CN101201107B - Gasket material - Google Patents
Gasket material Download PDFInfo
- Publication number
- CN101201107B CN101201107B CN2007101610993A CN200710161099A CN101201107B CN 101201107 B CN101201107 B CN 101201107B CN 2007101610993 A CN2007101610993 A CN 2007101610993A CN 200710161099 A CN200710161099 A CN 200710161099A CN 101201107 B CN101201107 B CN 101201107B
- Authority
- CN
- China
- Prior art keywords
- joint fastener
- pad
- composition
- gasket material
- sample
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A gasket material which is comprised of a joint sheet which has a surface layer (1a), a back layer (1b) and an intermediate layer (1c), the layers being different from one another with respect to a reinforcing fiber or a filler, characterized in that the reinforcing fiber comprises an organic fiber and/or an inorganic fiber containing no asbestos and has a fibril form, and the filler comprises an inorganic filler in a needle form in an amount of 10 to 45 wt %. The gasket material comprised of the joint sheet (1) can provide a gasket being free from cracking or breaking owing to the fletting thereof.
Description
The application is to be on April 30th, 2003 applying date, and application number is 03815974.0, and denomination of invention is divided an application for " gasket material ".
Technical field
The invention relates to a kind of gasket material, be engine and the transmission device that is used for automobile and drill autofeeder etc., and particularly relevant for a kind of gasket material, it is by a joint fastener (jointsheet) manufacturing, wherein make a composition of this joint fastener, be by mixing and kneading one rubber, a reinforced fiber and a stuffing, the sheet of pressurizeing then, and add this composition gained of sulphur hermo-hardening.The present invention also relates to a kind of pad of planting the gasket material manufacturing thus.
Background technique
Up to the present, so-called asbestos joint fastener is often used as the material into the pad of the periphery of the engine of institute's loads such as drill autofeeder.This kind joint fastener is by combining the asbestos manufacturing with phenolic resin with nitrile rubber (nitrilerubber), and forms the sheet material.
Yet in recent years, because the influence of its surrounding enviroment, it is quite complicated that the control of this kind asbestos joint fastener becomes, so the present invention promptly proposes a kind of joint fastener, and it uses another kind of lamination coating to replace asbestos.Result of the present invention is published in by name " exploitation of non-asbestos washer material " in the paper of (Develo μ mentof non-asbestos gasket material), it is contained in a meeting record of a speech meeting, by Society of Automotive Engineers of Japan, Inc. published in May, 1992.
As shown in figure 14, pass through the method, when a pad is used to a structure, for example say, between a transmission device chest H who is connected to an engine, and a pad that is connected to by screw B between the lid C of chest H embeds the position, this main body wherein, by activating repeatedly and stopping engine or the like, and having a temperature change on a large scale, this temperature variation repeatedly is shown in an arrow among Figure 15, by the wall-attached surface between chest H, and the wearing and tearing that the relative displacement repeatedly between the pad G is caused produce.And because the weight reduction of drill autofeeder in recent years, its structure for example says that chest H and lid C develop towards low flintiness, so produces this kind friction by the external force that acts on lid C etc.
Yet this kind comprises with the joint fastener of asbestos seat as a reinforced fiber having a low stretching resistance, particularly, and the joint fastener of thickness 0.5mm commonly used, and do not have joint fastener to have high tensile power as yet above being developed more than the 40Mpa.Therefore, if a pad is manufactured as material with this kind joint fastener, and be used to the periphery etc. of engine, pad G is then from its home position, because the wearing and tearing shown in arrow among Figure 15, and be offset.And under the worst situation, the fracture of pad and the problem of damage can take place, and leak and make sealing substance produce.
Therefore known solution is, by reducing fracture and the damage of wearing and tearing to avoid pad, be by seeing through the number of the retaining screw that increases structure, or the flintiness of increase lid etc., to increase fixed surface pressure, or by register pin, the wall-attached surface that embeds the position at the structure pad provides meshing engagement structure.
Yet, these solutions, for example say, through increasing structure retaining screw number, increase fixed surface pressure and wear and tear, or pass through or increase lid flintiness etc. to reduce, or provide meshing engagement structure embeds the position in the pad of structure wall-attached surface etc. by register pin, consequently, owing to the complicated cost increase that causes structure of fixed structure, and owing to the increase of accessory number increases structure weight with the accessory volume.
In addition, in existing joint fastener, the adhesive force difference between front surface and rear surface is small.Therefore, that is to say as shown in figure 15, if the pad with existing joint fastener material manufacturing is used in engine periphery etc., the problem that can produce is that pad G is with respect to structure, for example say chest H and lid C etc., between the surface of the two, because above-mentioned wearing and tearing F can produce a slip S, when slip S takes place, the frictional force that pad G can pass through from its home position to be produced is offset, and position P embeds the outstanding thereby generation in position from pad.Therefore, as Figure 16 and shown in Figure 17, leakage efficiency thereby minimizing.
Therefore, the minimizing of the known gasket seal effect of trying to avoid with following solution:
1) see through the number that increases the structure retaining screw, or the flintiness of increase lid etc., fixed surface pressure increased, to reduce wear extent;
2) by increasing the pad mechanical strength, the wear-resistant strength of improvement pad;
3) by register pin, the wall-attached surface that embeds the position at the structure pad provides meshing engagement structure, to reduce wear extent;
4) through applying a solid lubricant, for example say graphite or molybdenum disulfide,, cause the power of pads placement skew with minimizing by reducing friction to gasket surface.
Yet, these solutions, for example say, seeing through increases structure retaining screw number, increase fixed surface pressure reducing wearing and tearing, or by or increase lid flintiness etc., the problem that is caused is, owing to the complicated cost increase that causes structure of fixed structure, and owing to the increase of accessory number increases structure weight with the accessory volume.And increase the solution of pad mechanical strength, and its problem is, joint fastener and pad hardening, so decrement tails off, and cause sealing effect relatively to become damnable.
In addition, by register pin, the wall-attached surface that embeds the position at the structure pad provides meshing engagement structure, solution, its problem is, owing to the complicated cost of structure that causes of fixed structure increases, and because the accessory number increases and the accessory volume increases structure weight.See through and to apply a solid lubricant, for example say graphite or molybdenum disulfide to gasket surface, solution, its problem is, having increased wear extent and quicken pad distortion and have low intensive generation, is owing to by this solid lubricant, make that the slip between pad and lid etc. becomes greatly.
In addition, as mentioned above, existing joint fastener comprises the joint fastener with asbestos reinforced fiber, has low-tension intensity (stretching resistance).Therefore,, and be used to the periphery etc. of engine if a pad is manufactured as material with existing joint fastener, the skew that then is worn of this pad from its home position, and, and make sealing substance produce leakage because surface pressure reduces.
Therefore, below variously be studied all in order to improve the joint fastener potency method, but all these methods and abundant inadequately.That is to say, by increasing reinforced fiber composition amount, or by increasing the length of staple of reinforced fiber, with practice improvement gasket strength and increase a method of monophorogy effect, but the problem of these methods is, cause the pad cost of material to improve, and owing to the deterioration of gasket surface flatness reduces leakage efficiency.
Other method is, manage to increase pad density, thereby the roll extrusion power when strengthen forming the thin slice joint fastener, and the improvement gasket strength, therefore and by improving the hot rolling wheel temperature when forming the thin slice joint fastener, promote the curing of joint fastener, and the improvement gasket strength increases the solidifying temperature of forming rubber material for some reason.Yet, as shown in figure 18, the problem of these methods is, when joint fastener intensity is increased to a certain degree, pad hardness is too high, make the endurance of the stress that the pad opposing is compressed repeatedly reduce, and under the worst situation, produce the deformation fatigue of pad, that is to say as shown in figure 18, because the edge that compression is damaged is outstanding, causes the permanent compression set of pad, and make the leakage efficiency thereby the minimizing of pad.
In addition, other method is, by when mixing the joint fastener raw material, reduce rubber material composition rate, increase gasket strength with the practice, thus joint fastener become harder, or when mixing the rubber material of joint fastener, (nitrile butadiene rubber, NBR) ratio of Xi Lie acrylonitrile (acrylic nitrile) is to surpassing 40% by increasing nitrile butadiene rubber.Yet, the problem that these methods also have is, the elasticity of joint fastener has reduced, and work as stress by the wearing and tearing under the effect of surface pressure, act directly on the extruding of pad, a big deformation quantity that is to say, a permanent compression set that causes thickness to reduce has produced, thereby causes gasket seal efficient to reduce.
In addition, for example say, as shown in figure 20, when a pad is used to a structure, for example say between a transmission device chest H who links with an engine, and a pad that is connected to by screw B between the lid C of chest H embeds the position, and wherein this main body is by activating repeatedly and stopping engine etc. and have a temperature change on a large scale.Between the wall-attached surface of chest H, and the relative displacement between the pad G, by caused temperature change is repeatedly produced as arrow D.On the other hand, be present in its surface, make to have high friction impedance as the pad of original material manufacturing, so being difficult to of becoming of this pad slides with this joint fastener because this rubber is formed.
Therefore, before this, when with the pad of this joint fastener as the original material manufacturing, being used to the engine periphery, similarly is transmission device etc., and its problem is that an abrading section W results from two surfaces of pad, is to be produced because of the slip by above-mentioned relative displacement.
Therefore, in order to solve the pad wear problems, the known practice with the amount of reducing wear, is to reach according to making gasket surface have a low friction with following solution.Has three-decker in manufacturing, comprise a front surface layer 1a, a rear surface layer 1b, and the mesosphere between this two surface layer, joint fastener 1 dull and stereotyped the time, one solid lubricant, for example say that fluorocarbon resin, molybdenum disulfide, mica etc. are added in the raw material of front surface layer 1a, and as shown in figure 21, this raw material is spread out.To reduce the composition ratio of joint fastener 1 rubber material own.Have three-decker, comprising a front surface layer 1a, a rear surface layer 1b, and the mesosphere between this two surface layer, the front surface layer 1a of joint fastener 1, a solid lubricant is for example said powdered graphite, or the molybdenum disulfide powder, as shown in figure 22, be applied in by method of deploying etc.
Yet, these solutions still have following problem, that is to say, solid lubricant in those solutions, for example say that fluorocarbon resin, molybdenum disulfide, mica etc. are added in the raw material of front surface layer 1a, and in raw material, be spread out and since the composition of solid lubricant on be limited to sufficiently, be the decline that is difficult to obtain friction factor, so the minimizing of wear extent is insufficient.In addition, reduce the solution of the composition ratio of joint fastener 1 rubber material own,, can't reduce the composition of rubber material, to obtaining enough friction factor owing to dull and stereotyped restriction of creating conditions.And, the solution of solid lubricant, for example say powdered graphite, or the molybdenum disulfide powder is applied to surface layer, to make a low-friction coating 2 of solid lubricant, the problem that has is that an electrical corrosion location EC can pass through pad, result from, be relevant to the maybe material pad Embedded Division position of this kind sealing substance of chest H and lid C.
Summary of the invention
A purpose of the present invention is to propose a gasket material to solve the above problems effectively.In first viewpoint of the present invention, one gasket material is by a joint fastener manufacturing, wherein makes a composition of this joint fastener, is by mixing and kneading one rubber, a reinforced fiber and a stuffing, the sheet of pressurizeing then, and add this composition gained of sulphur hermo-hardening.This gasket material comprises a reinforced fiber, this reinforced fiber is a kind of fiber tuft, at least formed by the inorfil one of them or the two of organic fiber and non-asbestos, an and stuffing, wherein the part of this stuffing is a needle inorganic fiber at least, and the composition of this needle inorganic fiber at 10wt% between the 45wt%.
According to gasket material of the present invention, this reinforced fiber is a kind of fiber tuft (a tiny chemical fibre dimension), formed (replacing asbestos) by organic fiber and non-asbestos type inorfil one of them or the two with inorfil, and the stuffing of at least one part is the needle inorganic fiber, and it consists of 10wt% to 45wt%.The stretching resistance of this joint fastener thereby increase are the interaction effects of tieing up by the tiny chemical fibre that organic fiber and inorfil are formed, and the effect that adds of tiny chemical fibre dimension and needle inorganic fiber.Therefore,, for example say between chest and the lid, then because pad from the skew in its home position, causes the generation of pad fracture damage to be avoided if wearing and tearing betide a structure.
In gasket material of the present invention, preferably add 2wt% to the phenol antioxidant of 26wt% in raw material.Because 2wt% to this phenol antioxidant of 26wt% give this joint fastener raw material enough stick efficient, when formerly expecting by adding, a hot rolling wheel that comprises the press polish wheel (calender roll) of a pair of hot rolling wheel and cold breakdown pinch roller, with compression and this raw material of sheet when forming this joint fastener, the sheet of composition can be stably obtained, and do not have the situation generation that raw material is adsorbed in the cold breakdown pinch roller.
In addition, in pad sample of the present invention, preferably, by what formed as the aramid fibre (aramid fiber) of reinforced fiber, have the basis of phenol antioxidant raw material, surpassing 15wt% is preferably.As the nitrile butadiene rubber (NBR) of rubber material, be for 10wt% arrives 30wt%, phenol antioxidant is for 2wt% arrives 26wt%, and hydrated magnesium silicate is as the needle inorganic fiber, and leftovers is the inorganic fillings as the stuffing material.According to these compositions, as described below, this joint fastener that 0.5mm is thick can have the stretching resistance above 45MPa, generally can be used as pad.
In addition, in gasket material of the present invention, preferably, it is that 40 μ m are to 200 μ m that this needle inorganic fiber has the particle main shaft.Particle with this main shaft value provides a suitable formability, and the joint fastener that can obtain to have abundant stretching resistance.
In second viewpoint of the present invention, a gasket material is by a joint fastener manufacturing, wherein makes the composition of this joint fastener, is by mixing and kneading rubber, reinforced fiber and stuffing, the sheet of pressurizeing then, and add this composition gained of sulphur hermo-hardening.This gasket material wherein two outermost surfaces one of them, be formed a non-associated layer, and another is formed the associated layer with strong attaching power with weak attaching power.
According to gasket material of the present invention, comprise this gasket material two outermost surfaces one of them, be formed a non-associated layer, and another is formed the associated layer with strong attaching power with weak attaching power.Therefore, though wearing and tearing are if betide a structure, for example say between chest and the lid, be formed because attach the associated layer of the pad of this pad to the structure from gasket material, and it is maintained the home position, therefore, non-associated layer is by a less friction, give pad with respect to structure one slip S, make because pad from the displacement in its home position, causes the generation of leakage efficiency minimizing to be avoided.
In addition, in gasket material of the present invention, preferably, the attaching power of associated layer wherein is at least more than 5 times of attaching power of non-associated layer, and the attaching power of associated layer, and being at least more than the 2.5MPa is preferably.If the attaching power of associated layer, above more than 5 times of attaching power of non-associated layer, and the attaching power of associated layer, surpass more than the 2.5MPa, as described below, the sufficient sealing endurance of pad opposing wearing and tearing will be obtained.
In addition, in gasket material of the present invention, preferably, the composition of associated layer comprises the calcium carbonate of 2wt% to coumarone-polyenoid resin (coumarone indene resin) of 15wt%, 5wt% to 60wt%, the 10wt% nitrile butadiene rubber (NBR) to 25wt%.And, comprise total composition of these compositions of the layer of these compositions being equal to or less than 100wt%.As described below, according to these compositions, the attaching power of associated layer can surpass more than 5 times of attaching power of non-associated layer, and the attaching power of associated layer, can surpass more than the 2.5MPa, and therefore, the sufficient sealing endurance of pad opposing wearing and tearing will be obtained.
In addition, in the 3rd viewpoint of the present invention, a gasket material is by a joint fastener manufacturing, wherein makes the composition of this joint fastener, is by mixing and kneading rubber, reinforced fiber and stuffing, the sheet of pressurizeing then, and add this composition gained of sulphur hermo-hardening.This gasket material comprises an aramid fibre, as a reinforced fiber, form and surpass 20wt%, a rubber material, composition 23wt% between the 30wt%, barium monosulfide, as a stuffing, composition is a remaining material, as a material of this stuffing between 7% to 30% and an inorganic fillings.
According to gasket material of the present invention, when the composition of aramid fibre surpasses 20wt%, and the composition of barium sulphide is when 7wt% is between 30vt%, can be by keeping the high flexibility of joint fastener, to strengthen the intensity of joint fastener.Therefore,, for example say between chest and the lid, then because pad from the skew in its home position, causes the generation of pad fracture damage to be avoided if wearing and tearing betide a structure.
In addition, this gasket material is strengthened the practice of intensity, neither increases the combining proportion of reinforced fiber, do not increase the length of staple of reinforced fiber yet, therefore the cost of material that can keep pad is at lower cost, and can be so that the having an even surface of pad, and leakage efficiency is increased fully.And this joint fastener is strengthened the practice of intensity, and the roll extrusion power the when rete that neither is increased in joint fastener forms does not increase the temperature of hot rolling wheel yet, therefore can keep the low hardness of joint fastener and obtain the endurance of pad, with the opposing stress of compression repeatedly.Therefore, because deformation fatigue causes weakening of gasket seal effect, can be avoided.
In addition, this gasket material is strengthened the practice of intensity, neither reduces the ratio of mixture of rubber material in joint fastener is formed, and does not also increase the ratio of acrylonitrile composition in the nitrile butadiene rubber (NBR), therefore, can keep the high flexibility of joint fastener.Therefore, because the gasket seal effect that a large amount of wearing and tearing caused of pad weakens, under the influence of surface pressure, resist the stress of the direction of extrusion, and can be avoided by these wearing and tearing.
In addition, in gasket material of the present invention, the specific surface area of aramid fibre is preferably for surpassing 6m2/g.If represent the specific surface area of aramid fibre of the degree of fiber bunchy is 6m2/g, then the tension strength of joint fastener and pad and deformation fatigue surface pressure can be increased fully.
In addition, in gasket material of the present invention, the mean particle diameter of barium sulphide is preferably below 3 μ m.Be used if mean particle diameter is the barium sulphide powder of 3 μ m, therefore the tired surface pressure of the deformation of joint fastener and pad can increase.
In addition, in the 4th viewpoint of the present invention, a gasket material is by a joint fastener manufacturing, wherein makes the composition of this joint fastener, is by mixing and kneading rubber, reinforced fiber and stuffing, the sheet of pressurizeing then, and add this composition gained of sulphur hermo-hardening.This gasket material comprises a low friction coating layer, is by applying a low friction treatment liquid, be formed on a single face or the two sides of a joint fastener, wherein should comprising a teflon by low friction treatment liquid.
According to gasket material of the present invention, wherein, be formed on the single face or the two sides of a joint fastener by applying the low friction treatment liquid that comprises teflon, can be so that gasket surface obtains enough low coefficient of friction.Therefore,, for example say between chest and the lid, then because pad from the skew in its home position, causes the generation of pad fracture damage to be avoided if wearing and tearing betide a structure.For the relative displacement between the wall-attached surface of chest H or lid C etc. and pad G, the wearing and tearing on the surface of pad G that produces, if this pad G is by gasket material manufacturing of the present invention, then the wearing and tearing on the surface of pad G can be avoided.And the leakage efficiency of pad, the pad compared to existing joint fastener manufacturing can improve significantly.
In addition, in gasket material of the present invention, should hang down friction treatment liquid, preferably, by mixing a concentration is the emulsion of 30wt% to this teflon of 85wt%, with phenolic resin colloidal sol (the resol of phenol resin) manufacturing of 15wt% to 70wt%, wherein this total weight percent maintains 100wt%.According to the composition of this treatment fluid, when the number of occurrence of sliding increased, the low coefficient of friction of pad can be kept.And because the surface of joint fastener, be by (polytetrafluoroethylene PTFE) covers, so the absorption aqueous vapor of joint fastener, with the corrosion of chest H and lid C etc., can be avoided by the teflon of phenolic resin institute bond constraint.
In addition, in gasket material of the present invention, it is preferable that the thickness of this coating surpasses 3 μ m.Therefore, if the thickness of this coating surpasses 3 μ m, though then this coating is worn gradually, the low coefficient of friction of pad still can be kept segment length's time.
Description of drawings
Fig. 1 is a sectional drawing, illustrates the gasket material of a joint fastener, is the embodiment 1 according to first viewpoint of the invention described above, and the embodiment 2 of second viewpoint of the invention described above.
Fig. 2 is the icon of the stretching resistance of joint fastener, illustrates a gasket material of the above embodiments 1, with existing non-asbestos pad and the existing contrast that contains the pad of asbestos;
Fig. 3 is a sectional drawing, illustrates the pad of embodiment 2 gasket material manufacturing, wear-resistant effect;
Fig. 4 is a sectional drawing, illustrates a joint fastener, is the gasket material according to the embodiment 3 of the 3rd viewpoint of the invention described above;
Fig. 5 is the icon of the stretching resistance of joint fastener, illustrates a gasket material of the above embodiments 3, with the comparison of the available pad of existing commerce;
Fig. 6 is the icon of the tired surface pressure of deformation of joint fastener, illustrates a gasket material of the above embodiments 3, with the comparison of the available pad of existing commerce;
Fig. 7 is the icon of the limit sealing load of joint fastener, illustrates a gasket material of the above embodiments 3, with the comparison of the available pad of existing commerce;
Fig. 8 is a correlogram, illustrates the particle diameter of the barium sulphide of the composition that is binding on joint fastener among the embodiment 3, with the relation of tired surface pressure of the deformation of joint fastener and limit sealing load;
Fig. 9 is a correlogram, illustrates the specific surface area of the aramid fibre of the composition that is binding on joint fastener among the embodiment 3, with tension strength, and the relation of the tired surface pressure of the deformation of joint fastener;
Figure 10 is a sectional drawing, illustrates a joint fastener, is the gasket material according to the embodiment 4 of the 4th viewpoint of the invention described above;
Figure 11 is a correlogram, illustrates the sample and the comparative sample of the above embodiments 4, the result of the test of sliding;
Figure 12 is a correlogram, illustrates the sample and the comparative sample of the above embodiments 4, for the result of sticking ionization meter of lid;
Figure 13 is a correlogram, illustrates the sample and the comparative sample of the above embodiments 4, and the weight that absorbs aqueous vapor increases the measurement result of ratio;
Figure 14 is a sectional drawing, illustrates the chest that is embedded in a transmission device and the pad between the lid;
Figure 15 is a sectional drawing, illustrates the pad of the available gasket material manufacturing of existing commerce, wear-resistant effect;
Figure 16 is a sectional drawing, and it is outstanding owing to what displacement caused to illustrate existing pad;
Figure 17 is a planimetric map, and it is outstanding owing to what displacement caused to illustrate existing pad;
Figure 18 is a correlogram, illustrates existing joint fastener, the relation between tension strength and the tired surface pressure of deformation;
Figure 19 is a correlogram, illustrates existing joint fastener, the relation between tension strength and limit sealing load;
Figure 20 is a sectional drawing, illustrates the chest that is embedded in a transmission device and the pad between the lid;
Figure 21 is a sectional drawing, illustrates an embodiment of the gasket surface with low coefficient of friction; And
Figure 22 is a sectional drawing, illustrates another embodiment of the gasket surface with low coefficient of friction.
[graphic description of symbols]:
1: joint fastener
1a: front surface layer 1a
1b: rear surface layer
1c: mesosphere
1e: main stor(e)y
1f: surface layer
3: low friction coating
C: lid
F: wearing and tearing
H: chest
G: pad
S: slide
Embodiment
For above and other objects of the present invention, feature and advantage can be become apparent, a preferred embodiment cited below particularly, and cooperate appended graphicly, be described in detail below: below, one embodiment of the invention will be narrated according to its relevant icon.
Fig. 1 illustrates the gasket material of a joint fastener, is the embodiment 1 according to first viewpoint of the invention described above.Numeral 1 expression one joint fastener is the gasket material of present embodiment.Joint fastener 1 has three-decker, comprises a front surface layer 1a, a rear surface layer 1b, and the mesosphere 1c between front surface and rear surface layer.
Embodiment 1 joint fastener 1 is formed by following processing procedure.At first, one composition material is manufactured to come out, be (for example to say by mixed rubber, nitrile butadiene rubber (nitrile butadiene rubber, NBR)), the tinyization reinforced fiber (fiber of fiber fasciculation, for example say, as the aramid fibre (aramid fiber) of an organic fiber), glass fibre (as an inorfil to replace asbestos), needle inorganic stuffing, and other stuffing manufacturings such as (for example saying barium sulphide).Then, this composition material is added into, and comprises a hot rolling wheel of the press polish wheel (calender roll) of a pair roller (hot rolling wheel and cold breakdown pinch roller), by the kneading and the extruding of those rollers, with the composition that forms a thin slice on hot rolling wheel.Then, by using the temperature of hot rolling wheel, add the sulphur hermo-hardening and solidify this composition, to form a joint fastener.Then, by separating, to form this joint fastener with hot rolling wheel.As shown in Figure 1, in this processing procedure, three layers front surface layer 1a of above-mentioned joint fastener 1, rear surface layer 1b and mesosphere 1c, mainly be formed (, see also aforesaid paper " Develo μ ment ofnon-asbestos gasket material ") as for the more detailed content of this processing procedure by the composition amount that changes reinforced fiber.
In embodiment 1 joint fastener, by what formed, have the basis of phenol antioxidant composition as the fiber fasciculation aramid fibre of reinforced fiber, surpassing 15wt% is preferably.As the nitrile butadiene rubber (NBR) of rubber material, be to arrive 30wt% for 10wt%.Phenol antioxidant is for 2wt% arrives 26wt%, and hydrated magnesium silicate is as the needle inorganic fiber, and leftovers is the inorganic fillings as the stuffing material.
In this joint fastener, for hydrated magnesium silicate, it is that 40 μ m are used to 200 μ m that an acicular crystal material has a particle main shaft.Particle with this scope main shaft value provides a suitable formability, and can obtain sufficient joint fastener stretching resistance.
Fig. 2 is the icon of the stretching resistance of joint fastener, illustrates a gasket material of the above embodiments 1, with existing non-asbestos pad and the existing contrast that contains the pad of asbestos.
As shown in Figure 2, embodiment 1 joint fastener 1 compared with existing non-asbestos pad and the existing pad that contains asbestos, has an extra high stretching resistance.
Experimental example 1
Following table 1 is listed the result of test of the stretching resistance of joint fastener, and wherein sample 1-1 is to 1-3, be respectively to have same thickness 0.5mm, and the joint fastener 1 of different mixing composition.And comparative sample 1-1 and 1-2 for being similar to the joint fastener of joint fastener 1, have identical thickness 0.5mm, and the composition of each raphioid fiber, are respectively 0wt% and 50wt%.These samples are manufactured, and under JIS K 6251 defined test conditions, test its stretching resistance by tensile test.In table shown in the result, the two stretching resistance of comparative sample 1-1 and 1-2 is lower than 40Mpa.On the other hand, all samples 1-1 all surpasses 45Mpa to the stretching resistance of 1-3, and hence one can see that, and these samples are the gasket material with suitable high tensile power.
Table 1
In above-mentioned sample, aramid fibre is that the aromatic inorfil of fiber fasciculation (is the pulpous state type, pulp type), rubber is nitrile butadiene rubber (NBR), the needle inorganic stuffing is the acicular crystal material of hydrated magnesium silicate, phenol antioxidant is binary (bis-) or trisome (tri-) polymerization phenolic resin or solation phenolic resin, and inorganic fillings is barium sulphide or clay etc.
In addition, the present invention has more than and is limited to above-mentioned sample.For example say, joint fastener can be multi-layer structure, for example says the pair of lamina structure, and it comprises, be equivalent to a front surface layer 1a or the front surface layer of rear surface layer 1b or a rear surface layer (so-called disc composition), and a main stor(e)y (a so-called inter-level) that is equivalent to mesosphere 1c.Or joint fastener can be single layer structure, only has an inter-level that is equivalent to mesosphere 1c.
Below, Fig. 3 is a sectional drawing, illustrates the pad of embodiment 2 gasket material manufacturing, wear-resistant effect.As shown in Figure 1, as the joint fastener 1 of gasket material, be one to comprise three layers multi-layer structure among the embodiment 2, that is to say a front surface layer 1a, a rear surface layer 1b and a middle table surface layer 1c.
Embodiment 2 joint fastener 1 is formed by following processing procedure.At first, a composition material is manufactured to come out, and is by mixed rubber (for example saying nitrile butadiene rubber (NBR)), reinforced fiber (in order to replace the fiber of asbestos, for example saying aramid fibre or glass fibre) and stuffing manufacturings such as (for example saying barium sulphide).Then, this composition material is added into, and comprises a hot rolling wheel of the press polish wheel of a pair roller (hot rolling wheel and cold breakdown pinch roller), by the kneading and the extruding of those rollers, with the composition that forms a thin slice on hot rolling wheel.Then, by using the temperature of hot rolling wheel, add the sulphur hermo-hardening and solidify this composition, to form a joint fastener.Then, by separating, to form this joint fastener with hot rolling wheel.In this processing procedure, three layers front surface layer 1a of above-mentioned joint fastener 1, rear surface layer 1b and mesosphere 1c, mainly be formed (, see also aforesaid paper " Develo μ mentofnon-asbestos gasket material ") as for the more detailed content of this processing procedure by the composition amount that changes reinforced fiber.In being equivalent to the 179th page of this paper, its Fig. 5 has illustrated, one example of the composition of the aramid fibre in mesosphere, glass fibre and nitrile butadiene rubber (NBR), particularly, the percentage of pointed composition in the 5th, wherein aramid fibre is about 24wt%, and glass fibre is about 33wt%, and nitrile butadiene rubber (NBR) is about 43wt%.
In embodiment 2 joint fastener 1, one of them front surface layer of two outermost surfaces layers that is to say that front surface layer 1a or rear surface layer 1b are constructed as the non-associated layer with low attaching power.Surface layer 1b then, promptly another outermost surfaces layer is constructed as the associated layer with high attaching power.The attaching power of rear surface layer 1b is 5 times for the attaching power that surpasses front surface layer 1a, and the attaching power of rear surface layer 1b surpasses 2.5MPa.
In order to obtain above-mentioned attaching power, the composition of the rear surface layer of embodiment 2 joint fastener 1, comprise that coumarone-polyenoid resin is that 2wt% is between the 15wt%, calcium carbonate is that 5wt% is between the 60wt%, nitrile butadiene rubber (NBR) is that 10wt% is between the 25wt%, and, comprise total composition of these compositions of the layer of these compositions being equal to or less than 100wt%.
According to embodiment 2 joint fastener 1, as shown in Figure 2, wherein two outermost surfaces one of them, be formed a non-associated layer, and another is formed the associated layer with strong attaching power with weak attaching power.Therefore,, for example say between chest H and the lid C that because by the rear surface layer 1b of joint fastener 1 formed pad G, attaching pad G for example says to structure, on the chest H, and it is maintained the home position though wearing and tearing F betides a structure.Therefore, front surface layer 1a gives pad G opposing structure by a less friction, for example says lid C one slip S.Make because pad G from the displacement in its home position, causes the generation of leakage efficiency minimizing to be avoided.
In addition, in embodiment 2 joint fastener 1, because the composition of rear surface layer 1b, comprise the calcium carbonate of 2wt% to coumarone-polyenoid resin of 15wt%, 5wt% to 60wt%, 10wt% nitrile butadiene rubber (NBR) to 25wt%.And, comprise total composition of these compositions of the layer of these compositions being equal to or less than 100wt%.As described below, according to these compositions, the attaching power of rear surface layer 1b, more than 5 times of attaching power that can surpass front surface layer 1a, and the attaching power of rear surface layer 1b can surpass more than the 2.5MPa, therefore, the sufficient sealing endurance of pad opposing wearing and tearing will be obtained.
Experimental example 2
Following table 1 is listed the result of test of the stretching resistance of joint fastener, and wherein sample 1-1 is to 1-3, be respectively to have same thickness 0.5mm, and the joint fastener 1 of different mixing composition.And comparative sample 1-1 and 1-2 for being similar to the joint fastener of joint fastener 1, have identical thickness 0.5mm, and the composition of each raphioid fiber, are respectively 0wt% and 50wt%.These samples are manufactured, and under JIS K 6251 defined test conditions, test its stretching resistance by tensile test.In table shown in the result, the two stretching resistance of comparative sample 1-1 and 1-2 is lower than 40Mpa.On the other hand, all samples 1-1 all surpasses 45Mpa to the stretching resistance of 1-3, and hence one can see that, and these samples are the gasket material with suitable high tensile power.
In the above embodiments 2, the sample 2-1 of joint fastener 1 has the thickness of 0.5mm to 2-6, is by individually distinguishing the composition manufacturing of front surface layer 1a and rear surface layer 1b.Pad sample is that each sample by joint fastener 1 is formed, and is embedded into these samples between the chest H and lid C of the transmission device of reality.And these pad sample embed the wearing and tearing endurance test at position at it, be to test in that following condition is following: each sample is fixed in by screw between chest H and the lid C, wherein the axial force of each screw is 1 ton (ton), the temperature of transmission device is 80 ℃, and act on the torque load (twist load) of the direction of the inputting shaft of transmission device and the reciprocal rotation between the force-output shaft, change (cycles) 3000 and be 100N-m down.Its result is do not taken place by the caused pad distortion of this displacement, and all pads all to have splendid endurance.
Table 2: sample 2-1
Table 3: sample 2-2
Table 4: sample 2-3
Table 5: sample 2-4
Table 6: sample 2-5
Table 7: sample 2-6
In addition, the present invention has more than and is limited to above-mentioned sample.For example say, joint fastener can be multi-layer structure, for example says the pair of lamina structure, that is to say, with a front surface layer or a rear surface layer as associated layer, and with the main stor(e)y (being formed) that is equivalent to mesosphere 1c by a so-called inter-level as a non-associated layer.
Fig. 4 illustrates the gasket material of a joint fastener, is the embodiment 3 according to first viewpoint of the invention described above.Numeral 1 expression one joint fastener is the gasket material of present embodiment.Joint fastener 1 has and comprises two-layer multi-layer structure, comprises a main stor(e)y 1e (so-called inter-level), and a surface layer 1f (disc composition just).
Embodiment 3 joint fastener 1 is formed by following processing procedure.At first, one composition material is manufactured to come out, be (for example to say by mixed rubber, nitrile butadiene rubber (NBR)), the reinforced fiber (fiber of fiber fasciculation, tinyization, for example say, aramid fibre), stuffing (for example saying barium sulphide) and the manufacturings such as (for example saying clay) of another inorganic fillings.Then, this composition material is added into, and comprises a hot rolling wheel of the press polish wheel of a pair roller (hot rolling wheel and cold breakdown pinch roller), by the kneading and the extruding of those rollers, with the composition that forms a thin slice on hot rolling wheel.Then, by using the temperature of hot rolling wheel, add the sulphur hermo-hardening and solidify this composition, to form a joint fastener.Then, by separating, to form this joint fastener with hot rolling wheel.As shown in Figure 4, in this processing procedure, two layers the main stor(e)y 1e and the surface layer 1f of above-mentioned joint fastener 1, mainly be formed (, see also aforesaid paper " Develo μ ment of non-asbestos gasket material ") about the more detailed content of this processing procedure by the composition amount that changes reinforced fiber.
In embodiment 3 joint fastener 1, the basis of this composition, comprise that an aramid fibre is as a reinforced fiber, it is formed and surpasses 20wt%, nitrile butadiene rubber (NBR) as a rubber material, its form 23wt% between the 30wt%, barium monosulfide is as a stuffing, it forms between 7% to 30% and an inorganic fillings, is a surplus material.
In the present embodiment, for example say, aromatic inorfil (being the pulpous state type, pulp type) is used as aramid fibre, wherein represents the specific surface area of this fiber of the degree of fiber bunchy, surpass 6m2/g, if the specific surface area of aramid fibre surpasses 6m2/g, and is as described below, then the tired surface pressure of the tension strength of joint fastener and pad and deformation can be increased fully.
In addition, in the present embodiment, have the barium sulphide of mean particle diameter below 3 μ m and be used.When mean particle diameter is the barium sulphide powder of 3 μ m when being used, therefore the tired surface pressure of the deformation of joint fastener and pad can be special and be increased.
According to embodiment 3 joint fastener 1, when the composition of aramid fibre surpasses 20wt%, and the composition of barium sulphide is when 7wt% is between 30vt%, can be by keeping the high flexibility of joint fastener, to strengthen the intensity of joint fastener.Therefore,, for example say between chest and the lid, then because pad from the skew in its home position, causes the generation of pad fracture damage to be avoided if wearing and tearing betide a structure.
In addition, this gasket material is strengthened the practice of intensity, neither increases the combining proportion of reinforced fiber, do not increase the length of staple of reinforced fiber yet, therefore the cost of material that can keep pad is at lower cost, and can be so that the having an even surface of pad, and leakage efficiency is increased fully.And this joint fastener is strengthened the practice of intensity, and the roll extrusion power the when rete that neither is increased in joint fastener forms does not increase the temperature of hot rolling wheel yet, therefore can keep the low hardness of joint fastener and obtain the endurance of pad, with the opposing stress of compression repeatedly.Therefore, because deformation fatigue causes weakening of gasket seal effect, can be avoided.
In addition, this gasket material is strengthened the practice of intensity, neither reduces the ratio of mixture of rubber material in joint fastener is formed, and does not also increase the ratio of acrylonitrile composition in the nitrile butadiene rubber (NBR), therefore, can keep the high flexibility of joint fastener.Therefore, because the gasket seal effect that a large amount of wearing and tearing caused of pad weakens, under the influence of surface pressure, resist the stress of the direction of extrusion, and can be avoided by these wearing and tearing.
Therefore, joint fastener 1 according to embodiment 3, work as structure, for example say transmission device, flintiness very low, and a high screw retention force acts on structure, when for example saying the pad embedding position between chest and the lid,, for example say on the lid if some masterpiece is used in structure, and it is out of shape when taking place, and this pad can obtain a splendid sealing endurance.
That is to say, when the flintiness of structure very low, and result from pad embed the below of retaining screw at position or this screw around surface pressure very high, but very low at the pressure of distance between between those screws.Therefore, this pad must have a high endurance of opposing deformation, and by the splendid leakage efficiency that elasticity obtained.And embodiment 3 joint fastener 1 can obtain these effects.
In addition, in the design at the sealing position of the structure of the joint fastener 1 by embodiment 3, the characteristic of joint fastener 1 can be strengthened the degrees of freedom (degree of freedom) of pitch (pitch), the size of retaining screw and the thickness of lid, so alleviating of structure weight can be obtained.
Fig. 5 illustrates the joint fastener 1 about embodiment 3, with the tensile test of three kinds of comparative sample 3-1 to 3-3 (the available joint fastener of existing commerce), the result under JIS K 6251 defined test conditions.This figure illustrates the comparison of the tension strength of the joint fastener of present embodiment and comparative sample.As shown in this figure, the tension strength of embodiment 3 joint fastener 1 (more particularly, below describe to the rough mean value of 3-7) with sample 3-1, more high than the value of the available joint fastener of existing commerce.
Fig. 6 illustrates the joint fastener 1 about embodiment 3, tests to the tired surface pressure of the deformation of 3-3 (the available joint fastener of existing commerce) with three kinds of comparative sample 3-1.Its test condition is, each ring-type sample is set between the pair of plates, one of them reciprocatingly slides two flat boards under a displacement distance 300 μ m medium frequency 1Hz, be one break of a predetermined surface pressure that is produced by high pressure washing to be arranged by having load, test is that whether the fine hair of fiber produces under 3000 commentaries on classics at oscillation cycle.And when the fine hair of sample produced, the tired surface pressure of this deformation was set to its surface pressure.This figure illustrates the comparison of the tired surface pressure of deformation of the joint fastener of present embodiment and comparative sample.As shown in this figure, the tired surface pressure of the deformation of embodiment 3 joint fastener 1 (more particularly, below with the rough mean value description of sample 3-1) to 3-7, more high than the value of the available joint fastener of existing commerce.
In addition, Fig. 7 illustrates the joint fastener 1 about embodiment 3, with the limit sealing load test of three kinds of comparative sample 3-1 to 3-3 (the available joint fastener of existing commerce), its test condition is, nitrogen is applied to through this flat board and produces in the sample of fine hair, and aqueous soup solution is applied to the periphery of sample to check the leakage of nitrogen.And when leaking generation, this limit sealing load is used as this gas pressure.As shown in this figure, the limit sealing load of embodiment 3 joint fastener 1 (more particularly, below describe to the rough mean value of 3-7 with sample 3-1) is about as much as the maximum value of the available joint fastener of existing commerce.
Embodiment 3
Following table 8 is listed the result of tensile test, deformation Fatigue test and the test of limit sealing load of joint fastener, wherein the sample 3-1 of embodiment 3 joint fastener 1 is to 3-7, all these sample thickness are all 0.5mm, but each sample has different compositions.And comparative sample 3-1 is that thickness is the joint fastener of 0.5mm to 3-6, and the composition of these comparative samples is according to joint fastener 1, but wherein the composition of aramid fibre or barium sulphide is outside embodiment 3 scope.These tests are carried out under above-mentioned condition.Its result shows, comparative sample 3-1 has the value of lower tension strength, the tired surface pressure of deformation and limit sealing load to 3-6, but all samples 3-1 has high tensile strength intensity above 5MPa to 3-7, remain on the tired surface pressure of the high deformation that surpasses 80MPa, and remain on limit sealing load above 2.0kgf/cm2.Hence one can see that, and embodiment 3 sample is the gasket material with excellent characteristics.
Table 8
Fig. 8 illustrates the result of study of the contribution of barium sulphide shape of particle, is by being similar under the above-mentioned test condition, according to deformation Fatigue test and the limit sealing load test of deformation fatigue with the character of limit sealing load.The basis of embodiment 1 joint fastener 1 comprises that the barium sulphide of the aramid fibre of 20wt%, the nitrile butadiene rubber of 23wt% (NBR), 20wt% and surplus material are inorganic fillings, and the barium sulphide particle diameter difference in each sample.As shown in this figure, when the barium sulphide particle diameter surpasses 4 μ m, the tired surface pressure P1 of deformation is inclined to minimizing significantly, and becomes big when the barium sulphide particle diameter, and limit sealing load also is inclined to minimizing.Therefore, barium sulphide is that the fine powder of diameter below 3 μ m is preferably.In addition, as Figure 18 and The above results shown in Figure 19, be that deformation Fatigue test and the test of limit sealing load under the same terms obtains.
Fig. 9 illustrates the result of study of contribution of degree of the fiber fasciculation of aramid fibre, is by being similar under the above-mentioned test condition, according to the tensile test and the deformation Fatigue test of the character of tension strength and deformation fatigue.The basis of embodiment 1 joint fastener 1 comprises that the barium sulphide of the aramid fibre of 20wt%, the nitrile butadiene rubber of 23wt% (NBR), 7wt% and surplus material are inorganic fillings, and the specific surface area of the aramid fibre of each sample is neither together.As shown in this figure, when the specific surface area of this aramid fibre of the degree of expression fiber bunchy, be lower than 6m2/g when following, tensile stress reduces and begins to take place, and the character of the tired trend minimizing of deformation, and is synchronous with the minimizing of tensile stress.Therefore, the specific surface area of aramid fibre, surpassing 6m2/g is preferably.
In addition, the present invention has more than and is limited to above-mentioned sample.For example say that joint fastener can be multi-layer structure, for example says three-decker, it comprises, is equivalent to the surface layer 3 (so-called disc composition) of a front surface layer and a rear surface layer 1b, and a main mesosphere (a so-called inter-level) that is equivalent to main stor(e)y 1e.Or joint fastener can be single layer structure, only has an inter-level that is equivalent to mesosphere 1e.
At last, Figure 10 illustrates a sectional drawing of the gasket material of a joint fastener, is the embodiment 4 according to the 4th viewpoint of the invention described above.Numeral 1 expression one joint fastener 1 has three-decker, comprises a front surface layer 1a, a rear surface layer 1b, and the mesosphere 1c between front surface and rear surface layer.And numeral 3 is represented a low friction coating.
Embodiment 4 gasket material is formed by following processing procedure.At first, a composition material is manufactured to come out, and is by mixed rubber (for example saying nitrile butadiene rubber (NBR)), reinforced fiber (in order to replace the fiber of asbestos, for example saying aramid fibre or glass fibre) and stuffing manufacturings such as (for example saying barium sulphide).Then, this composition material joins, and comprises a hot rolling wheel of the press polish wheel of a pair roller (hot rolling wheel and cold breakdown pinch roller), by the kneading and the extruding of those rollers, with the composition that forms a thin slice on hot rolling wheel.Then, by using the temperature of hot rolling wheel, add the sulphur hermo-hardening and solidify this composition, to form a joint fastener.Then, by separating, to form this joint fastener with hot rolling wheel.In this processing procedure, three layers front surface layer 1a of above-mentioned joint fastener 1, rear surface layer 1b and mesosphere 1c, mainly be formed (, see also aforesaid paper " Develo μ ment ofnon-asbestos gasket material ") as for the more detailed content of this processing procedure by the composition amount that changes reinforced fiber.In being equivalent to the 179th page of this paper, its Fig. 5 has illustrated, one example of the composition of the aramid fibre in mesosphere, glass fibre and nitrile butadiene rubber (NBR), particularly, the percentage of pointed composition in the 5th, wherein aramid fibre is about 24wt%, and glass fibre is about 33wt%, and nitrile butadiene rubber (NBR) is about 43wt%.
Then, comprise that (polytetrafluoroethylene, low friction treatment liquid PTFE) by a roller coating machine, is applied to the surface of the front surface layer 1a of joint fastener 1 to teflon.For example say, the amount that is applied be 300mg/m2 between the 1500mg/m2, then low friction treatment liquid is heated and dries.By this, as shown in figure 10, a low friction coating 3 is formed on the front surface layer 1a, and its thickness surpasses 3 μ m.
In the present embodiment, what comprise polytetrafluoroethylene (PTFE) should hang down friction treatment liquid, preferably, by mixing a concentration is that 30wt% (for example says to an emulsion of this teflon of 85wt%, the product D-1 of DAJKIN Industries Ltd., wherein solid constituent is 60wt%), (for example say to the phenolic resin colloidal sol of 70wt% with 15wt%, the products C T-E300 of Nihon Parkerizing Co.Ltd., wherein solid constituent is 10wt%) manufacturing, wherein this total weight percent maintains 100wt%.
According to the gasket material of the embodiment of the invention 4, a low friction coating 3 can be formed by applying the low friction treatment liquid that comprises teflon, to obtain low coefficient of friction μ.Therefore, for the relative displacement between the wall-attached surface of chest H or lid C etc. and pad G, the wearing and tearing on the surface of pad G that produces, if this pad G is the gasket material manufacturing by the embodiment of the invention 4, then the wearing and tearing on the surface of pad G can be avoided.And the leakage efficiency of pad, the pad compared to existing joint fastener manufacturing can improve significantly.
In addition, if low friction treatment liquid is to be the emulsion of 30wt% to this teflon of 85wt% by mixing a concentration, with the phenolic resin colloidal sol manufacturing of 15wt% to 70wt%, wherein this total weight percent maintains 100wt%.As described below, when the number of occurrence of sliding increased, the low coefficient of friction of pad can be kept.And because the surface of joint fastener, be by being covered, so the absorption aqueous vapor of joint fastener,, can be avoided with the corrosion of chest H and lid C etc. by the polytetrafluoroethylene (PTFE) of phenolic resin institute bond constraint.
In addition, according to embodiment 4 gasket material, because the thickness of the coating that should lowly rub surpasses 3 μ m.Therefore, though this coating is worn gradually, the low coefficient of friction of pad still can be kept segment length's time.
According to embodiment 4, test to be engaged in a slip by the sample that uses several joint fasteners, use is following sample: sample 4-1 and sample 4-2, be by applying the composition ratio of polytetrafluoroethylene (PTFE) and phenolic resin, be individually the treatment fluid of 85: 15 and 30: 70, and have a low friction coating.Sample 4-3 is the treatment fluid that has the 100wt% polytetrafluoroethylene (PTFE) by applying, and has a low friction coating.The be untreated comparative sample 4 of material does not differ from the treatment fluid of above-mentioned sample 4-1 to 4-3 for applying.According to these samples, the test of sliding is carried out under following condition: by by the aluminium manufacturing, probe (measuring pin) with diameter 3mm, with a surface pressure 4.9MPa, act on each sample, and each sample is with the slided distance of 25mm of Sliding velocity 24mm/min.As shown in figure 11, increase along with the composition ratio of polytetrafluoroethylene (PTFE), friction factor has tailed off, but shown in sample 4-3, when wherein contained phenolic resin composition ratio becomes less than 15wt%, when the slip number of occurrence arrived a certain number, friction factor had raise widely at this point.
In addition, the lid that expression maintains the easy degree on this product attaches intensity (the easy degree of the separation of lid C), for the treatment fluid that by the composition ratio that applies polytetrafluoroethylene (PTFE) and phenolic resin is 20: 80, those samples of manufacturing are with to add sample 4-4 therefore measured.This measurement is carried out under following condition: surface pressure is 9.8MPa, and heat treatment temperature is that 100 ℃ and heat treatment time are 60min.As shown in figure 21,4 samples of embodiment 4 have non-attaching power, so lid C can be by easily from the free-hand separation of pad, and still in comparative sample, the instrument of need using separates.
In addition, for above-mentioned sample and comparative sample, it is measured to increase ratio (%) by the weight that absorbs the aqueous vapor generation.Its condition is, these samples were dipped in the water 5 hours.As shown in figure 13 as can be known, having sample 4-1, the 4-2 and the 4-4 that comprise the coating of phenolic resin in treatment fluid, have splendid water proofing property, is each surface because of these pad sample, and the polytetrafluoroethylene (PTFE) that is contained phenolic resin has covered.Therefore, the absorption of aqueous vapor has been limited.
By comprehensive these results, following table 9 is listed above-mentioned T ﹠ M result's evaluation.As shown in Table 9, embodiment 4 sample 4-1 is to 4-4, has low coefficient of friction (for the lattice of non-avaible among the sample 4-4, can be from Figure 11 the amount based on teflon estimate), by caused splendid the keeping usefulness and, can avoid the water proofing property of corroding of its non-attaching power with respect to comparative sample.Particularly, can know sample 4-1 and 4-2, see through a result who tests on a large scale, have high-effect.In table 9, the unit of the value of polytetrafluoroethylene (PTFE) and phenolic resin is wt%, and each symbol " ◎ " expression " splendid ", " zero " expression " height ", " △ " expression " centre " and " * " expression " low ".
Table 9
In addition, the invention is not restricted to the embodiments described, for example says, this low friction is coated with 3, can be formed on the both sides on the surface of joint fastener 1, and the structure of joint fastener 1 can be changed.
And gasket material of the present invention as in the above embodiments 1 to 4, certainly is used as the pad of engine periphery, is embedded in the chest H of transmission device and the pad between the lid C with replacement.
According to the gasket material of first viewpoint of the present invention, the stretching resistance of this joint fastener can increase, and is the interaction effect of tieing up by the tiny chemical fibre that organic fiber and inorfil are formed, and the effect that adds of tiny chemical fibre dimension and needle inorganic fiber.Therefore,, for example say between chest and the lid, then because pad from the skew in its home position, causes the generation of pad fracture damage to be avoided if wearing and tearing betide a structure.
According to the gasket material of second viewpoint of the present invention, its two outermost surfaces one of them, be formed a non-associated layer, and another is formed the associated layer with strong attaching power with weak attaching power.Therefore,, for example say between chest and the lid,, and it is maintained the home position because the associated layer that attaches the pad of this pad to the structure from gasket material is formed though wearing and tearing betide a structure.Therefore, non-associated layer is given a slip S of pad antagonism structure by a less friction, makes because pad from the displacement in its home position, causes the generation of leakage efficiency minimizing to be avoided.
In addition, according to the gasket material of the 3rd viewpoint of the present invention, when the composition of aramid fibre surpasses 20wt%, and the composition of barium sulphide is when 7wt% is between 30vt%, can be by keeping the high flexibility of joint fastener, to strengthen the intensity of joint fastener.Therefore,, for example say between chest and the lid, because pad from the skew in its home position and the minimizing of surface pressure, causes the generation of the leakage of sealing substance to be avoided if wearing and tearing betide a structure.And the cost of material that can keep pad is at lower cost, and can be so that the having an even surface of pad, and leakage efficiency is increased fully.
In addition, this gasket material is strengthened the practice of intensity, neither reduces the ratio of mixture of rubber material in joint fastener is formed, and does not also increase the ratio of acrylonitrile composition in the nitrile butadiene rubber (NBR), therefore, can keep the high flexibility of joint fastener.In addition, this joint fastener can be kept the low hardness of joint fastener and obtain the endurance of pad, to resist the stress of compression repeatedly.Because deformation fatigue causes weakening of gasket seal effect, can be avoided.In addition, this gasket material can be kept the high flexibility of joint fastener.Therefore, because the gasket seal effect that a large amount of wearing and tearing caused of pad weakens, under the influence of surface pressure, resist the stress of the direction of extrusion, and can be avoided by these wearing and tearing.
In addition,,, be formed on the single face of a joint fastener or the low friction coating on two sides wherein by applying the low friction treatment liquid that comprises teflon according to the gasket material of the 3rd viewpoint of the present invention, can be so that gasket surface obtains enough low coefficient of friction.Therefore, for the relative displacement between the wall-attached surface of chest H or lid C etc. and pad G, the wearing and tearing on the surface of pad G that produces, if this pad G is by gasket material manufacturing of the present invention, then the wearing and tearing on the surface of pad G can be avoided.And the leakage efficiency of pad, the pad compared to existing joint fastener manufacturing can improve significantly.
Though the present invention discloses as above with a preferred embodiment; right its is not in order to limiting the present invention, anyly has the knack of this skill person, without departing from the spirit and scope of the present invention; when can doing a little change and retouching, so protection scope of the present invention is as the criterion when looking claims person of defining.
Claims (3)
1. a gasket material is by the joint fastener manufacturing, wherein makes the composition of aforementioned joint fastener, is by mixing and kneading rubber, reinforced fiber and stuffing, the sheet of pressurizeing then, and add the aforementioned composition gained of sulphur hermo-hardening, aforementioned gasket material comprises:
Aramid fibre as reinforced fiber, is formed and is surpassed 20wt%;
Rubber material is formed at 23wt% between the 30wt%;
Barium sulphide is formed at 7wt% between the 30wt%;
Inorganic fillings is remaining material,
Wherein aforementioned barium sulphide and aforementioned inorganic fillings are as aforementioned stuffing.
2. gasket material as claimed in claim 1 is characterized in that: the mean particle diameter of aforementioned barium sulphide, and below 3 μ m.
3. gasket material as claimed in claim 1 or 2 is characterized in that: the specific surface area of aforementioned aramid fibre, and at 6m
2More than/the g.