of the reactor, and the interior of the piping connecting the remote plasma chamber and the reactor. Because of using the interior of the remote plasma chamber, the interior of the reactor can be significantly reduced, and thus, the distance between the upper electrode and the lower electrode can be reduced. This leads to not only downsizing the reactor, but also uniformly controlling a plasma over the substrate surface. Any suitable remote plasma chamber and any suitable operation conditions can be used in the present invention. For example, usable are the apparatus and the conditions disclosed in U.S. patent application Ser. No. 09/511,934 filed Feb. 24, 2000 and No. 09/764,523 filed Jan. 18, 2001, U.S. Pat. No. 5,788,778, and U.S. Pat. No. 5,788,799. The disclosure of each of the above is incorporated herein by reference in its entirety.
- Further, the excitation of the reaction gas may comprise exciting the additive gas and contacting the excited additive gas and the source gas. The excitation of the reaction gas can be accomplished in the reactor or upstream of the reactor. As described above, both the source gas and the additive gas can be excited in a remote plasma chamber. Alternatively, the excitation of the reaction gas can be accomplished by exciting the additive gas in a remote plasma chamber and mixing it with the source gas downstream of the remote plasma chamber. Alternatively, the reaction gas can be heated in a pre-heat chamber installed upstream of a reactor, the reaction gas is excited in the reactor, and film is deposited on the substrate in the reactor. The source gas and the additive gas can be introduced into the pre-heater chamber. In this case, the reaction space is composed of the interior of the pre-heater chamber, the interior of the reactor, and the interior of the piping connecting the pre-heater chamber and the reactor. Because of using the interior of the pre-heater chamber, the interior of the reactor can be significantly reduced, and thus, the distance between the upper electrode and the lower electrode can be reduced. This leads to not only downsizing the reactor, but also uniformly controlling a plasma over the substrate surface. Any suitable remote plasma chamber and any suitable operation conditions can be used in the present invention. For example, usable are the apparatus and the conditions disclosed in the aforesaid references.
- Further, the excitation of the reaction gas comprises exciting the additive gas and contacting the excited additive gas and the source gas. In this embodiment, the additive gas can be excited in a remote plasma chamber, and the source gas is heated in a pre-heater chamber where the excited additive gas and the source gas are in contact, and then the reaction gas flows into the reactor for deposition of a film. In this case, deposition of unwanted particles on a surface of the remote plasma chamber, which causes a failure of ignition or firing, can effectively be avoided, because only the additive gas is present in the remote plasma chamber. The source gas is mixed with the excited additive gas downstream of the remote plasma chamber.
- In order to form siloxan polymers or oligomers in the present invention, the residence time of a reaction gas may be controlled as disclosed in U.S. Pat. No. 6,352,945, U.S. Pat. No. 6,383,955, and U.S. Pat. No. 6,432,846, all of which are incorporated herein by reference in their entirety. However, in the present invention, the residence time can very more widely than the above. In embodiments, Rt may be 50 msec or higher (including 70 msec, 90 msec, 100 msec, 150 msec, 200 msec, 250 msec, and ranges including any of the forgoing).
- The flow rate of the reaction gas is determined based on the intensity of RF power, the pressure selected for reaction, and the type of source gas and cross-linking gas. The reaction pressure is normally in the range of 1-10 Torr, preferably 3-7 Torr, so as to maintain a stable plasma. This reaction pressure is relatively high in order to lengthen the residence time of the reaction gas. The total flow of the reaction gas is important for reducing the relative dielectric constant of a resulting film. In general, the longer the residence time, the lower the relative dielectric constant becomes. The source gas flow necessary for forming a film depends on the desired deposition rate and the area of a substrate on which a film is formed. For example, in order to form a film on a substrate [r(radius)=100 mm] at a deposition rate of 300 nm/min, at least 50 sccm of the source gas (preferably 100-500 sccm, including 150, 200, 250 sccm) is expected to be included in the reaction gas. A temperature of the semiconductor wafer may be maintained at a temperature of e.g., 350 to 450° C.
- Examples of the present invention will be described below, wherein as a source gas, divinyldimethylsilan (DVDMS), dimethyldimethoxysilane (DMDMOS), 1,1,3,3-tetramethyldimethoxydisiloxane (TMDMOS), and 1,3,5-trimethyl-1,3,5-trivinyilycyclotrisiloxane (TMTVS) were used. As a plasma CVD apparatus, Eagle™-10 (manufactured by ASM Japan in Tokyo) was used.
- Using the plasma CVD apparatus, an insulation film was formed on a φ200 mm silicon substrate by changing the ratio of DVDMS to DMDMOS. Experimental conditions and results are shown in Table 1.
TABLE 1 Example 1 2 3 4 5 DVDMS [sccm] 134 114 94 54 0 DMDMOS [sccm] 0 20 40 80 134 Ratio 100% 85% 70% 40% 0% He [sccm] 140 140 140 140 140 HRF* [W] 950 950 950 950 950 Press [Torr] 4.5 4.5 4.5 4.5 4.5 k-value 2.79 2.79 2.81 2.90 3.23 Stress [MPa] 28.8 32.4 39.7 41.5 72.4
*27.12 MHz
- Using the plasma CVD apparatus, an insulation film was formed on a (200 mm silicon substrate by changing the ratio of DVDMS to TMDMOS. Experimental conditions and results are shown in Table 2.
TABLE 2 Example 6 7 8 9 10 DVDMS [sccm] 134 114 67 40 0 TMDMOS [sccm] 0 20 67 94 134 Ratio 100% 85% 50% 30% 0% He [sccm] 140 140 140 140 140 HRF* [W] 950 950 950 950 950 Press [Torr] 4.5 4.5 4.5 4.5 4.5 k-value 2.72 2.72 2.68 2.72 3.00 stress 36 41 45 44 53
*27.12 MHz
-
FIG. 1 is a graphs showing the relationship between the mixing ratio of DVDMS/DMDMOS and dielectric constants and film stress under the above-mentioned experimental conditions.FIG. 2 is a graphs showing the relationship between the mixing ratio of DVDMS/TMDMOS and dielectric constants and film stress under the above-mentioned experimental conditions. Both show that the higher the mixing ratio, the lower the dielectric constant and the lower the film stress become. Conventionally, to reduce film stress, low-frequency power and high-frequency power were overlaid. However, by doing so, the dielectric constant will increase. In the above embodiments, when the mixing ratio of DVDMS to DMDMOS was 100%, film stress was reduced to about 40% of that obtained when the ratio was 0% (100% DMDMOS), and further, the dielectric constant was 0.44 lower than that obtained when the ratio was 0%. When the mixing ratio of DVDMS to TMDMOS was 100%, film stress was reduced to about 70% of that obtained when the ratio was 0% (100% TMDMOS), and further, the dielectric constant was 0.3 lower than that obtained when the ratio was 0%. Thus, it is understood that by using a Si-vinyl compound as a source gas, both objectives, i.e., lowering a dielectric constant and lowering film stress, can effectively be accomplished simultaneously. - Using the plasma CVD apparatus, an insulation film was formed on a φ200 mm silicon substrate by using TMTVS and He. Experimental conditions and results are shown in Table 3.
TABLE 3 Example 11 12 1,3,5-TMTVS [sccm] 100 100 He [sccm] 180 100 HRF [W] 500 500 Press [Torr] 4 4 k-value 2.74 2.65 Stress [MPa] 35 32
* 27.12 MHz
- Using the plasma CVD apparatus, an insulation film was formed on a φ200 mm silicon substrate by using DVDMS and TMDMOS as a source gas and further using He, O2, and isopropyl alcohol (IPA) as an additive gas. Experimental conditions and results are shown in Table 4. Rt (residence time) described above was about 93 msec in Examples 13 and 15, and about 73 msec in Examples 14 and 16.
Example 13 14 15 16 DVDMS [sccm] 67 67 20 20 TMDMOS [sccm] 67 67 114 114 He [sccm] 140 140 140 140 O2 [sccm] 110 110 110 110 IPA [sccm] 0 100 0 100 HRF [W] 950 950 950 950 Press [Torr] 6.0 6.0 6.0 6.0 Stability** unstable stable unstable stable k-value — 2.57 — 2.58 Stress [MPa] — 50 — 54
* 27.12 MHz;
**plasma stability
- In the above, in Examples 13 and 15, a plasma was unstable, and thus, deposition of a film was not successful. The examples show that when adding an oxidizing gas, plasma reaction is overly activated, thereby rendering a plasma unstable. However, by adding a plasma stabilizing gas, a plasma can be stabilized. When adding an inert gas in order to stabilize a plasma, instead of a plasma stabilizing gas, the dielectric constant increases.
- According to the present invention, by using a Si-vinyl compound as a source gas, a dielectric film having low film stress can be manufactured without impact on the manufacturing cost and without sacrificing other film properties.
- It will be understood by those of skill in the art that numerous and various modifications can be made without departing from the spirit of the present invention. Therefore, it should be clearly understood that the forms of the present invention are illustrative only and are not intended to limit the scope of the present invention.
Claims (16)
1. A method for forming a silicon-containing insulation film on a substrate by plasma polymerization, comprising the steps of:
introducing a reaction gas comprising (i) a source gas consisting of a silicon-containing hydrocarbon linear compound containing at least one vinyl group (Si-vinyl compound), and (ii) an additive gas, into a reaction chamber where a substrate is placed; and
applying radio-frequency power to the gas to cause plasma polymerization, thereby depositing an insulation film on the substrate.
2. The method according to claim 1 , wherein the Si-vinyl compound is a compound or compounds selected from the group consisting of linear silicon-containing hydrocarbon compounds having the formula SiαOα−1R2α−β+2(OR)β wherein α is an integer of 1-3, β is 0, 1, or 2, R is C1-6 saturated or unsaturated hydrocarbon, and at least one R attached to Si contains a vinyl group.
3. The method according to claim 2 , wherein R is —CzH2(z−w)+1 wherein z is an integer of 2-4, and w represents the number of unsaturated carbon bonds and is an integer of 1-3.
4. The method according to claim 3 , wherein the Si-vinyl compound is a liner compound wherein α is 1 and β is 0.
5. The method according to claim 4 , wherein the compound is (CH3)2Si(C2H3)2.
6. The method according to claim 1 , wherein the reaction gas further comprises (iii) a silicon-containing hydrocarbon compound (Si compound) having no vinyl group.
7. The method according to claim 6 , wherein the introducing step further comprises controlling the ratio of the Si-vinyl compound to the Si compound in the range of 50% to 100%.
8. The method according to claim 6 , wherein the Si compound is a compound or compounds selected from the group consisting of linear compounds having the formula SiαOα−1R2α−β+2(OR)β wherein α is an integer of 1-3, β is 0, 1, or 2, R is C1-6 saturated hydrocarbon; and cyclic compounds having the formula SinOnR2n, wherein n is an integer of 3-6, R is C1-6 saturated hydrocarbon.
9. The method according to claim 6 , wherein the ratio is controlled to obtain a siloxan polymer having a film stress of 40 MPa or lower and a dielectric constant of 3.0 or lower.
10. The method according to claim 6 , wherein the Si-vinyl compound and the Si compound do not contain Si—O bonds, and the insulation film is a hard film composed of a silicon carbide material.
11. The method according to claim 1 , wherein the additive gas is selected from the group consisting of a carrier gas, an oxidizing gas, and a plasma stabilizing gas.
12. The method according to claim 11 , wherein the plasma stabilizing gas is selected from the group consisting of H2, CnH2n+2, CnH2n, and CnH2n+1OH wherein n is an integer of 1-5.
13. The method according to claim 11 , wherein the oxidizing gas is selected from the group consisting of O2, CO2, H2O, O3, and NO2.
14. The method according to claim 11 , wherein the carrier gas is an inert gas selected from the group consisting of He, Ar, and N2.
15. The method according to claim 1 , wherein the radio-frequency power is high-frequency power.
16. The method according to claim 15 , wherein the high-frequency power has a frequency of 2 MHz or higher.