US20040120040A1 - Optical component - Google Patents
Optical component Download PDFInfo
- Publication number
- US20040120040A1 US20040120040A1 US10/721,104 US72110403A US2004120040A1 US 20040120040 A1 US20040120040 A1 US 20040120040A1 US 72110403 A US72110403 A US 72110403A US 2004120040 A1 US2004120040 A1 US 2004120040A1
- Authority
- US
- United States
- Prior art keywords
- optical component
- image
- light
- images
- analyser
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
An optical component contains two or more hidden images for authentication and antiforgery purposes. The images are successively revealed and concealed when the optical component is held between two polarisers and one of them is rotated. The optical component comprises one or more optical retarder(s) in which the images are embedded in separate adjacent stripes or areas, each image being associated with a different mode of interaction with polarised light. Instead of two polarisers, one will suffice if the component is mounted on a reflector.
Description
- The invention relates to an optical component containing a normally hidden image.
- A particular use of the components according to the invention is in the field of protection against forgery and copying and simple yet unambiguous document authentication.
- The increasingly high-quality copying techniques which are becoming available make it increasingly difficult to safeguard banknotes, credit cards, securities, identity cards and the like against forgery. Furthermore, counterfeit branded products (even including counterfeit pharmaceuticals) and copies of copyright-protected products, for example compact discs, computer software and electronics chips, are being produced and distributed worldwide. The increasing number of forgeries necessitates new authentication elements which are safeguarded against forgery and can be identified both visually and by machine.
- In the field of copy-protecting banknotes, credit cards etc., there are already a considerable number of authentication elements. Depending on the value of the document to be protected, very simple or relatively highly complex elements are employed. Some countries are content to provide banknotes with metal strips which come out black on a photocopy. Although this prevents them from being photocopied, elements of this type are very easy to imitate. In contrast to this, there are also more complex authentication elements, for example holograms and cinegrams. Authentication elements of this type are based on the diffraction of light by gratings and need to be observed under different viewing angles in order to verify their authenticity. These diffracted elements produce three-dimensional images, colour variations or kinematic effects which depend on the angle of observation and have to be checked on the basis of predetermined criteria or rules. It is not practically possible to use machines for reading information, for example images or numbers, encoded using this technique. Furthermore, the information content of these elements is very limited, and only an optical specialist will be capable of discriminating definitively between forgeries and an original.
- A further consideration with diffractive optical effects is that these have also been used for consumer articles such as wrapping paper, toys and the like. The relevant production methods have therefore become widely known and are correspondingly straightforward to imitate.
- Further to the diffractive elements mentioned above, other components are also known which are suitable for optimum copy protection. These include optical components, as disclosed for example by EP-A-689084 or EP-A-689065, that is to say components with an anisotropic liquid-crystal layer, which latter has local structuring of the molecular orientation.
- These components are based on a hybrid layer structure which consists of an orientation layer and a layer which is in contact with it and consists of liquid-crystal monomers or pre-polymers cross-linked with one another. In this case, the orientation layer consists of a photo-oriented polymer network (PPN)—synonymous with LPP used in other literature—which, in the oriented state, through a predetermined array, defines regions of alternating orientations. During the production of the liquid-crystal layer structure, the liquid-crystal monomers or pre-polymers are zonally oriented through interaction with the PPN layer. This orientation which, in particular, is characterised by a spatially dependent variation of the direction of the optical axis, is fixed by a subsequent cross-linking step, after which a cross-linked, optically structured liquid crystal monomer or pre-polymer (LCP) with a pre-established orientation pattern is formed. Under observation without additional aids, both the orientation pattern itself and the information written into the cross-linked LCP layer are at first invisible. The layers have a transparent appearance. If the substrate on which the layers are located transmits light, then the LCP orientation pattern or the information which has been written become visible if the optical element is placed between two polarisers. If the birefringent LCP layer is located on a reflecting layer, then the pattern, or the corresponding information, can be made visible using only a single polariser which is held over the element. LPP/LCP authentication elements make it possible to store information, virtually without restriction, in the form of text, images, photographs and combinations thereof. In comparison with prior art authentication elements, the LPP/LCP elements are distinguished in that the authenticity of the security feature can be verified even by a layman since it is not first necessary to learn how to recognise complicated colour changes or kinematic effects. Since LPP/LCP authentication elements are very simple, reliable and quick to read, machine-readable as well as visual information can be combined in the same authentication element.
- However, there remains the risk that, in the course of time, forgers will be able to master this technique.
- In the components described above, one pictorial element is present (whether visible or invisible).
- It would be desirable to improve the security or entertainment value of such a component.
- According to the present invention, an optical component comprises one or more retarder(s) in which are embedded a plurality of images, the images being so arranged that, at any point in the plane of the component, an element of not more than one image is present, each image being associated with a different interaction with polarised light. This association can be achieved in various ways, for example, each image is embedded in patterned retarder(s) (one or more), each of them having patterns with different optical axis.
- The invention also provides a viewing system, comprising a source of polarised light, a component as set forth above, through which the polarised light can travel, and an analyser (in practice, a polarising sheet) for light which has traversed the component, the analyser being rotatable about the axis of the direction of travel of the light. The source of polarised light may be a polarising sheet applied to the surface of the component.
- The different images may be contained in successive parallel stripes, each preferably narrower than the eye can resolve, into which the surface area of the component is divided; if these are n images, any one image will usually be represented on every nth stripe.
- Such an optical component has the surprising property, valuable in the fields of entertainment, document authentication and forgery countermeasures, that simply by rotating a polariser (=the analyser), a plurality of different images, all visible in ordinary light, can be seen one after the other. Previously, it was possible to reveal only one hidden image in this way. However, all the advantages of the “one hidden image” technology, as described for example in EP-A-689065, PCT/IB98/00687 or CH 841/98, can be maintained.
- The invention will now be described by way of example with reference to the accompanying drawings, in which:
- FIG. 1 shows magnified a first optical component according to the invention, manufactured with two retarders, in its appearance when viewed through an analyser in the orientation indicated in the Figure;
- FIG. 2 shows the same component as FIG. 1, in its appearance when viewed through an analyser in the orientation indicated in FIG. 2, and
- FIG. 3 shows the same component as FIG. 1, in its appearance when viewed through an analyser in the orientation indicated in FIG. 3 leading to the ‘negative’ counterpart of the image shown in FIG. 1;
- FIG. 4 shows the same optical component as FIG. 1, in its appearance when viewed through an analyser in the orientation indicated in FIG. 4 leading to the ‘negative’ counterpart of the image shown in FIG. 2;
- FIG. 5 shows a striped photo mask which includes the information of picture I. This striped photo mask is needed for (this example of) the production process of the optical component.
- FIG. 6 shows a striped photo mask which includes the information of a second image, picture II. This photo mask is optional in the production process of the optical component.
- FIG. 7 shows a striped but otherwise completely unpatterned photo mask, in other words including no picture information. This striped photo mask is used in the production process of the optical component.
- FIG. 8 shows a photo mask which reflects picture II. This mask does not include any stripes as shown in FIGS. 5, 6 and7.
- FIG. 9 shows the contrast dependence of each image (here 2 images) related to the analyser angle with respect the optical component. The analyser angle is interrelated to the x-axis (when the analyser is parallel to the x-axis then the angle is 0°). At specific analyser angles peaks of maximum contrasts are reached.
- FIG. 10 shows the contrast dependence of each image (here 2 images) related to the analyser angle in case of a second optical component according to the invention and described in the following Figures, this second optical component being manufactured with 1 retarder. The analyser angle is interrelated to the x-axis (when the analyser is parallel to the x-axis then the angle is 0°). At specific analyser angles peaks of maximum contrasts are reached.
- FIG. 11 shows, magnified, the second optical component in its appearance when viewed through an analyser in the indicated orientation;
- FIG. 12 shows the second optical component in its appearance when viewed through an analyser in the indicated orientation different from FIG. 11;
- FIG. 13 shows a striped photo mask which includes the ‘positive’ (‘positive’ means dark information patterns on bright background) information of picture I of the second optical component.
- FIG. 14 shows a striped photo mask which includes the ‘negative’ (‘negative’ means bright information patterns on dark background) information of picture I.
- FIG. 15 shows a striped photo mask which includes the ‘positive’ information of a second image, picture II.
- FIG. 16 shows a striped photo mask which includes the ‘negative’ information of a second image, picture II. The photo masks of FIGS.13-16 are all needed in this example of the production process of the optical component.
- FIG. 17 shows schematically an optical component according to the invention, working in the reflective mode.
- An optical component according to FIGS. 1, 2,3 and 4 is made by applying a layer of suitable orientable linearly photopolymerisable (LPP) material such as cinnamic acid derivatives or ferulic acid derivatives illustrated for instance in patent publications EP-A-611786, WO 96/10049 and EP-A-763552 to a transparent substrate. This layer with a thickness of about 50 nm is exposed through a photo mask, shown schematically in FIG. 5, to polarised light of different polarisation directions. The photo mask is of alternative adjacent opaque (II) and in-principle-transparent (I) stripes which, when projected onto the layer of LPP material, have a width of ⅛ mm each, which is smaller than the eye can resolve. The stripes (I) are themselves blacked out in parts, to leave the image of an upright cross. The illumination sequence for this first LPP layer is shown in Table 3 with ultimate result shown in Table 1: the angle α of the linear polarised light with a suitable wavelength in respect to the x-Axis travelling through the bright picture areas of stripes I (FIG. 5) is +13.5° (illumination step 1); the picture illustrated in FIG. 5 is an upright cross but any image can be used. Then, this mask is replaced by the photo mask shown in FIG. 7. The opaque stripes (II) of both masks coincide, but the former unexposed areas of stripes I of FIG. 5 will be now exposed at an angle α of −13.5° (illumination step 2); finally this mask is removed and a third illumination step parallel to the x-Axis (α=0°) is applied to expose the stripes II of FIG. 5 (illumination step 3). After these 3 illumination steps all areas of the first LPP layer has been exposed to polarised light of a suitable wavelength. These exposures cause polymerisation, in respectively different preferred alignments.
- Thereafter, this first LPP layer is coated with a cross-linkable liquid crystal monomer or pre-polymer mixture (LCP) which shows birefringence, such as LCP mixture MLCP described in more detail later. (MLCP has an optical anisotropy Δn of 0.13 leading to a film thickness of 1.5 μm). The LCP material adopts the alignment (if any) of the immediately underlying region of the LPP layer. The whole is then exposed to unpolarised (isotropic) light of a suitable wavelength to crosslink the LCP material (illumination step 4 of Table 3).
- Then, a second LPP layer (film thickness about 50 nm) is coated directly on the former LCP layer. Similar to the first LPP layer further 4 exposures (illumination steps 5 to 8 in Table 3) to polarised light of a suitable wavelength are applied to this second LPP layer: the angle α of the linear polarised light in respect to the x-Axis travelling through the bright picture areas of stripes I of the photo mask (FIG. 5) is +31.5° (illumination step 5). Then, this mask is replaced by the photo mask shown in FIG. 7 and the former unexposed areas of stripes I of FIG. 5 will now be exposed at an angle α of −31.5° (illumination step 6). Then, the current (FIG. 7) mask is replaced by the photo mask without any stripes of FIG. 8; the picture II illustrated in FIG. 8 is a diagonal cross but any image can be used. The bright areas of stripes II which were not exposed yet are illuminated with polarised light at an angle α of +45° (illumination step 7). Finally also this mask is removed and all areas which were not exposed before are illuminated by polarised light parallel to the x-Axis (α=0°) (illumination step 8). These exposures cause polymerisation, in respectively different preferred alignments.
- Thereafter, this second LPP layer is coated with a cross-linkable liquid crystal monomer or pre-polymer mixture (LCP) which shows birefringence, such as LCP mixture MLCP (MLCP has an optical anisotropy Δn of 0.13 leading to a film thickness of 1.5 μm). Again, the LCP material adopts the alignment (if any) of the immediately underlying region of the LPP layer. The whole is then exposed to unpolarised (no mask necessary) light of a suitable wavelength to crosslink the LCP material (illumination step 9).
- The various retarder layers may have the same (as here) or different optical retardations Δnd.
- This completes the manufacture of the optical component, which in normal light is transparent.
- In use, the optical component will be examined for authenticity in the following way.
- It is placed on a light box emitting linearly polarized light, and appears transparent in transmission.
- To check it, it is viewed through a rotatable sheet carrying a polarizing grating; such sheets are known as analysers.
- In summary, because of the different modes of interaction of the two images with polarised light, as the analyzer is rotated, the upright cross (stripes I, FIG. 1) appears and disappears, to be replaced by the diagonal cross (stripes II, FIG. 2), which also disappears on continued rotation of the analyzer. It is easy to verify whether or not a document of unknown authenticity displays two different images when inspected this way. The dependence of the contrast on the analyser angle is also represented in FIG. 9.
- In more specific detail, the appearance of images depends on various angles and retardation's as set forth in the following tables, in which the symbols have the following meaning:
- δ1 Optical axis of first LCP layer;
- δ2 Optical axis of second LCP layer;
- x-axis: Axis of polarising grating of inspection arrangement; α=0° means parallel to the x-Axis
- x, y: colour co-ordinates indicate the position in the Chromaticity Diagram; for example, stripes I in FIG. 2 appear grey to brownish; the colour co-ordinates of these stripes are calculated as x=0.3684 and y=0.3609 leading to such a slightly coloured appearance described as brownish.
- normed brightness: 1.000=brightness of inspection light as viewed through polarisers and analyser arranged parallel, no retarder present.
- Δnd1, Δnd2 Optical retardations of the LCP layers (Δnd1=Δnd2=0.2 μm)
- d1, d2: Thickness of LCP retarder layers (d1=d2=1.5 μm).
- Table 2 shows calculated values of the feasible contrast ratios and colours which can be achieved with the optical component described in Example 1.
- In another example according to the invention, it is possible to make a similar secure component with only one retarder layer. This component is examined for authenticity by the procedure already described. Upon rotating the analyser, peaks of maximum contrast are obtained at specific rotation angles, at each of which a respective one of the (otherwise hidden) images becomes visible (FIG. 10).
- An optical component according to FIGS. 11 and 12 (their ‘negative’ counterparts are not shown here, but appear—similar to Example 1—when the analyser angle to the x-axis is 0° and −45°, respectively) is made by applying a layer of suitable orientable linearly photo-polymerisable (LPP) material such as cinnamic acid derivatives or ferulic acid derivatives illustrated for instance in patent publications EP 611786, WO 96/10049 and EP 763552 to a transparent substrate. This layer with a thickness of about 50 nm is exposed through a photo mask, shown schematically in FIG. 13, to polarised light of different polarisation directions. The photo mask is of alternative adjacent opaque (II) and in-principle-transparent (I) stripes which, when projected onto the layer of LPP material, have a width of ⅛ mm each which is smaller than the eye can resolve (same resolutions show masks illustrated in FIGS. 14, 15 and16). The stripes (I) are themselves blacked out in parts, to leave the image of a character ‘3’. The illumination sequence for this LPP layer is: the angle α of the linear polarised light with a suitable wavelength in respect to the x-axis travelling through the bright picture areas of stripes I (FIG. 13) is +45° (illumination step 1); the picture illustrated in FIG. 13 is a character ‘3’ but any image can be used. Then, this mask is replaced by the photo mask shown in FIG. 14. This mask is—except the opaque stripes II—exactly the ‘negative’ counterpart of the mask shown in FIG. 13. The opaque stripes (II) of both masks coincide, but the former unexposed areas of stripes I of FIG. 13 will be now exposed at an angle α of 0° (illumination step 2); then a third mask (FIG. 15) is applied including the image information of picture II; the picture illustrated in FIG. 15 is a character ‘4’, but any image can be used. The angle α of the linear polarised light in respect to the x-axis travelling through the bright picture areas of stripes II of the photo mask (FIG. 15) is +22.5° (illumination step 3). Then, this mask is replaced by the photo mask shown in FIG. 16 and the former unexposed areas of stripes II of FIG. 15 will now be exposed at an angle α of +67.5° (illumination step 4). These exposures cause polymerisation, in respectively different preferred alignments.
- Thereafter, this LPP layer is coated with, a cross-linkable liquid crystal monomer or pre-polymer mixture (LCP) which shows birefringence, such as mixture MLCP (MLCP has an optical anisotropy Δn of 0.13 leading to a film thickness of 1.5 μm). The LCP material adopts the alignment (if any) of the immediately underlying region of the LPP layer. The whole is then exposed to unpolarised (no mask necessary) light of a suitable wavelength to crosslink the LCP material (illumination step 5).
- This completes the manufacture of the optical component, which in normal light is transparent.
- In use, the optical component will be examined for authenticity in the following way.
- It is placed on a light box emitting linearly polarised light, and appears transparent in transmission.
- To check it, it is viewed through a rotatable sheet carrying a polarising grating; such sheets are known as analysers.
- In summary, because of the different modes of interaction of the various images patterns with polarised light, as the analyser is rotated, the character ‘3’, (stripes I, FIG. 13) appears and disappears, to be replaced by the character ‘4’ (stripes II, FIG. 14), which also disappears on continued rotation of the analyser. It is easy to verify whether or not a document of unknown authenticity displays two different images when inspected this way.
- When placing or attaching the optical components described in Examples 1 and 2 on top of a reflector which maintains the polarisation direction of incident light, and when using a polariser which is rotatable about the axis of the direction of travel of the light which has traversed the polariser and the optical component, such light is reflected at said reflector and traverses a second time the optical component and said polariser (schematically shown in FIG. 17). Then similar images as seen in the transmissive mode illustrated in Example 1 and 2 are observed: by rotating said polarizer, peaks of maximum contrasts for each image are obtained at specific rotation angles of the polarizer, enabling, at each such angle, visualisation of a respective image not otherwise visible; the image appears bluish/white or violet/whitish with relative poor contrasts because the optical retardations and its optical axis were not optimised for the reflective operation mode.
- The production of a PPN (=LPP) and LCP layer which can be used according to the invention will be described still by way of example, in more detail below.
- 1. Production of a PPN Layer
-
- A glass plate was spin-coated with a 2 percent strength solution of the PPN material in cyclopentanone for one minute at 2000 rpm. The layer was then dried for 5 to 10 minutes at 120° C. on a hotplate. The layer was then exposed to linearly polarized light, Hg high-pressure lamp for 20 to 405 seconds (depending on the strength of the lamp and on the number of LPP/LCP layers of the optical component) at room temperature. The layer was then used as an orientation layer for liquid crystals.
- 2. Mixture MLCP of Cross-Linkable LC Monomers for the LCP Layer.
-
- Using these components, a supercoolable nematic mixture MLCP with particularly low melting point (Tm ˜35° C.) was developed, making it possible to prepare the LCP layer at room temperature.
- The diacrylate monomers were present with the following composition in the mixture:
- Mon180%
- Mon215%
- Mon25%
- In addition a further 2% of the Ciba-Geigy photoinitiator IRGACURE (trade mark) was added to the mixture.
- The mixture MLCP was then dissolved in anisol. By means of the MLCP concentration in anisol, it was possible to adjust the LCP layer thickness over a wide range. Especially for the examples of optical components described in this patent, desired retardations Δnd of 0.2 μm could be achieved.
- For photoinitiated cross-linking of the LC monomers, the layers were exposed to isotropic light from a xenon lamp for about 5 to 30 minutes (depending on the strength of the lamp) in an inert atmosphere.
- The optical effects described above, as well as the corresponding layer structures and material compositions, represent no more than a choice from many possibilities according to the invention, and may in particular be combined in a wide variety of ways in order to develop authenticating elements.
- Thus, it is of course possible for any other kind of birefringent layer than the LCP layer described to be used to produce an optical effect that can be employed in optical components, for example for authentication elements.
- It is furthermore possible for the examples described above, to use not a PPN orientation layer but a different orientation layer which, according to the desired optical property and resolution, has the same or similar properties to a PPN layer. It is also conceivable to produce the orientation required for a retarder layer using a correspondingly structured substrate. A structured substrate of this type can for example, be produced by embossing, etching and scratching.
TABLE 1 Arrangement of the optical axis of the LCP layers and optical appearance of the optical element. Optical Retardations Δnd, and Δnd2 of the LCP-Retarder Layers Δnd1 and Δnd2 = 0.2 μm Angle of x axis to polariser 0° 0° 0° 0° Angle of x axis to analyser 45° 45° 90° 90° Angle of x axis to δ1 +13.5° 0° +13.5° 0° Angle of x axis to δ2 +31.5° +45° +31.5° +45° Normed brightness 0.9925 0.5000 0.4859 0.8104 Colour co-ordinates x 0.3343 0.3334 0.3684 0.3062 y 0.3355 0.3333 0.3609 0.3186 Colour white white whitish/brownish white Appearance of the pixel BRIGHT GREY GREYISH BRIGHT Angle of x axis to polariser 0° 0° 0° 0° Angle of x axis to analyser 45° 45° 90° 90° Angle of x axis to δ1 −13.5° 0° −13.5° 0° Angle of x axis to δ2 −31.5° 0° −31.5° 0° Normed brightness 0.0052 0.5000 0.5000 0.0000 Colour co-ordinates x 0.2669 0.3334 0.3684 0.3334 y 0.1539 0.3333 0.3603 0.3333 Colour ca. violet white whitish/brownish white Appearance of the pixel DARK GREY GREYISH DARK -
TABLE 2 Contrasts overall effect overall effect Point on image BRIGHT GREY BRIGHT GREY BRIGHT BRIGHT Colour white white ˜white whitish/brownish white ˜whitish Normed brightness 0.993 0.500 0.747 0.486 0.810 0.648 Point on image DARK GREY DARK GREY DARK DARK Colour ca. violet white ˜dark violet whitish/brownish white ˜black Normed brightness 0.005 0.500 0.253 0.500 0.000 0.250 Maximum contrast 199:1 1:1 3:1 1:1 >200:1 2.6:1 -
Claims (12)
1. An optical component, comprising one or more retarder(s) in which is/are embedded a plurality of images, the images being so arranged that, at any point in the plane of the component, an element of not more than one image is present, each image being associated with a different interaction with polarised light.
2. An optical component according to claim 1 , wherein there is a plurality of retarders in which the images are embedded, the retarders having the same or different retardation values Δnd.
3. An optical component, according to claim 1 or 2, wherein the images are embedded in one or more retarder(s) having specific image patterns each having a different optical axis from the other specific image patterns.
4. An optical component according to any preceding claim, wherein the respective images are contained in alternate areas.
5. An optical component according to any preceding claim, wherein the respective images are contained in successive optionally parallel stripes.
6. An optical component according to claim 4 or 5, wherein the areas or stripes are smaller or narrower than the eye can resolve enabling an optical component wherein one or more image(s) is/are (a) photographic image(s).
7. An optical component according to claim 4 , 5 or 6, wherein there are n mages, each respectively being represented on every nth stripe or nth area.
8. Element for protection against forgery and/or copying, characterized by an optical component according to any one preceedingd claims.
9. A viewing system, comprising a source of polarised light, an optical component according to any preceding claim, through which component the polarised light can travel, and an analyser for light which has traversed the optical component, the analyser being rotatable about the axis of the direction of travel of the light; whereby, by rotating the analyser, peaks of maximum contrasts for each image are obtained at specific rotation angles of the analyser, enabling, at each such angle, visualisation of a respective image not otherwise visible.
10. A system according to claim 8 , wherein the source of polarised light is a polarising sheet applied to the surface of the component.
11. A system accorded to claim 9 or 10, wherein the analyser is a polarising sheet.
12. A viewing system, comprising a reflector which maintains the polarisation direction of incident light, an optical element according to claims 1 to 7 attached to said reflector, and a polariser which is rotatable about the axis of the direction of travel of the light, such that light which has traversed the polariser and the optical component is reflected at said reflector and traverses a second time the optical component and said polariser; whereby, by rotating said polariser, peaks of maximum contrasts for each image are obtained at specific rotation angles of the polariser, enabling, at each such angle, visualisation of a respective image not otherwise visible.