CA2683204C

CA2683204C - Stabilized lithium metal powder for li-ion application, composition and process

Info

Publication number: CA2683204C
Application number: CA2683204A
Authority: CA
Inventors: Marina Yakovleva; Yuan Gao; Yangxing Li
Original assignee: FMC Corp
Current assignee: Livent USA Corp
Priority date: 2007-05-16
Filing date: 2008-05-14
Publication date: 2014-12-23
Anticipated expiration: 2028-05-14
Also published as: EP2144723B1; GB0917815D0; KR101524257B1; EP2144723A1; CA2683204A1; US8377236B2; GB2460380B; US8021496B2; DE112008001008T5; US20080283155A1; JP5258878B2; GB2460380A; RU2009146567A; WO2008143854A1; CN103447541A; KR20100022006A; CN101678459A; RU2467829C2; US20110300385A1; JP2010535936A

Abstract

The present invention provides a method for stabilizing lithium metal powder. The method comprises the steps of heating the lithium metal powder to above its melting point to provide molten lithium metal, dispersing the molten lithium metal, and contacting the dispersed molten lithium metal with a phosphorous-containing compound to provide a substantially continuous protective layer of lithium phosphate on the lithium metal powder.

Description

STABILIZED LITHIUM METAL POWDER FOR LI-ION APPLICATION, COMPOSITION AND
PROCESS
FIELD OF THE INVENTION

[0002] The present invention relates to stabilized lithium metal powder ("SIMPH) having better stability and a longer storage life. Such improved SLMP can be used in a wide variety of applications including organo-metal and polymer synthesis, rechargeable lithium batteries, and rechargeable lithium ion batteries.
BACKGROUND OF THE INVENTION

[0003] The highly reactive, i.e., pyrophoric, nature of lithium metal, particularly high surface area lithium metal powder, can be a deterrent for its use in a variety of applications. Thus lithium metal is typically in a stabilized form. It is known to stabilize lithium metal powder by passivating the metal powder surface with CO2 such as described in U.S. Patent Nos. 5,567,474, 5,776,369, and 5,976,403.
The CO2 passivated lithium metal powder, however, can be used only in air with low moisture levels for a limited period of time before the lithium metal content decays because of the reaction of the lithium metal and air.

[0004] Another option has been to coat the lithium powder with a protective layer. For example, U.S. Patent No. 6,911,280 81 proposes coating with an alkali or alkaline earth metal carbonate. U.S. Patent No. 4,503,088 proposes coating an epoxy resin on a lithium negative electrode as a passivation layer. U.S. Patent Nos. 5,342,710 and 5,487,959 propose using a complex of 12 and poly-2-vinylpyridine as a passivation layer. These suggested protective layers;
however, often result in a decrease in conductivity and weak mechanical strength.

SUMMARY OF THE INVENTION

[0005] The present invention provides a method for stabilizing lithium metal powder.
The method comprises the steps of heating the lithium metal powder to above its melting point to provide molten lithiuni metal, dispersing the molten lithium metal, and contacting the dispersed molten lithium metal with a phosphorous-containing compound such as phosphoric acid to provide a substantially continuous protective layer of lithium phosphate on the lithium metal powder.
BRIEF DESCRIPTION OF THE DRAWINGS

[0006] FIG. 1 is a comparison of SEM images for stabilized lithium powder prepared according to Examples 1-4.

[0007] = FIG. 2 is a comparison of SEM images for stabilized lithium powder prepared according to Examples 1 and 5.

[0008] FIG. 3 is an air stability comparison of Comparative Example 1, Comparative Example 2, and Example 1.

[0009] FIG. 4 is an Advanced Reactive Screening Tool Colorimeter (ARSST) Test comparing the stability of Comparative Example 1 and Example 4.

[0010] FIG. 5 is a Vent Sizing Package 2 (VSP2) test comparing the stability of Example 1 and Example 5 in NMP.
. DETAILED DESCRIPTION OF THE INVENTION

[0011] In the drawings and the following detailed description, various embodiments are described in detail to enable practice of the invention. Although the invention is described with reference to these specific embodiments, it will be understood that the invention is not limited to these embodiments. But to the contrary, the invention includes numerous alternatives, modifications and equivalents as will become apparent from consideration of the following detailed description and accompanying drawing.

[0012] The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used herein, the term "and/or" includes any and all combinations of one or more of the associated listed items.
As used herein, the singular forms "a", "an," and "the" are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms "comprises" and/or "comprising," when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof. Furthermore, the term "about," as used herein when referring to a measurable value such as an amount of a compound or agent of this invention, dose, time, temperature, and the like, is meant to encompass variations of 20%, 10%, 5%, 1%, 0.5%, or even 0.1% of the specified amount.

[0013] Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.

[0014] The citation of a reference herein should not be construed as an acknowledgement that such reference is prior art to the present invention described herein.

[0015] The present invention relates to a method of providing stable lithium metal powder.
The method includes the step of heating lithium metal powder to above its melting point in an inert atmosphere. Typically this is above about 200 C. Often this is done by heating a non-combustible hydrocarbon oil. Exemplary hydrocarbon oils include mineral oil, or any other saturated hydrocarbon solvent having a branched, straight chain or saturated cyclic structures and a flash point above about 200 F. A variety of hydrocarbon oils may be used in the present invention. The term hydrocarbon oil, as used herein, includes various oily liquids consisting chiefly or wholly of mixtures of hydrocarbons and includes mineral oils, i.e., liquid products of mineral origin having viscosity limits recognized for oils and hence includes but is not limited to petroleum, shale oils, paraffin oils and the like. There are many manufacturers of these useful hydrocarbon oils. Among these useful hydrocarbon oils are highly refined oils, such as, PeneteckTM manufactured by Penreco Division of Pennzoil Products Inc., which has a viscosity in the range of 43-59 pascal-sec at 100 F. and a flash point of 265 F, Parol 100, which has a viscosity of 213-236 pascal-sec at 100 F. and a flash point of 360 F
(available from Penreco, Div. of Pennzoil Products), and Carnation" white oil (viscosity=133-165 pascal-sec at 100 F) made by Sonnebom Div. of Witco. Even certain purified hydrocarbon solvents which boil in a range encompassing the melting point of lithium may be used, such as UNOCAL's 140 SolventTM. In addition, unrefined oils, such as Unocal's 460 Solvent' and Hydrocarbon Seal' oil and Exxon's Telura 401TM and Telura 407" may also be used. The selection of a hydrocarbon oil will be within the skill of one in the art.

[0016] The molten lithium metal is then dispersed such as by agitating or stirring vigorously to apply high sheer forces. The dispersion step using high sheer or other equivalent forces is conducted to form uniform droplets or particles of the lithium metal, and to facilitate distributing the droplets or particles in the hydrocarbon oil while avoiding agglomeration.

[0017] The dispersed molten lithium is contacted with a phosphorous-containing compound such as phosphoric acid (H3PO4) to provide a substantially continuous protective layer of lithium phosphate (Li3PO4) on the lithium metal powder. Other phosphorous-containing compounds can be used, particularly if phosphoric acid is formed during its reaction with the lithium. For example, P205 can be used if reacted in the presence of moisture so that H3PO4 is formed first and then the Li3PO4 is formed. Alternatively POF3 gas could be hydrolyzed into HF and H3PO4 which then reacts with lithium to form Li3PO4.

[0018) The phosphorous-containing compound can be introduced to contact the lithium droplets during the dispersion at a temperature above the lithium melting point, or at a lower temperature after the lithium dispersion has cooled. The phosphorous-containing compound could be introduced in a crystalline form or in a solution form in mineral oil or any other suitable solvent. It is understood that combinations of different process parameters could be used to achieve specific coating characteristics. For example, control of reaction rate between lithium and the phosphorous-containing compound is essential in preventing cavities and/or cracks being formed. Furthermore, it is beneficial to combine the coating with an organic coating, for example, different types of waxes with different chemical compositions, molecular weights, melting points and hardness could be used to achieve specific coating characteristics for particular applications and the like, to improve both air stability and polar solvent stability that would allow both safer handling and possibility of using commonly used polar solvents that dissolve commonly used polymer binders.

[0019] Suitable waxes can be natural wax such as 12-hydroxystearic acid, synthetic wax such as low molecular weight polyethylene, petroleum waxes such as paraffin wax, and microcrystalline waxes. The wax can be introduced to contact the lithium droplets during the dispersion, or at a lower temperature after the lithium dispersion has cooled. It is understood that combinations of different types of waxes with different chemical compositions, molecular weights, melting points and hardness could be used to achieve specific coating characteristics for particular applications. For example, degree of stickiness could be controlled to allow introduction of the SLMP using a "transfer release paper"
concept, wherein a certain degree of stickiness is required.

[0020] Suitable waxes described above could produce two types of coatings on lithium particles: first type representing physical or adhesive type where non-pOlar waxes are used and a second type, representing chemically bonded coatings where waxes with functional groups, having both hydrophobic and hydrophilic features, are used.
The coating thickness could vary in the range of about 20nm to about 200 nm.

[0021] The present invention also provides a lithium metal powder protected by Li3PO4. A thin, dense, substantively continuous Li3PO4 layer of the invention provides improved protection such as compared to typical CO2 and LiF passivation techniques. The lithium phosphate layer may comprise about 0.5% to 20% by weight of the stabilized lithium metal powder. This range is estimated based on a 45 micron particle: 0.01 micron coating corresponds to 0.74% Li3PO4 and 0.3 micron coating corresponds to 18.6%
Li3PO4. The resulting lithium metal powder has improved stability and improved storage life. To this end, a more stable lithium metal powder is provided. The lithium metal powder is passivated by H3PO4. Such a thin, dense, continuous Li3PO4 layer provides better passivation as compared to CO2 and LiF because of the insolubility of Li3PO4 in water (i.e., 0.04 g in 100 g H20 at 25 C) vs. LiF (i.e., 0.133 g in 100 g H20 at 25 C) and Li2CO3 (i.e., 1.29 g in 100g H20 at 25=C). The Li3PO4 passivation layer serves as a better barrier against moisture and atmosphere gases.

[0022] The following examples are merely illustrative of the invention, and are not limiting thereon.
=
EXAMPLES
Example 1

[0023] Battery grade lithium metal (411 grams) was cut into 2x2 inch pieces and charged under constant flow of dry argon at room temperature to a 3 liter stainless steel flask reactor with a 4" top fitted with a stirring shaft connected to a fixed high speed stirrer motor.
The reactor was equipped with top and bottom heating mantles. The reactor was assembled and 1078 g of PeneteckTm oil were added. The reactor was then heated to about 200 C and gentle stirring was maintained in the range of 250 rpm to 800 rpm to ensure all metal was molten. Then the mixture was stirred at high speed (up to 10,000 rpm) for 2 minutes. Oleic acid, 8.22 g was charged into the reactor and high speed stirring continued for another 3 minutes. Then the high speed stirring was stopped, the heating mantles were removed and = the dispersion was allowed to cool to about 46 C. Next, 21.4 grams of phosphoric acid melted in advance in 68.59 grams of oil was charged into the reactor while stirring at about 800 rpm, the temperature rise of 2 C was noted. The dispersion was stirred for another. 10 minutes and then transferred to the storage bottles. Further, lithium dispersion was filtered and washed three times with hexane in an enclosed, sintered glass filter funnel and once with n-pentane to remove the hydrocarbon oil medium. The funnel was heated with a heat gun to remove traces of the solvents and the resulting free-flowing powder was transferred to tightly capped storage bottles.
Exatnple 2

[0024] 1102g of non-stabilized lithium dispersion in oil (11.3%) that contained -124.5g of lithium with a medium particle size of 45 micron was charged under constant flow of dry argon at room temperature to a 2 liter three neck glass flask reactor fitted with a stirring shaft connected to a fixed high speed stirrer motor. 7.81 g of phosphoric acid (Aldrich) in a form of a 2 phase solution in 8g of mineral oil at 21 C was charged into the reactor. Temperature rise of 4 C was noted along with significant foaming and stirring = continued for another hour and then transferred to the storage bottles.
Further, lithium dispersion was filtered and washed three times with hexane in an enclosed, sintered glass filter funnel and twice with n-pentane to remove the hydrocarbon oil medium.
The funnel was heated with a heat gun to remove traces of the solvents and the resulting free-flowing powder was transferred to a tightly capped storage bottles.
Example 3

[0025] 1128.5g of non-stabilized lithium dispersion in oil (11.2%) that contained 126.4g of lithium with a medium particle size of 63 micron was charged under constant flow of dry argon at room temperature to a 5 liter three neck glass flask reactor fitted with a stirring shaft connected to a fixed high speed stirrer motor. 7.81 g of phosphoric acid (Aldrich) in a form of a 2 phase solution in 8g of mineral oil at 20 C was charged into the reactor drop-wise over the period of 6 minutes; higher agitation than in example 2 was used.
Temperature rise of 4.5 C was noted within 20 minutes, no foaming was observed, and stirring continued for another 5 hours and then transferred to the storage bottles. Further, lithium dispersion was filtered and washed three times with hexane in an enclosed, sintered = glass filter funnel and twice with n-pentane to remove the hydrocarbon oil medium. The funnel was heated with a heat gun to remove traces of the solvents and the resulting free-flowing powder was transferred to a tightly capped storage bottles.
Example 4

[0026] 55.00 grams of non-stabilized lithium dispersion in oil (11.275%) containing 6.20 grams of lithium with a medium particle size of 63 micron was charged into 120 ml hastelloy can equipped with a 1" Teflon"' coated stir bar. The solution was heated to 200 C and 0.4g Anhydrous H3PO4 previously melted in 2 ml of mineral oil was added to the lithium dispersion.
This mixture was continuously stirred at 200 rpm for 30 minutes while holding the temperature at 2000C. Sample was allowed to cool to the room temperature and transferred to the storage bottle.
Further, lithium dispersion was filtered and washed three times with hexane in an enclosed, sintered glass filter funnel and twice with n-pentane to remove the hydrocarbon oil medium. The funnel was heated with a heat gun to remove traces of the solvents and the resulting free-flowing powder was transferred to a tightly capped storage bottles.
(00271 FIG. 1 demonstrates that process parameters affect the quality of the coating. From left to right: amount of cavities/cracks reduced providing better hermeticity for the Li particle. Example 4 represents liquid/liquid reaction interface and is believed to provide even better protection: passivating layer is like a crust of microcrystalline Li3PO4. Adding, for example wax, will ensure that all the porosity, cracks, cavities are protected against moisture and atmospheric gases.
Example 5 [00281 52.3 grams of lithium dispersion in oil (12.0%), produced in example 1, containing 6.3 grams of lithium with a median particle size of 31 micron was charged into 120 ml hastelloy can equipped with a 1" Teflon"' coated stir bar. 0.34g of LuwaxSTm dry powder was also added to the can.
The mixture was heated from ambient temperature to 7.5=C at a rate of 5.C/min and held for 10 minutes. The sample was further heated from 75"C to 175C at 5-C/min and held for one hour. Finally the mixture was heated from 175"C to 190"C at a rate of 20"C/min followed by slow cooling to ambient temperature. This mixture was continuously stirred at 200 rpm during the heating phase. Following cooling to the room temperature the sample was transferred to a glass storage bottle. Further, the lithium dispersion was filtered and washed three times with hexane in an enclosed, sintered glass filter funnel and twice with n-pentane to remove the hydrocarbon oil medium.
The funnel was heated with a heat gun to remove traces of the solvents and the resulting free-flowing powder was transferred to a tightly capped storage bottles.
=
[0029] FIG. 2 illustrates a comparison bf SEM images for Example 1 and EXample 5, and demonstrate the effect of a multi-coating approach.
Comparative Example 1 [0030] Battery grade lithium metal 441 grams was cut into 2x2 inch pieces and charged under constant flow of dry argon at room temperature to a 3 liter stainless steel flask reactor with a 4" top fitted with a stirring shaft connected to a fixed high speed stirrer motor.
The reactor was equipped with top and bottom heating mantles. The reactor was then assembled and 1215 g of PeneteckTM oil (Penreco, Division of the Penzoil products Company) were added. The reactor was then heated to about 200 C and gentle stirring was maintained in the range of 250 rpm to 800 rpm to ensure all metal was molten.
Then the mixture was stirred at high speed (up to 10,000 rpm) for 2 minutes. Oleic acid, 4A 1 g was= =
charged into the reactor and high speed stirring continued for another 3 minutes. Then the = high speed stirring was stopped, heating mantles removed and dispersion was allowed to cool = to about 100 C at which point 32.6 grams of fluorinating agent FC70,(perfluoropentylamine) was charged into the reactor while stirring .at about 800 rpm until cooled to about 45 C and transferred to the storage bottles. Further, lithium dispersion was filtered and washed three times with hexane in an enclosed, sintered glass filter funnel and once with n-pentane to =
remove the hydrocarbon oil medium. The funnel .was heated with a heat gun to remove traces of the solvents and the resulting free-flowing powder was transferred to a tightly capped storage bdttles.
Comparative Example 2 =
[0031] Battery grade lithium metal 441 grams was cut into 2x2 inch pieces and =
charged under constant flovv of dry argon at room temperature to a 3 liter stainless steel flask reactor with a 4" top fitted with a stirring shaft connected to a fixed high speed stirrer motor.
= The reactor was equipped with top and bottom heating mantles. The reactor was then =
assembled and 1215 g of PeneteckTM oil (Penreco, Division of the Penzoil products Company) were added. The reactor was then heated to about 200 C and gentle stirring was maintained in the range of 250 rpm to 800 rpm to ensure all metal was molten.
Then the mixture was stirred at high speed (up to 10,000 rpm) for 2 minutes. Oleic acid, 4.41 g was charged into the reactor and high speed stirring continued for another 3 minutes. Then the . high speed stirring was stopped, heating mantles removed and dispersion was allowed to cool to about 100 C at which point 32.6 grams of fluorinating .agent FC70 (perfluoropentylamine) was charged into the reactor while stirring at about .800 rpm until cooled to about 45 C and = transferred to the storage bottles. Further, lithium dispersion was filtered and washed three times with hexane in an enclosed, sintered glass filter funnel and once with tiTentane to = remove the hydrocarbon oil.medium. The funnel Was heated with a heat' gun to remove traces of the solvents and the resulting free-flowing powder Was transferred to a tightly capped storage bottles. Physical properties for Examples 1-4 and Comparative Examples 1 and 2 are provided in. Table 1. The table is shown that the physical properties demonstrate = that the properties are similar and there is no surface area effect.
[0032]
Referring= to = FIG. 3, in the= standard air stability. test, Example 1 'clearly retained more metallic lithium. Lithium metal powder is spread in a thin layer in the Petri =
dishes and exposed to certain moisture/temperature conditions.
Metallic lithiOrn concentration is monitored, the more metallic lithium is retained, the better the stability of the =. sample is.
=
. Table 1. Comparison of Physical Properties Coating Type ==D50, micron Calculated SA, M24;
Comparative Sample 1 = Li2CO3 _ . 32 ==0.22 -=
Comparative Sample 2 = = UF =34 = =0.19 =
Example 1 U3PO4 = 31 . 0.20 =
Example2 = U3PO4 ==45 = 0.14 Exaniple3 = U3PO4 85 = 0.11 =
Example4 = LisPO4 63 = 0.11 =
=
= .
[0033]
Referring to FIG. 4, there is a comparison of the stability of Example 4 and comparative example 1 in Ø6% water doped NMP is provided. This test shows that while CO2-coated SLMP exhibits runaway reaction at about 48 hours of exposure to the solvent = . doped with moisture, the SLMP produced according to the invention of example 4 has = significantly improved tolerance to moist NMP. The Example 4 SLMP does not have runaway reaction when exposed to room temperature for 72 hours and when exposed to 55 C
- for about 30 hours.
= 9 =

[0034] Referring to FIG. 5, a comparison of the stability of samples produced according to Example 1 and Example 5 in NMP is provided. Test shows immediate runaway was observed for the reaction system containing Example 1 sample while no runaway reaction was observed for the system containing the Example 5 sample. The test was conducted at 30.0 for 24 hours.
[0035] Having thus described certain embodiments of the present invention, it is to be understood that the invention defined by the appended claims is not to be limited by particular details set forth in the above description as many apparent variations thereof are possible without departing from the scope thereof as hereinafter claimed.

Claims

WHAT IS CLAIMED IS:

1. A method of providing a stable lithium metal powder comprising the steps of:
a) heating lithium metal powder to above its melting point to provide molten lithium metal;
b) dispersing the molten lithium metal; and c) contacting the dispersed molten lithium metal with a phosphorous-containing compound to provide a substantially continuous protective layer of lithium phosphate on the lithium metal powder.

2. The method according to claim 1, wherein the step of heating the lithium metal is conducted in a hydrocarbon oil.

3. The method according to claim 2, wherein the hydrocarbon oil is selected from the group consisting of mineral oil, petroleum oil, shale oils, and highly refined oils.

4. The method according to claim 1, wherein the step (c) of contacting the dispersed molten lithium metal with the phosphorous-containing compound is conducted during step (b) of dispersing the molten lithium metal.

5. The method according to claim 1, wherein the dispersed molten lithium metal of step (b) is cooled prior to step (c).

6. The stable lithium metal powder produced according to the method of claim 1.

7. The stable lithium metal powder according to claim 6, further including an organic coating.

8. The stable lithium metal powder according to claim 7, wherein the organic coating is a wax.

9. The stable lithium metal powder according to claim 6, wherein the phosphorus-containing compound is selected from the group consisting of phosphoric acid, P2O5 and POF3.

10. Stabilized lithium metal powder having a substantially continuous protective layer of lithium phosphate.

11. The stabilized lithium metal powder of claim 10, further including an organic coating layer.

12. The stabilized lithium metal powder of claim 11, wherein the organic layer is a wax.

13. A method of providing a stable lithium metal powder comprising the steps of:
a) heating lithium metal powder to above its melting point to provide molten lithium metal;
b) dispersing the molten lithium metal; and c) contacting the dispersed molten lithium metal with a phosphoric acid to provide a substantially continuous protective layer of lithium phosphate on the lithium metal powder.

14. The method according to claim 13, wherein the step of heating the lithium metal is conducted in a hydrocarbon oil.

15. The method according to claim 14, wherein the hydrocarbon oil is selected from the group consisting of mineral oil, petroleum oil, shale oils, and highly refined oils.

16. The method according to claim 13, wherein the step (c) of contacting the dispersed molten lithium metal with the phosphoric acid is conducted during step (b) of dispersing the molten lithium metal.

17. The method according to claim 13, wherein the dispersed molten lithium metal of step (b) is cooled prior to step (c).

18. The stable lithium metal powder produced according to the method of claim 13.

19. The stable lithium metal powder according to claim 18, further including an organic coating.

20. The stable lithium metal powder according to claim 19, wherein the organic coating is a wax.