CA2325714A1 - Multi-layer compositions comprising a fluoropolymer - Google Patents

Multi-layer compositions comprising a fluoropolymer Download PDF

Info

Publication number
CA2325714A1
CA2325714A1 CA002325714A CA2325714A CA2325714A1 CA 2325714 A1 CA2325714 A1 CA 2325714A1 CA 002325714 A CA002325714 A CA 002325714A CA 2325714 A CA2325714 A CA 2325714A CA 2325714 A1 CA2325714 A1 CA 2325714A1
Authority
CA
Canada
Prior art keywords
layer
fluorinated
group
article
sodium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
CA002325714A
Other languages
French (fr)
Inventor
Naiyong Jing
Sehyun Nam
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Co
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of CA2325714A1 publication Critical patent/CA2325714A1/en
Abandoned legal-status Critical Current

Abstract

This invention provides a method of bonding substantially non-fluorinated polymeric material to dissimilar polymers, particularly fluoropolymer materials, utilizing a bonding composition comprising substantially nonfluorinated polymeric material comprising a blend of carboxyl, anhydride, imide, or oxycarboxy functional polyolefin with a suitable organic or inorganic base and an organo-onium compound that is stable in the presence of the base. Multi-layer articles and composite constructions, including retroreflective sheeting, fuel line hoses, and adhesive articles made of a fluoropolymer layer and a substantially non-fluorinated layer are also provided.

Description

Multi-Layer Compositions Comprising a Fluoropoiymer FIELD OF THE INVENTION
The invention relates to multi-layer constructions comprising a fluoropolymer and a substantially non-fluorinated polymeric material as well as to methods of producing such constructions and materials. In another aspect, this invention relates to methods of improving the adhesion between a fluoropolymer and other dissimilar materials, including polyolefins. In yet another aspect, the invention relates to bonding compositions useful to adhere two dissimilar polymeric materials.
BACKGROUND OF THE INVENTION
Fluorine-containing polymers (i.e., fluoropolymers or fluorinated polymers), are an important class of polymers that include, for example, fluoroelastomers and fluoroplastics. Among this broad polymer class are polymers of high thermal stability, polymers exhibiting chemical (and solvent) resistance, and polymers exhibiting usefulness along a broad spectrum of temperatures. Many of these polymers also are almost totally insoluble in a wide variety of organic solvents; see, for example, F.W. Billmeyer, Textbook ofPo_lymer Science, 3rd ed., pp. 398-403, John Wiley & Sons, New York (1984).
Fluoroelastomers, particularly the copolymers of vinylidene fluoride with other ethylenically unsaturated halogenated monomers such as hexafluoropropylene find particular utility in high temperature applications, such as in seal gaskets and linings. See, for example, Brullo, R.A., "Fluoroelastomer Rubber for Automotive Applications," Automotive Elastomer & Desiun, June 1985, "Fluoroelastomers Seal Up Automotive Future," Materials Engineering, October 1988, and "Fluorinated Elastomers," Kirk-Othmer, Encyclopedia of Chemical TechnoloQV, 3rd ed., Vol.
8, pp. 500-515, John Wiley & Sons, New York (1979).
Fluoroplastics, particularly polychlorotrifluoroethylene, polytetrafluoroethylene, copolymers of tetrafluoroethylene and hexafluoropropylene, and poly(vinylidene fluoride), have numerous electrical, ny, . '~.r'~.. .. . . _. _ ., _ __ _ ~ "~.,~ ....
.,~. ....v L'vn'v ' v mr.n . i . . ~ vv .r U- i v.rr yr . ~-r.

sneclarnical, and kcal applications. Fluoroptasticg are useful, For example, as wire coatings, elcetrical components, seals, and in solid atx! Bred pipes and piexodectric detectors. See, for trample, "Organic Fluorine Co~npauc~ds," Kirk-p, ~.,..,~~ ig of~;hemical'fechnOloev, Vol. 11, pp. 20, Z1, 32, 33, ~0, #1, 48, 50, ~2, 62, '~~1, and 71, 3ohn Whey & Sons, New Park (1980).
Mull-tsya coons containing a fluorinated polymer enjoy wide industrial application; molt:-layer Ruoropolyrner constructions find utility in, far example, fuel line hoses and related containers and in retro8ective sheeting materials. Increased cocxerns with evaporative fuel sxandards give rise to a need for fuel system components that have increased barrier properties to iriuiirnize the permeation of fud vapors through automotive components including fuel filler lines, fuel supply lines, fuel tanks, and other cornporents ofthe engine's f4ei system control system. Various types of constructions have lien proposed to address tl~se concerns. fn general, the most successful ofthese are co-extrsuied mufti-layer constructions.
Mufti-layer compositions comprising a fluorinated polymer layer and $
palyamide or palyolefsn layer are known. U.S. Pat. No, 4,933,090 ~lKrevor), for example, discloses laminate tubular articles that can comprise layers of fluoroca.-bon elastomers, and P'CT Publication '9V0 93114933 (LaCourt) discloses a lamir~a.r film 2t? structure comprising a poVyirnide and a fluoropolymer. The use of fluorinated polymers in rctrosefiective sheeting also is known. 11.5. Pat. Nos. 3,551,025 and 4,348,312, for example, desrn'be products that include glass rnicrospheres, and PCT
WO 9511 14f~ and WO 95l11464 descn'be products containing retrorellective cube corner arrays.
ZS A variety of methods c~ be used to intxease the adhesion between a fluorinated polymer layer and a potyamide or polyotefin layer. An aa9hesive layer caa, for exempla, ise added between the two polymer layers. U. S. Pat. No.
S,E~47,287 discloses a disphragrn, sciitable for use in automotive applications, that comprises a base fabric having bonded to at least one surface a fluororubber layer 30 by an adhesive that includes an acrytonitrile-butadiene or acrylonitrile-isoprene rubber having an amino group.
_Z_ At~~~iQFD Sf~Et WO 99/529'75 PCTlUS98/17556 Surface treatment of one or both of the layers also sometimes is employed to aid bonding. Some, for example, have taught treating fluoropolymer layers with charged gaseous atmosphere {e.g., corona treatment) and subsequently applying a layer of a second material, for example a thermoplastic polyamide. E.g., European Patent Applications 0185590 (Ueno et al.) and 0551094 (Krause et al.) and U.S.
Pat. Nos. 4,933,060 (Prohaska et al.) and 5,170,011 (Martucci).
Blends of the fluoropolymer and the dissimilar layer themselves are in some cases employed as an intermediate layer to help bond the two layers together.
European Patent Application 0523644 (Kawashima et al.) discloses a plastic laminate having a polyamide resin surface layer and a fluororesin surface layer. The reference recognizes the difficulties encountered when making laminates having a polyamide layer and a fluororesin layer because of the incompatibility of the two materials. The laminate of the reference is prepared by use of an intermediate layer composed of a blend of an aliphatic polyamide resin with a fluorine-containing graft copolymer. .
The addition of a di- or polyamine as an auxiliary bonding agent to a "tie"
layer that comprises the dissimilar, non-fluorinated polymer also has been suggested to increase the degree of chemical bonding between the fluoropolymer and the non-fluorinated layer. Such methods generally employ those fluoropolymers and non-fluorinated polymers having some measure of reactivity with the di- or polyamine to achieve an acceptable level of adhesion. Many non-fluorinated polymers that are reactive with a di- or polyamine can, however, sufl'er a significant change in physical properties by the amine reaction when employed to construct such tie layers;
polyurethanes, for example, can suffer a significant degradation in melt viscosity in the presence of even a minimal amount of a di- or polyamine, leading to a viscosity differential between the tie-layer it comprises and the other layers that can make it prohibitively difficult to co-process the multiple layers. Another significant drawback to the use of such tie layers lies in the presence of the di- or polyamine itself. The di- or polyamine also can be a difficult material to handle directly in any process, and any method that decreases or eliminates the necessity of direct contact with a di- or polyamine presents a substantial benefit to the art. There also is an ever-present need to expand the range of materials useful in such bonding techniques to allow for a broader, more cost effective choice of materials from which to make composite structures.
SUMMARY OF THE INVENTION
Briefly, in one aspect, this invention provides a method of bonding fluoropolymer to substantially non-fluorinated polymeric material, the method comprising the steps of (a) blending carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefin with a suitable organic or inorganic base and an organo-opium compound that is stable in the presence of the base to form a substantially non-fluorinated polymeric material;
(b) providing a fluoropolymer;
(c) forming a mufti-layer article comprising a substantially non-fluorinated layer made of the substantially non-fluorinated polymeric material in contact with a fluorinated layer made of the fluoropolymer and exposing the mufti-layer article to temperature and pressure conditions suil'~cient to bond the layers.
In other aspects, the present invention provides mufti-layer constructions, including retroreflective sheeting, adhesive articles, and fuel fine hoses and related components, comprising mufti-layer articles made according to the above-described methods.
In another aspect the invention provides a bonding composition useful to adhere two dissimilar materials to one another, said composition comprising substantially non-fluorinated polymeric material that comprises a blend of carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefin with a suitable organic or inorganic base and an organo-opium compound that is stable in the presence of the base.

In practice of the invention, the use of a "tie" comprising a carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefin, an organo-onium compound and an inorganic base provides a mechanism for bonding a wide array of substantially non-fluorinated polymeric materials to layers composed of fluoropolymers. The substantially non-fluorinated polymeric layers containing such a tie layer also are processable with a fluoropolymer layer and exhibit resulting physical properties that meet or exceed the properties inherent to the polymers that comprise the composite structure.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
Fluoropolymer materials useful in the present invention include those fluoropolymers broadly categorized structurally into two basic classes. A
first class includes those thermoplastic and elastomeric fluorinated polymers, homopolymers, copolymers, terpolymers, etc, comprising interpolymerized units derived from vinylidene fluoride (sometimes referred to as "VF2" or "VDF"). Preferably fluoropolymer materials of this first class comprise at least 3% by weight of interpolymerized units derived from VF2. Such polymers may be homopolymers of VF2 or terpolymers and copolymers of VF2 and other ethylenically unsaturated monomers.
VF2-containing polymers and copolymers can be made by well-known conventional means, for example by free-radical polymerization of VF2 with or without other ethylenically-unsaturated monomers. The preparation of colloidal aqueous dispersions of such polymers and copolymers is described, for example, in U.S. Pat. No 4,335,238. It follows the customary process for copolymerizing fluorinated olefins in colloidal aqueous dispersions, which is carried out in the presence of water-soluble initiators that produce free radicals, such as, for example, ammonium or alkali metal persulfates or alkali metal permanganates, and in the presence of emulsifiers, such as, in particular, the ammonium or alkali metal salts of perfluorooctanoic acid.
Useful fluorine-containing monomers include hexafluoropropylene ("HFP"), tetrafluoroethylene ("TFE"), chlorotrifluoroethylene ("CTFE"), 2--S-chloropentafluoro-propene, perfluoroalkyl vinyl ethers, e.g. CF~OCF=CF2 or CF3CFZOCF=CF2, 1-hydropentafluoropropene, 2-hydro-pentafluoropropene, dichlorodifluoroethylene, trifluoroethylene, 1,1-dichlorofluoroethylene, vinyl fluoride, and perfluoro-1,3-dioxoles such as those described in U.S. Pat. No.
4,558,142 (Sduire). Certain fluorine-containing di-olefins also are useful, such as perfluorodiallylether and perfluoro-1,3-butadiene. Said fluorine-containing monomer or monomers also may be copolymerized with fluorine-free terminally unsaturated olefinic comonomers, e.g., ethylene or propylene. Preferably at least 50% by weight of all monomers in a polymerizable mixture are fluorine-containing.
Said fluorine-containing monomer may also be copolymerized with iodine- or bromine-containing cure-site monomers in order to prepare peroxide curable polymer. Suitable cure-site monomers include terminally unsaturated monoolefins of 2 to 4 carbon atoms such as bromodifluoroethylene, bromotrifluoroethy1ene, iodotrifluoroethylene, and 4-bromo-3,3,4,4-tetrafluoro-butene-1.
Commercially available fluoropolymer materials of this f rst class include, for example, T.HV 200 fluoropolymer (available from Dyneon LLC of Saint Paul, ~, THV S00 fluoropolymer (also available from Dyneon LLC), KynarTM 740 fluoropolymer (available from Elf Atochem North America, Inc.), Fluorel'I'"~
FC-2178 fluoropolymer (available from Dyneon LLC) and those fluoropolymers sold under the "Viton" tradename by DuPont.
A second class of fluorinated material useful in the practice of the invention broadly comprises those thermoplastic and elastomeric fluorinated polymers, copolymers, terpolymers, etc, comprising interpolymerized units derived from one or more of hexafluoropropylene ("HFP") monomers, tetrafluoroethylene {"TFE") monomers, chlorotrifluoroethylene monomers, and/or other perhalogenated monomers and further derived from one or more hydrogen-containing and/or non-fluorinated olefinically unsaturated monomers. Useful oleflnically unsaturated monomers include alkylene monomers such as ethylene, propylene, 1-hydropentafluoropropene, 2-hydropentafluoropropene, vinylidene fluoride, etc.
Fluoropolymers of this second class can be prepared by methods known in the fluoropolymer art. Such methods include, for example, free-radical polymerization of hexafluoropropylene and/or tetrafluoroethylene monomers with non-fluorinated ethylenically-unsaturated monomers. In general, the desired olefinic monomers can be copolymerized in an aqueous colloidal dispersion in the presence of water-soluble initiators which produce free radicals such as ammonium or alkali S metal persulfates or alkali metal permanganates, and in the presence of emulsifiers such as the ammonium or alkali metal salts of perfluorooctanoic acid. See for example U.S. Pat. No 4,335,238.
Representative of the fluoropolymer materials of the second class are poly(ethylene-co-tetrafluoroethylene) (ETFE), poly{tetrafluoroethylene-co-propylene), poly(chlorotrifluoroethylene-co-ethylene) (ECTFE), and the terpolymer poly(ethylene-co-tetrafluoroethylene-co-hexafluoropropylene), among others;
all of which may be prepared by the above-described known polymerization methods.
Many useful fluoropolymer materials also are available commercially, for example from Dyneon LLC under the trade designations Hostaflon't'M Xb810, and X6820;
from Daikin America, Inc., under the trade designations NeoflonTM EP-541, EP-521, and EP-610; from Asahi Glass Co. under the trade designations AflonTM COP
CSSA, CSSAX, C88A; and from DuPont under the trade designations TefzelTM 230 and 290.
The above-described fluoropolymers may be blended with one another or blended with another fluorinated or non-fluorinated polymer to form a composite blend material useful to construct a fluorinated layer. Polyvinylidene fluoride, for example, may be blended with polymethylmethacrylate. The described fluoropolymers may also be dehydrofluorinated according to the method described in WO 98/08879.
The substantially non-fluorinated, or "tie," layer of the invention comprises, in its most essential aspect, a melt-processable, carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefin, one or more organo-onium compounds and a suitable organic or inorganic base. One or more additional non-fluorinated polymers miscible with the a melt-processable, carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefin may also be blended into the tie layer. Some amount of one or more _7_ WO 99!52975 PCTIUS98/17556 aliphatic di- or polyamines also may be added to the tie layer to further improve its bonding properties. The tie layer material, comprising the above components along with any additional adjuvants, may be made by melt mixing the components in accordance with conventional methods as a batch process or by a twin screw extruder as a continuous process.
The above components may be compounded together according to any conventional method, for example in a bowl mixer or other such tool, to form the substantially non-fluorinated material. Typically, the components will be compounded such that the carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefin comprises between about 80 and about 99.8 percent of the blend by weight. The organo-opium typically will comprise between about 0.1 and about 5 weight percent of the blend, and the base typically will comprise between about 0.1 and about 10 percent of the blend by weight.
Any of a broad class of organic and inorganic bases may be employed to blend with the carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefin in the manner described above. Such classes of bases incll<de those depicted by any one of the formulas:
X+ (OH) n X+ (OR)'"
X+ (OCY2Rp)'"
X+ '(ORO)' X+
X' '(OCYZR~ CY20)' X+
X+ (OSi(R)3)'"
X+ (SC(O)R)'~
where:
n is 1 or 2;
_g_ X is a monovalent or divalent alkali or alkaline earth ion, preferably potassium or sodium;
R is a substituted or unsubstituted alkyl, aryl, allyl, aralkyl or arallyl group that may contain one or more catenary or noncatenary heteroatoms such as nitrogen, sulfur and oxygen, and that may contain linear or branched and cyclic or acyclic segments; R preferably contains no more than about six carbon atoms;
Rf is a partially or fully fluorinated, substituted or unsubstituted alkyl, aryl, allyl, aralkyl or arallyl group that also may contain one or more catenary or noncatenary heteroatoms such as nitrogen, sulfur and oxygen, and that may also contain linear or branched and cyclic or acyclic segments;
like the above-defined R group, Rf preferably contains no more than about six carbon atoms; and each Y is independently a hydrogen atom or is an R or Rf group as above-defined with the proviso that both Y groups are not Rf.
Other bases useful in practice of the invention include the sodium salt of 4,4'-hexafluoroisopropylidenyl bisphenol ("Na2BF6"), carbonate salts, and sodium sulfide.
Any among a large class of organo-onium compounds that are stable in the presence of the chosen base are useful for incorporation into the substantially non-fluorinated polymeric material. As is known in the art, an organo-onium is the conjugate acid of a Lewis base {e.g. phosphine, amine and ether) and can be formed by reacting said Lewis base with a suitable alkylating agent (e.g., an alkyl halide or acyl halide) resulting in an expansion of the valence of the electron donating atom of the Lewis base and a positive charge on the organo-onium compound. Many of the organo-onium compounds useful in the present invention contain at least one heteroatom, i.e., a non-carbon atom such as N, P, O, bonded to organic or inorganic moieties. One class of quaternary organo-onium compounds particularly useful in the present invention broadly comprises relatively positive and relatively negative ions wherein a phosphorus, arsenic, antimony or nitrogen generally WO 99/5x975 PCTIUS9$/1~556 comprises the central atom of the positive ion, and the negative ion may be an organic or inorganic anion (e.g., halide, sulfate, acetate, phosphate, phosphonate, hydroxide, alkoxide, phenoxide, bisphenoxide, etc.). Because of their relative stability in the presence of most inorganic bases, phosphoniums are the most S preferred organo-oniums for use in the present invention. Sulfoniums are not chemically stable in the presence of most useful organic and inorganic bases and therefore are not considered useful in the invention.
Many of the useful organo-onium compounds are described and known in the art. See, for example, U.S. Pat. Nos. 4,233,421 (Worm), 4,912,171 (Grootaert et al.), 5,086,123 {Guenthner et al.), and 5,262,490 (Kolb et al.) all of whose descriptions are herein incorporated by reference. Fluorinated oniums, such as those described in U.S. Pat. No. 5,591,804 {Coggio et al.), and multifunctional oniums, such as those comprising two or more onium groups in the same molecule (e.g., bis-phosphoniums) may also be employed. Representative examples include the following individually listed compounds and mixtures thereof triphenylbenzyl phosphonium chloride tributylallyl phosphonium chloride tributylbenzyl ammonium chloride tetrabutyl ammonium bronude 8-benzyl-1,8-diazabicyclo [5,4,0]-7-undecenium chloride benzyl tris(dimethylamino) phosphonium chloride benzyl(diethylamino)diphenylphosphonium chloride Any melt-processable, carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefin may be used to make the substantially non-fluorinated polymeric material of the invention.
Polyolefins, e.g., polymers of ethylene, propylene, acrylic monomers, other higher oc-olefins, or other ethylenically unsaturated monomers, may be fixnctionalized by homopolymerization of functional olefin monomers or by co-polymerization of non-functional olefin monomers with functional monomers, for example, with acrylic acid or malefic anhydride, vinyl acetate, etc. PolyoIefins may also be modified, or functionalized, after polymerization, for example by grafting, by oxidation or by forming ionomers.

WO 99/52975 PCTNS98/1'7556 Such polymers and copolymers can be prepared by conventional free-radical polymerization or catalysis of such ethylenically unsaturated monomers. The degree of crystallinity of the hydrocarbon polymer or copolymer can vary; the polymer may, for example, be a semi-crystalline high density polyethylene or may be an elastomeric copolymer of ethylene and propylene. Representative of such substantially non-fluorinated polymer useful in the present invention include, but are not limited to, co- and terpolymers of the above-listed functional monomers with, for example, propylene, ethylene, vinyl acetate, etc. The carboxyl, anhydride, or imide functional polymers useful as the hydrocarbon polymer generally are commercially available. Anhydride modified polyethylenes, for example, are available commercially from the E.I. DuPont DeNemours Co., Wilmington, DE, under the trade designation "BYNEL," and useful oxycarboxy functional polyethylenes are available under the tradename "ELVAX" also available from DuPont.
Blends of one or more of the carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefins may be blended together or with other suitable polymers to find utility in forming the substantially non-fluorinated Layer or layers of the invention.
The polymeric layers comprising the composite structures of the invention, including the tie layer described above, may include optional additives, such as those typically used in other thermoplastic applications. Such additional adjuvants include, for example, pigments, tackifiers, fillers, electrically conductive materials (such as those described in U.S. Patent 5,552,199), electrically insulative materials, stabilizers, antioxidants, lubricants, processing aids, impact modifiers, viscosity modifiers, as well as any appropriate mixture or mixtures thereof.
Methods known in the fluoropolymer art can be used to produce a bonded multi-layer article wherein a fluoropolymer material is in substantial contact with the substantially non-fluorinated polymeric blend material. For instance, the fluoropolymer and the substantially non-fluorinated polymeric material can be formed into thin film layers by known methods. The fluorinated layer and the substantially non-fluorinated layer can then be laminated together under heat andlor pressure to foam a bonded, mufti-layer article. Alternatively, the fluoropolymer and the substantially non-fluorinated polymeric blend material, along with one or more additional layers where desired, can be co-extruded into a mufti-layer article. See e.g., U.S. Pat Nos. 5,383,087, and 5,284,184, whose descriptions are incorporated herein by reference for such purpose.
The heat and pressure of the method by which the layers are brought together (e.g., coextrusion or lamination) may be sufficient to provide adequate adhesion between the layers. It may, however, be desirable to further treat the resulting mufti-layer article, for example with additional heat, pressure, or both, to provide additional adhesive bond strength between the layers. One way of supplying additional heat, when the mufti-layer article is prepared by extrusion, is by delaying the cooling of the mufti-layer article after co-extrusion.
Alternatively, additional heat energy may be added to the mufti-layer article by laminating or coextruding the layers at a temperature higher than necessary for merely processing the several components. Or, as another alternative, the finished mufti-layer article may be held at an elevated temperature for an extended period of time. For example the finished mufti-layer article may be placed in an oven or heated liquid bath or a combination of both.
Similar methods may also be employed to produce a bonded mufti-layer article where the substantially non-fluorinated polymeric blend material is in substantial contact with a dissimilar non-fluorinated material.
The methods of the present invention provide mufti-layer articles exhibiting ease of processability and improved inter-layer adhesive bond strength between a fluorinated layer and a substantially non-fluorinated layer or between two substantially dissimilar non-fluorinated layers. Mufti-layer articles of the invention can have utility as films, containers, or tubing that require specific combinations of barrier properties, high and low temperature resistance, and chemical resistance.
Such methods and compositions are particularly useful for making mufti-layer articles comprising a fluoropolymer material suitable for use in motor vehicles, for example as fuel-line hoses, and for films and blow-molded articles such as bottles, where chemical resistance and barrier properties are important.

WO 99/529'IS PCT/US98/17556 The mufti-layer articles can have two, three, or even more separate layers.
For example, the present invention contemplates a mufti-layer article including a fluorinated layer, a substantially non-fluorinated layer, and optionally further comprising one or more additional layers comprising fluorinated or non-fluorinated S polymers. As a specific example, a bi-layer article can be prepared according to the present invention, the bi-layer article comprising a fluorinated layer and a substantially non-fluorinated layer containing the amine-functionalized base polymer, where the bonding composition is used to increase the adhesive bond strength between the two layers. One or more additional layers comprising fluorinated or non-fluorinated polymer can, either thereafter or simultaneously (i.e., to form a tri-layer article), be bonded to one or more of the fluorinated layer or substantially non-fluorinated layer, to produce a mufti-layer article having three or more layers.
Any appropriate fluorinated or non-fluorinated polymeric material may be 1 S utilized as an additional layer; useful among them are any of a number of well known, hydrocarbon-based polymers. Thermoplastic polyamides, polyurethanes, polyolefins, polyesters, and acrylate and methacrylate polymers and copolymers find utility in such embodiments. Any of the previously-described fluoropolymers may also be added to the mufti-layer articles of the invention.
The methods of the invention prove particularly advantageous in producing a composite structures of three or more layers where at least one of the additional layers is an unfunctionatized polyolefin, e.g., a linear low or high density polyethylene. Such unfunctionalized polyolefins typically are very difficult to adhere to directly or indirectly to fluorinated layers using conventional bonding methods.
Utilizing technidues of selection, a mufti-layer composite article may be constructed having the combined benefits of each constituent layer. For instance, a fluoropolymer that exhibits particular advantage in bonding to a chosen substantially non-fluorinated polymeric material (such as the commercially available THVTM
200) may be used as the fluoropolymer layer immediately adjacent to the layer of substantially non-fluorinated polymer, and a fluoropolymer exhibiting relatively w.~: s :'v ii i~..:. ~ . ... ~~ _~.. _ __ _._ _ "y yvv a .. . .r.r -ul -: :.
_~~ v~- n .... . ~ ~w ~ "v ~~"~ CAv02325714v200~0-09-25 superior vapor banria properties C~ch as the comtnacially available THVT" 500) may be bonded to the inunadiate 8uoropolymer layer. A composite so formed possesses the eombined advantages of 'its constituent layers: superior bond strength and superior vapor barrier properties.
T~nsparent embodirnema of mufti-layer c~positioa~s of the present irtveation may find pastiwlar utility in the constiucxian of rdtareflective sheeting articles generally, and Pam~~y when resistance to chemical agents, solvents, g~ and!!or reduced moisture vapor transmission andfor good interlayer adhesion ~ fl~bda sheexings subject to severe bending and flexing is required.
The compositions of this invexition tray be readered retroreflective by forming retrore~Ctive elernems on one side of the composition, or alternatively, by attaching a retroreflective base shed by means of a transparent adhesive or by direct lamination, The retrore~lective base sheet may comprise a member with cube corner retrore8ocxive elements or may comprise a microspl~re-based retroreflective st~uc~re, e.g. comprising s monolayer of transparent nucrospheres and reflective means disposed on the opposite side of the monalayer front the mufti-layer composition. It is preferred that the base layer is disposed on a non-fluoropolvmer layer of the muhi-layer composition. An embodiment of this invention i.~tcludes the a,~pretrore8ective sheeting ~i~~ ~ ~ d<s~o~ ~ U.g. Patent Na.
2D 3, t 90,178, in which the cover layer is provided by a muhi-layer composition according to the present invention.
Retroreflective articles of the invention may be made in rigid or flexible form. ?vlulti-layer compositions of the present invention may be used as barrier layers. An embodiment ofthe present inveation incla~des articles in accordance with 25 U.S. Pat. No. S,Ob9,964 which is incorporated herein by reference, in wtuich ttrr plasticizar-resistant barrier layer comprises a multi~laycr c~srrtposition in accordance with the present invention. The mufti-layer compositions of the present invention may fend particular utility in the canstiuction of fleauble retmrefleotive sheeting articles. A preferred embod'unent of the present invention includes a retroreflective ~oja ~ ~~~ y,~ p~ ~l0 9511144 or Wa 95111, both of which are incorporated herein by reference, wherein the dex~'blc overlay film described in :~i~~~~t~i:~ ~i-rind' _. _ __ __ _ __ _.__ y ..,... ,. ,.... ., .:..."' -..-: .-. .... ~ -,~I . ~r ,.~
CA~023257~14v2000-09-25 PCT WO 95111464 ur the fl~dbie body layer ofW~ 95Jt 1466 is constituted by a ,~lti-l:ya eor~aposition in s~rardance with the invention. Suitmble fluoropotyniers ~~n8 ;~rpolymerized units of vnylidenc fluoride of t~ type specif ed for use with flexible oher~ing ist accordaEace with these two pateait applications may be poly(vinylidene fluorsde-co-6~exatluoropropy3ene~, for e~rnple, ICynar Flex'-available from Elf Atod>erre North ~rmerica, lnc., Phaladetphia, Pennsylvania, os poly(tetrafluotoethyleno-co-hexaftuoropropylene-co-vinylidene fluoride), for example, T~ 200 or 500. The non-tluaropolymer layer in such constructions may be any of the non-8uoropo~ specafied in the above patent applications, for exaaa>ple, ionomeric dhylene copo3ymers, low density polyethylenes, polyethylene copolymers, or aliphatic or aromatic polyurethanes or far compounds. For highly flexible products, a mufti-layer composition of this invention that includes a THV layer and a polyurethane layer is particularly preferred. The microstructure elements including either solidly connected or segregated cube corners may be 1 S easiaroeeplxsted, preferably onto the non-8uoropofyma layer. ~lterradveiy, the ~~.~ya ~mpositiQns array be adhered to microstructure elements. As will be understood, any conveartional foran of retroreflective anicrostructure elements rnay be used including, for example, arrays flf canted, tiled, specially shaped, colored, or colorless cube corner elements.
Similarly, mufti-1$yer compositions array be used with retroreflect'rve sheeting products including microspheres in a base layer. Specific embodimesdts of the invention include retroretltctive articles according to U.S. Pat htos.
4,896,943, U.S.
Pat No. 4,025,159 or U.S. Fat No. S,Ofi6,098, all of which are included herein by ~f~Ce, is which the cover film ofU.S. Pat Nos. 4,896,943 ar 4,02~,I59 or the cover sheet of U.S. Pat No. x,066,098 is constituted by a anulti-layer composition in arcords3ace with this invention. The mufti-layer compositions of the present irntention further array theanselves include retroreflective mocro-e8em~ts, such as traasspareaat anicrospheres, incorporated into the fluoropolyazder or the non-fiuoropoiyrnet layer, for example in a further embodiment of the present inveaition, 38 the $uoropolymer layer of a mufti-layer composition according to the present ~vention may constitute the continuous overlaying transparent topcoat of U. S.
Pat.

~i~=~~! ~E~ SH~ETi No. 3,551,025 which is incorporated here by reference and the non-fluoropolymer layer may constitute the binder of the same.
The adhesive articles taught by the present invention comprise an adhesive layer composed of an adhesive material disposed as the outer layer of the multilayer composite constructions already described, and such articles may find particular utility as paint replacement films. Any of a wide variety of adhesives may be usefully incorporated into such articles, including those which are thermoplastic (fusible), thermosetting (cure to a crosslinked state), or combinations of both. One particular class of adhesives are those which are pressure-sensitive in nature. That is, they display permanent and aggressive tackiness to a wide variety of substrates at room temperature. Many pressure-sensitive adhesive materials are known in the adhesive art, and those that are suitable may comprise acrylate esters, acrylamides, thermoplastic elastomers, natural rubbers, olefins, silicones, vinyl ethers, esters, urethanes, etc., as well as selected polymers, and copolymers of these materials, and mixtures thereof. The actual choice of the adhesive is largely dependent on the end use to which an artisan will apply the final adhesive article. Some useful pressure sensitive adhesives are described, for example, in U.S. Patent Nos. Re.
24,906, 4,112,213, 4,323,557. Those skilled in the art will recognize that the aforementioned adhesive components might also include various chemical modifiers so as to provide utility required by a particular application; e.g., tackifiers, crosslinkers, stabilizers, initiators, etc.
Also useful are various thermosetting adhesives that can cure, for example, upon exposure to moisture, heat, radiation, etc. to an infusible, crosslinked state.
Useful thermosetting adhesives include those formed by addition polymerization methods from, for example, unsaturated polyesters, epoxies, urethanes, cyanoacrylates, as well as mixture of these components or polymers, copolymers, graft copolymers, and interpenetrating networks comprising these components.
Further information about many different types of adhesive may be found in I.
Skeist, Ed., Handbook of Adhesives, Third Edition, 1990.
To apply an adhesive layer to the substrate backing material, any known coating method can be used, such as gravure coating methods, spray coating methods, die coating methods such as curtain coating and fluid bearing die methods, hat melt coating methods, etc. The particular method chosen can depend on the type of adhesive chosen (i.e., a structural adhesive versus a pressure sensitive adhesive) as well as the chemistry of the chosen adhesive. Optionally, after the adhesive is applied to the substrate, the adhesive layer can be cured by known methods such as by exposure to radiation, heat, moisture, etc.
Other embodiments of the adhesive articles provided herein comprise three or more additional layers, positioned on either the opposing surface of a fluorinated or substantially non-fluorinated layer, onto at least one of the outer layers of which is placed an adhesive material. It will be understood that where one or more said additional layers comprise a substantially non-fluorinated polymer, that additional layer also can contain bonding composition. This would prove useful, for example, where a fluoropolymer layer is "sandwiched" between two dissimilar polymeric layers, and to bond the three layers together, both dissimilar layers contacting the fluorinated layer could contain bonding composition. Additional layers may then be placed on either or both sides of such a construction.
In another specific embodiment of the invention, the adhesive article can find application as a drag reducing article such as a drag reduction film.
In such an application, a fluoropolymer layer is formed into a drag reducing patterned layer before, during, or after bonding to one or more layers of the article.
Such a drag reducing patterned fluoropolymer layer may be prepared, for example, by extruding or coating the fluoropolymer onto a patterned sheet or roll. When the fluoropolymer is removed from the patterned sheet or roll, a surface of the fluoropolymer will be formed into a drag reducing pattern. The non-patterned surface of the patterned fluoropolymer layer is bonded to other layers, including the substantially non-fluorinated layer, to produce a drag reducing adhesive article.
Such a drag reducing adhesive article can reduce the resistance to drag created by a fluid (e.g., air, gas, water, etc.) flowing across the patterned fluorinated layer. The outer, exposed surface of such an article is provided with a drag reducing pattern.
While a variety of waveforms may be employed to produce the patterned layer, those that are preferred typically comprise a series of essentially parallel peaks separated by a series of essentially parallel valleys. The patterned surface may be a symmetric saw tooth pattern an which each of the peaks are identical as are each of the valleys, although parallel peaks of different heights may be separated by a series of parallel valleys. The saw tooth pattern may also comprise alternating, parallel, S asymmetric peaks separated by a series of parallel, asymmetric valleys.
The dimensions of the peaks and valleys are not critical provided that whatever patterned surface is employed, it provides a desired reduction in drag.
The optimum dimensions are somewhat dependent upon the speed at which the body to be covered passes through the fluid (or the speed at which the fluid passes over the body). It has been found that peaks having a height of about 10 to microns (about 0.4 to 10 mils) are useful. Within this range it is preferred that the peaks be about 20 to 150 microns (about 0.8 to 6 mils) high for high speed uses {e.g., aircraft). The peak-to-peak spacing between adjacent peaks can likewise vary depending upon, for example, the application of the article. A spacing of about 10 to 250 microns (about 0.4 to 10 mils) is useful, although, for aircraft applications, a spacing of about 20 to 150 microns (about 0.8 to 6 mils) is preferred. The included angle between adjacent peaks can also vary. While flat and round bottom valleys may be useful, it is preferred that the valleys and peaks be generally V-shaped and have an included angle of from 15° to 140°, more preferably from 50° to 60°.
The drag reduction articles of the invention may readily be applied to a variety of bodies to reduce the drag experienced when that body moves through a fluid medium or when a fluid moves past the body. Preferably the article is positioned on the body such that the patterned surface will provide maximum drag reduction. When the patterned surface comprises essentially parallel peaks and valleys, maximum drag reduction is achieved when the peaks and valleys are generally parallel to the fluid flow. Bodies to which the drag reducing article may be applied include the surface of an airplane, the hull of a boat or other watercraft, the surface of the motor vehicle, or the interior surface of a fluid-conveying conduit.
The patterned adhesive articles of the invention also may be used as patterned paint replacement films and may also be employed to achieve certain desired optical WO 99/52975 PC'TlUS98117556 effects that can be utilized to alter the appearance of the body onto which they are applied.
The following examples are offered to aid in the understanding of the present invention and are not to be construed as limiting the scope thereof.
Unless otherwise indicated, all parts and percentages are by weight.
EXAMPLES
TEST PROCEDURES
Peel Stren tg_h Peel strength of laminated samples was determined following the test procedures described in ASTM D-1876 entitled "Standard Test Method for Peel 1 S Resistance of Adhesives," more commonly known as the "T-peel" test. Peel data was generated using an InstronTM model 1125 tester (available from Instron Corp., Canton, MA) equipped with a Sintech Tester 20 (available from MTS Systems Corporation, Eden Prairie, Ml~. The Instron tester was operated at a cross-head speed of 100 mm/min. Peel strength, which is reported in kg/2.54 cm width as an average of at least three samples, was calculated as the average load measured during the peel test.
TIE-LAYER PREPARATIONS
Example 1 A tie-layer composition consisting of a mixture of ElvaxTM-250 (23.5 g, an ethylene/vinyl acetate copolymer available from E.I. DuPont DeNemours Co., Inc., Wilmington, DE), potassium hydroxide (1.0 g) and tetrabutyl phosphonium bromide (~nium# 1, 0.5 g, available from Aldrich Chemical Co., Inc., Milwaukee, WI ) was compounded in a PlasticorderT"' (an internal bowl mixer equipped with roller blades, available from C.W. Brabender Instuments, Inc., South Hackensack, Nn at 200 °C for 10 minutes at a mixing rate of 60-70 revolutions per minute (rpm).
After mixing, a portion of the compounded material was pressed into a 0.20 mm thick film by pressing between TeflonT~" cloth at 200 °C in a Wabash Hydraulic Press at approximately 30 KPa pressure for approximately 30 seconds. The film was cut into 1.25 cm x 5.08 cm coupons for subsequent conversion into peel test specimens.
Example 2 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of ElvaxTM-250 (23.5 g), potassium hydroxide (0.5 g), and tetrabutyl phosphonium bromide (0.2 g).
Example 3 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted ofElvax-350 (20 g), sodium methoxide (0.25 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 4 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding rriixture consisted of Elvax-350 (20 g), sodium methoxide (0.2 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 5 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of Elvax-450 (20 g), cesium hydroxide (1.3 g of a 50% aqueous solution) and tetrabutyl phosphonium bromide (0.2 g).
Example 6 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of Elvax-450 (20 g), sodium methoxide (0.25 g) and tetrabutyl phosphonium bromide (0.2 g).

WO 99152975 PC'f/US98/17556 Example 7 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of Elvax-450 (20 g), potassium hydroxide (0.2 g) and tetrabutyl phosphonium bromide (0.2 g).
S
Example 8 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of Elvax-450 (20 g), potassium hydroxide (0.1 g) and tetrabutyl phosphonium bromide (0.1 g).
Example 9 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of Elvax-450 (20 g), potassium hydroxide (0.2 g) and tetrabutyl phosphonium bromide (0.1 g).
Example 10 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of Elvax-450 (20 g), potassium thioacetate (available from Aldrich Chemical Co., 0.6 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 11 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of Elvax-450 (20 g), sodium trimethylsilanolate (available from Aldrich Chemical Co., 1.0 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 12 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of Elvax-450 (20 g), sodium phenoxide (available from Aldrich Chemical Co., 0.4 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 13 S A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of AT1841 (23.5 g, an ethylene/vinyl acetate copolymer available from AT Polymer , Edmonton, Canada), potassium hydroxide ( 1.0 g) and tetrabutyl phosphonium bromide (0.5 g).
Example 14 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of AT1841 (23.5 g), potassium hydroxide (0,2 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 15 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of AT1841 (23.5 g), potassium hydroxide (0.1 g) and tetrabutyl phosphonium bromide (0.1 g).
Example 16 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of AT1841 (23.5 g), sodium hydroxide (1.0 g) and tetrabutyl phosphonium bromide (0.5 g).
Example 17 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-1123 (20 g, an acid modified ethylene/vinyl acetate copolymer, available from E.I. DuPont DeNemours, Inc., Wilmington, DE), potassium hydroxide (0.2 g) and tetrabutyl phosphonium bromide {0.2 g).

WO 99/52975 PCTIUS98f17556 Example 18 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-3101 (20 g, an acid modified ethylene/vinyl acetate copolymer, available from E.I. DuPont DeNemours, Inc., Wilmington, DE), potassium hydroxide (0.1 g) and tetrabutyl phosphonium bromide (0.1 g).
Example 19 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-3101 (20 g), potassium hydroxide (0.2 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 20 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-31 O 1 (20 g), sodium phenoxide (1.0 g, available from Aldrich Chemical Co.) and tetrabutyl phosphonium bromide (0.2 g).
Example 21 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-31 O1 (20 g), sodium phenoxide (0.6 g, available from Aldrich Chemical Co.) and tetrabutyl phosphonium bromide (0.2 g).
Example 22 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-3101 (20 g), sodium pares-chlorophenoxide (1.0 g, available from Aldrich Chemical Co.) and tetrabutyl phosphonium bromide (0.2 g).

Example 23 . A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-3101 (20 g), sodium trimetylsilonate (0.2 g, available from Aldrich Chemical Co.) and tetrabutyl phosphonium bromide (0.2 g).
Example 24 A tie-layer composition was prepared substantially as described in Example I except that the compounding mixture consisted of BynelTM-3101 (20 g), sodium 2,2,2-trifluoroethoxide (2.0 g) and tetrabutyl phosphonium bromide (0.2 g, prepared by the reaction of 2,2,3,3,3-pentafluoropropanol with an equivalent weight of sodium methoxide at room temperature and subsequently removing the methanol in a rotary evaporator).
Example 25 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-3101 (20 g), sodium 2,2,2-trifluoroethoxide (0.5 g, prepared by the reaction of 2,2,2-trifluoroethanol with an equivalent weight of sodium methoxide at room temperature and subsequently removing the methanol in a rotary evaporator) and tetrabutyl phosphonium bromide (0.2 g).
Example 26 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-3101 (20 g), potassium carbonate (0.2 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 27 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-31 SO (20 g, a nominally 9713 parts by weight ethylene/acrylic acid copolymer, nominally 97/3 wt.%, available from Dow Chemical Co., Inc., Midland, MI), sodium methoxide (0.25 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 28 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-3150 (20 g), potassium hydroxide (0. I g) and tetrabutyl phosphonium bromide (0.2 g).
Example 29 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-31 SO (20 g), potassium hydroxide (0.2 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 30 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-3150 (20 g), potassium hydroxide (0.5 g) and tetrabutyl phosphanium bromide (0.2 g).
Example 31 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-31 SO (20 g), Na2BF6 salt ( I .0 g, prepared by the reaction of BF6 and two eqivalents of sodium methoxide and removing the methanol on a rotary evaporator) and tetrabutyl phosphonium bromide (0.2 g).
Example 32 A tie-layer composition was prepared substantially as described in Example I except that the compounding mixture consisted of PrimacorTM-3150 (20 g), sodium phenoxide (0.5 g) and tetrabutyl phosphonium bromide (0.2 g).

Example 33 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of Primacor'''M-3150 (20 g), potassium carbonate (1.0 g} and tetrabutyl phosphonium bromide (0.2 g).
Example 34 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-3460 (20 g, a nominally 91/9 parts by weight ethylene/acrylic acid copolymer, available from Dow Chemical Co., Inc.), potassium hydroxide (1.0 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 35 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-3460 (20 g), potassium hydroxide (0.5 g) and tetrabutyl phosphoruum bromide (0.2 g).
Example 36 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-3460 (20 g), sodium phenoxide (1.0 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 37 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-3460 (20 g), sodium 2,2,2-trifluoroethoxide (1.0 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 38 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-3340 (20 g, a nominally 93.5/6.5 parts by weight ethyleneJacrylic acid copolymer, available from Dow Chemical Co., Inc.), potassium hydroxide (0.5 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 39 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of EMAC 2220 (20 g, a nominally 80/20 parts by weight ethylene/methyl acrylate copalymer, available from Chevron Chemical Co., Houston, 'T3~, potassium hydroxide (0.2 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 40 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of EMAC 2220 (20 g), potassium hydroxide (0.4 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 41 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of EMAC 2220 (20 g), sodium phenoxide (0.5 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 42 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of EVAL 105 (20 g, an ethylene vinyl alcohol copolymer, available from Eval Company of Am., Lisle, IL), Na2BF6 salt ( 1.0 g) and tetrabutyl phosphonium bromide (0.2 g).
Example 43 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of EVAL 105 (20 g), potassium hydroxide (0.2 g) and tetrabutyl phosphonium bromide (0.2 g).

WO 99!52975 PCT/US98/17556 Example 44 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of AT 1841 (23 .5 g), potassium hydroxide ( 1.0 g) and tributyl methoxy propyl phosphonium chloride (Opium #2 , 0.9 g, available from Dyneon Corp., St. Paul, Ml~
Example 45 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of AT 1841 (23.5 g), potassium hydroxide ( 1.0 g) and (ethylcarboxymethyl) tributyl phosphonium chloride (Opium #3, 0.5 g, available from Dyneon Corp.).
Example 46 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of AT1841 {23.5 g}, potassium hydroxide (1.0 g) and tetraethyl phosphonium chloride (Opium #4, 0.5 g, available from Aldrich Chemical Co., Inc.).
Example 47 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of AT1841 (23.5 g), potassium hydroxide (0.2 g) and tetraethyl phosphonium chloride (0.2 g).
Example 48 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-3101 (20 g), potassium carbonate {0.2 g) and tetrabutyl phosphonium chloride (Opium #5, 0.2 8)~

Example 49 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-3101 (20 g), potassium tert-butoxide (0.4 g) and tetrabutyl phosphonium chloride (0.2 g).
Example 50 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of BynelTM-3101 (20 g), potassium tert-butoxide (0.4 g), potassium hydroxide (0.2 g), and tetrabutyl phosphonium chloride (0.2 g).
Example 51 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted ofElvaxTM-450 (10 g), PrimacorTM-3340 (10 g), potassium hydroxide (0.4 g), and tetrabutyl phosphonium bromide (0.2 g).
Example 52 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted ofElvaxTM-450 (10 g), EMAC
2220T ( 10 g), potassium hydroxide (0.2 g), and tetrabutyl phosphonium bromide (0.2 g).
Example 53 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-3150 ( 15 g), MorthaneTM L424.167, MI+9.8, an aliphatic polyurethane, available from Morton International, Chicago, IL, 5.0 g), potassium hydroxide (0.2 g) and tetrabutyl phosphonium bronvde (0.2 g).

WO 99/52975 PCT/US98~17556 Example 54 A tie-layer composition was prepared substantially as described in Example 1 except that the compounding mixture consisted of PrimacorTM-3150 (10 g), EMAC 220, 10 g), potassium hydroxide (0.4 g) and tetrabutyl phosphonium bromide (0.2 g).
Comparative Example C-1 ElvaxTM-250 pellets were pressed into a 0.20mm thick film by pressing between TeflonTM cloth at 200 °C for 30 seconds at approximately 30 kPa initial pressure. The resulting film was cut into 1.25 cm x 5.08 cm coupons for subsequent conversion into peel test specimens.
Comparative Example C-2 A tie-layer composition was prepared substantially as described in Example C-1 except that the compounding mixture consisted of AT1841 (23.5 g) and tetrabutyl phosphonium bromide (0.5 g).
Comparative Example C-3 A tie-layer composition was prepared substantially as described in Example C-1 except that the compounding mixture consisted of AT1841 (23.5 g) and potassium hydroxide ( 1.0 g).
Comparative Example C-4 AT1841 pellets were pressed into a 0.20mm thick film by pressing between TeflonTM cloth at 200°C for 30 seconds at approximately 30 kPa initial pressure.
The resulting film was cut into 1.25 cm x 5.08 cm coupons for subsequent conversion into peel test specimens.
Comparative Example C-5 EVAL 105 pellets were pressed into a 0.20mm thick film by pressing between TeflonTM cloth at 200°C for 30 seconds at approximately 30 kPa initial pressure. The resulting film was cut into 1.25 cm x 5.08 cm coupons for subsequent conversion into peel test specimens.
Peel Test Specimen Preparation Peel test specimens for the tie layer compositions of Examples 1-24 and comparative Examples C-1 through C-4 were prepared by laminating a film of the tie-layer formulation to a 0.2 mm thick film of THVTM 200 (a nominally parts by weight tetrafluoroethylene (TFE), hexafluoropropylene (HFP), vinylidene fluoride (VDF) terpolymer, available from Dyneon Corp.), THVTM 500 ( a nominally 40/20/40 parts by weight TFE/I~'P/VDF terpolymer, available from Dyneon Corp.), polyvinylidene fluoride (PVDF, available from Autochem Company of Glen Rock, NJ), linear low density polyethylene (LLDPE, available from Dow Chemical, Midland, MI) or high density polyethylene (HDPE, available from Dow Chemical) as indicated in Table 1. The unbonded laminate constructions were 1 S subjected to a pressure of approximately 1 kgf/cm2 (initial pressure) for a period of two minutes at 200°C in a Wabash Hydraulic Press. Tabs to grip the two film components of the laminate were provided by inserting a strip of silicone release paper (#7520, available from 3M Company, St. Paul, MN) between a portion of the tie-layer sheet and the THVTM 200 sheet to a depth of approximately 1.25 cm along one short edge of the laminate construction to prevent the two materials from bonding together. The laminate specimens were removed from the hot laminating press after 2 minutes and immediately transferred to a second press which was maintained at room temperature to provide consistent thermal history for all test samples. T-Peel data for all samples is reported in Table 1.

Table 1: T-Peel Data Adhesion to Substrate k 2.54 cm Tie Layer CompositionTHVT"' THVTM PVDF LLDPE HDPE

Ex. Com osition in 200 500 #

1 ELVAX 250/KOH/Onium#1Break' 3.8 0.9-1.45.5 5.9 23.5/1.0/0.5 2 ELVAX 250/KOH/Onium#1Break' 1.9 - 5.5 5.5 23.5/0.5/0.2 3 ELVAX 350/NaOMe/Onium#10.2 4.0 - - -(20/0.25/0.2 4 ELVAX 350/NaOMelOnium#1- - 0.7 -20/0.2/0.2 4a ELVAX 350/NaOMe/Onium#1- - 1.3 - -(20/0.25/0.2 2 ELVAX 450/CeOH/Onium#17.0 6.9 - - -(20/1.3/0.2 6 EL VAX 0.2 4.8 - - -450/NaOCH~/Oruum#

(20/0.25/0.2 7 ELVAX 450/KOH/Onium#5.1 Break 0.7 - -(2010.2/0.2 7a ELVAX 450/KOH/Onium#1- - 1.3 - -(20/0.2/0.2 3 8 ELVAX 450/KOH/Onium#1- 3.7 - - -(20/0.1/0.1 9 ELVAX 450/KOH/Onium#1- 7.4 - - -(20/0.1/0.1)3 ELVAX 450IPotassium - 0.7 - - -Thioacetate/Onium#1 20/0.6/0.2) 11 ELVAX 450/Sodium 1.7 7.0 - - -Trimethylsilanolate/Onium#

20/0.1/0.2) 12 ELVAX 450/Sodium - 5.3 - - -Sulfide/Onium#1 (20/0.4/0.2 13 AT1841/KOH/Onium#1 3.9 2.1 0.9-1.45.5 5.5 (23.5/1.0/0.5) 14 AT184I/KOH/Onium#1 0.6 3.9 - 5.5 5.0 (23.5/0.2/0.2) WO 99!52975 PCT/US98I17556 Table 1 lcont_L T-Peel Data Ad hesion 2.54 to Substrate cm c Tie Layer Composition THV''M THV~'"' PVDF LLDPE HDPE

Ez. Com osition in 200 500 #

15 AT1841IKOH/Onium#1 0.3 0.2 - 5.0 5.9 (23.5/0.1/0.1) 16 AT184I/NaOH/Onium#1 3.9 1.4 - - -23.5/1.0/0.5 17 Bynel-1123/NaON/Onium#1- 6.6 - -(20.010.2/0.2) 18 Bynel-3101/KOH/Onium#1 - 2.4 1.0 - -(20.0/0.1/0.1 18a Bynel-3 l O 1/KOH/Onium#- 2.4 4.3 - -(20.0/0.1/0.1 Z

19 Bynel-3101/KOH/Onium# - - 2.0 - -(20.0/0.2/0.2 2 20 Bynel-3101/Sodium 1.6 11.2 - - -Phenoxide/Onium#1 (20.0/1.0/0.2 21 . Bynel-3101/Sodium 1.4 2.2 - -PhenoxidelOnium# 1 (20.0/0.610.1 22 Byne1-31011Sodiump- 2.8 2.5 - - -Chlorophenoxide/Onium#

20.010.110.1 23 Bynel-3101/Sodium 1.3 5.4 - - -TrimethylsilanolateJOnium#1 (20.0/0.2/0.2 24 Bynel-3101/Sodimn 2,2,3,3,3-0.5 5.2 - - -Pentafluoropmpoxide/Onium#1 20.012.010.2 25 Hynel-3101/Sodium 2,2,20.4 2.1 - - --Trifluoroethoxide/Onium#

(20.0/0.5/0.2 26 Hyne1-3101/KOH/Onium# - 1.6 - - -(20.0//0.1/0.1 27 Primacor 3150/NaOCH~lOnium#16.1 0.2 - - -(20/0.25/0.2 28 Primacor 3150/KOHIOnium#13.5 0.7 - - -(20/0.1/0.2 29 Primacor 3150/KOH/Oruum#12.3 - - - -20/0.2/0.2 Tahle 1 (cont_1 T Peel Data Ad hesion bstrate2.54 to Su cm Tie Layer Composition THVTM THVT"' PVDF LLDPE HDPE

Ex. Com osition in 200 500 #

30 Primacor 3150/KOHIOnium#5.3 2.7 - -(20/0.6/0.2 31 Primaeor 3150/Na2BF6Salt/Onium#11.4 - - -20/1.0/0.2 32 Primacor 3150/Sodium 6.1 - - -Phenoxide/Onium#1 20/0.5/0.2 33 Primacor 3150/K2CO~/Onium#11.1 - - -20/1.0/0.2 34 Primacor 3460/KOH/Onium#18.0 0.2 - - -2011.0/0.2 35 Primacor 3460/KOH/Onium#11.4 0 - - -2010.5/0.2 36 Primacor 3340/Sodium 2.0 -Phenoxide/Onium# 1 20/1.0/0.2 37 Primacor 3340/Sodium 2.3 - -2,2,2-Trifluoroethoxide/Onium#1 (20/1.0/0.2) 38 Primacor 3340/KOH/Onium#12.2 0 - - -20/0.210.2) 39 _ 0.2 5.0 - - -EMAC-2220IKOH/Onium#1 20/0.2/0.2 40 EMAC-2220/KOH/Onium# - 6.3 - - -20/0.4/0.2 41 EMAC-2220/Sodium 8.1 8.7 - - -Phenoxide/Onium# 1 (break) 20/0.5/0.2 42 EVALINazBF6SaIdOnium#1 High High - - -(20/1.0/0.2 43 EVAL/KOH/Onium#1 17.0 - - - -(20/0.2/0.2 44 AT1841/KOH/Onium#2 4.7 2.9 - 4.1 3.6 23.5/1.010.9 45 AT1841/KOH/Onium#3 High 1.6 - - -(23.511.0/0.5 46 AT1841/KOH/Onium#4 >5.9 >5.9 - 7.1 6.1 (23.5/1.0/0.5 TahlP 1 Irnnt_l' T-Peel Data A dhesion ubstrate2.54 to S k cm Tie Layer CompositionTHVT"' THV~'"' PVDF LLDPE HDPE

Ex. Com position in 200 500 #

47 AT1841IKOH/Onium#4 0 1.6 - 5.5 5.9 20/0.2/0.2 48 Bynel-3101/KOHIOnittm#51.8 7.4 - - -20.010.2/0.2 49 Bynel-3101IPotassium- 4.8 0.5 - -t-Butoxide/Onium#2 (20.0/0.410.2 50 Bynel-3101/Potassium6.2 12.8 -t-ButoxidelKOH/Oruum#2 20.0/0.4/0.210.2) 51 ELVAX450/PItIMACOR .5 2.3 - - -3340/KOH/Onium# 1 ( 10/10/0.4/0.2) 52 ELVAX450 0.5 4.9 - -/EMAC2220T/KOHIOnium#

(10/10/0.2/0.2 53 Primacor-3150/Morthane1.7 10.4 - - -L424IKOH/Onium#1 (15.0/5.0/0.2/0.2 54 Primacor 3150/EMAC 5.5 - - - -KOHIOnium#I

10.0/10.0/0.4/0.2) C-1 ElvaxTM 250 0 0 - - -C-2 AT1841/Onium#1 0 0 - - -(23.5/0.5) 23.5/1.0 C-5 EVAL 105 1.6 0.2 - - -1. Substrate faihue, no adhesive failure observed.
2. Laminated at 230 °C.
3. Laminated at 180 °C.

Example 55 A tie layer composition was prepared using a twin screw extruder instead of a Brabender batch mixer as shown in the above examples. A Haake conical intermeshing counter rotating twin screw extruder was used. The temperature profile for each zone was: zone 1 - 25 °C; zone 2 - 170 °C; zone 3 - 200 °C; zone 4 - 200 °C. BynelT"' 3101 containing 1.5 wt % KOH was fed into a hopper and a 2.5 mm diameter strand was extruded into an ice water bath at 70 rpm and was pelletized and dries overnight at approximately 65 °C. Tetrabutyl phosphonium bromide ( 1 wt %) was added to the pellets and the mixture was again extruded and pelletized under the same conditions. The tie layer composition was evaluated in laminate constructions as described in Example 1, giving peel adhesion values of 3.9 kg/ 2.54 cm far THV 200 and 12.6 kg12.54 cm for THV 500.
Various modifications and alterations of this invention will be apparent to 1 S those skilled in the art without departing from the scope and spirit of this invention, and it should be understood that this invention is not limited to the illustrative embodiments set forth herein.

Claims (14)

We Claim:
1. A method of bonding fluoropolymer to substantially non-fluorinated polymeric material, the method comprising the steps of:
(a) blending carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefin with base and organo-onium compound that is stable in the presence of the base under processing conditions to form substantially non-fluorinated polymeric material where the base is selected from the group consisting of:
(1) those bases represented by the formulas:
X+ (OH)-n X+ (OR)-n X+ (OCY2R f)-n X+ (ORO)- X+
X+ -(OCY2R f CY2O)- X+
X+ -(OSi(R)3)-n X+ (SC(O)R)-n where:
n is 1 or 2;
X is a monovalent or divalent alkali or alkaline earth ion;

R is a substituted or unsubstituted alkyl, aryl, allyl, aralkyl or arallyl group that may contain one or more catenary or noncatenary heteroatoms such as nitrogen, sulfur and oxygen, and that may contain linear or branched and cyclic or acyclic segments; R preferably contains no more than about six carbon atoms;
R f is a partially or fully fluorinated, substituted or unsubstituted alkyl, aryl, allyl, aralkyl or arallyl group that also may contain one or more catenary or noncatenary heteroatoms such as nitrogen, sulfur and oxygen, and that may also contain linear or branched and cyclic or acyclic segments;
like the above-defined R group, R f preferably contains no more than about six carbon atoms; and each Y is independently a hydrogen atom or is an R or R f group with the proviso that both Y groups are not R f.
(2) sodium salt of 4,4'-hexafluoroisopropylidenyl bisphenol, carbonate salts, and sodium sulfide;
(b) providing fluoropolymer;
(c) forming a multi-layer article comprising a substantially non-fluorinated layer made of the substantially non-fluorinated polymeric material in contact with a fluorinated layer made of the fluoropolymer and exposing the multi-layer article to temperature and pressure conditions sufficient to bond the layers.
2. The method of claim 1 further comprising the step of applying at least one additional layer to at least one side of the resulting mufti-layer composition.
3. A multi-layer article comprising:
(a) a first layer comprising fluoropolymer; and (b) a second layer comprising substantially non-fluorinated polymeric material comprising carboxyl, anhydride, imide, or acid functional polyolefin, base, and organo-onium compound that is stable in the presence of the base, wherein said base is selected from the group consisting of:
(1) those bases represented by the formulas:
X+ (OH)-n X+ (OR)-n X+ (OCY2R f)-n X+ -(ORO)- X+
X+ -(OCY2R f CY2O)- X+
X+ (OSi(R)3)-n X+ (SC(O)R)-n where:
n is 1 or 2;
X is a monovalent or divalent alkali or alkaline earth ion;
R is a substituted or unsubstituted alkyl, aryl, allyl, aralkyl or arallyl group that may contain one or more catenary or noncatenary heteroatoms such as nitrogen, sulfur and oxygen, and that may contain linear or branched and cyclic or acyclic segments; R preferably contains no more than about six carbon atoms;
R f is a partially or fully fluorinated, substituted or unsubstituted alkyl, aryl, allyl, aralkyl or arallyl group that also may contain one or more catenary or noncatenary heteroatoms such as nitrogen, sulfur and oxygen, and that may also contain linear or branched and cyclic or acyclic segments;
like the above-defined R group, R f preferably contains no more than about six carbon atoms; and each Y is independently a hydrogen atom or is an R or R f group with the proviso that both Y groups are not R f.
(2) sodium salt of 4,4'-hexafluoroisopropylidenyl bisphenol, ammonium carbonate, and sodium sulfide;
and wherein said first and said second layers are bonded to one another.
4. The article of claim 3 further comprising at least one additional layer on at least one side of said article.
5. The article of claim 3 or 4 further comprising adhesive material disposed on at least one outer surface of the article.
6. The article of claim 3, 4 or 5 wherein said article is a tape product, drag reduction film, paint replacement film, hose, container, or comprises a retroreflective base sheet.
7. The method or article according to any of the preceding claims wherein said organo-onium compound is a phosphonium or ammonium compound.
8. The method or article according to any of the preceding claims wherein said base is selected from the group consisting of sodium hydroxide, potassium hydroxide, sodium methoxide, cesium hydroxide, potassium thioacetate, sodium trimethylsilanolate, sodium phenoxide, sodium para-chlorophenoxide, sodium 2,2,2-trifluoroethoxide, potassium tent-butoxide.
9. The method or article according to any of the preceding claims wherein said substantially non-fluorinated polymeric material further comprises one or more additional non-fluorinated polymers miscible with the substantially non-fluorinated polymeric material.
10. The method or article according to any of the preceding claims wherein said fluoropolymer is a homopolymer of vinylidene fluoride; a copolymer or terpolymer derived vinylidene fluoride and one or more monomers selected from the group consisting of tetrafluoroethylene, and hexafluoropropylene; or comprises interpolymerized units derived from monomers comprising one or more hexafluoropropylene, tetrafluoroethylene, and chlorotrifluoroethylene monomer and one or more non-fluorinated olefinically-unsaturated monomer.
11. The method or article according to any of the preceding claims wherein said fluoropolymer is blended with at least one additional polymer comprising polymethylmethacrylate.
12. The method or article according to any of the preceding claims wherein said substantially non-fluorinated polymeric material comprises a blend of two or more carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefins or comprises a blend of polyolefin and carboxyl, carboxylate, anhydride, amide, imide, hydroxyl, or oxycarbonyl functional polyolefin.
13. A bonding composition comprising substantially non-fluorinated polymeric material comprising a blend of carboxyl, anhydride, imide, or oxycarboxy functional polyolefin with a suitable organic or inorganic base and an organo-onium compound that is stable in the presence of the base.
14. A multi-layer article comprising:
(a) a first layer comprising substantially non-fluorinated polymeric material comprising carboxyl, anhydride, imide, or acid functional polyolefin, base, and organo-onium compound that is stable in the presence of the base, wherein said base is selected from the group consisting of:
(1) those bases represented by the formulas:

X+ (OH)-n X+ (OR)-n X+ (OCY2R f)-n X+ -(ORO)- X+
X+ -(OCY2R f CY2PO)- X+
X+ (OSi(R)3)-n X+ (SC(O)R)-n where:
n is 1 or 2;
X is a monovalent or divalent alkali or alkaline earth ion, preferably potassium or sodium;
R is a substituted or unsubstituted alkyl, aryl, allyl, aralkyl or arallyl group that may contain one or more catenary or noncatenary heteroatoms such as nitrogen, sulfur and oxygen, and that may contain linear or branched and cyclic or acyclic segments; R preferably contains no more than about six carbon atoms;
R f is a partially or fully fluorinated, substituted or unsubstituted alkyl, aryl, allyl, aralkyl or arallyl group that also may contain one or more catenary or noncatenary heteroatoms such as nitrogen, sulfur and oxygen, and that may also contain linear or branched and cyclic or acyclic segments;
like the above-defined R group, R f preferably contains no more than about six carbon atoms; and each Y is independently a hydrogen atom or is an R or R f group as above-defined.
(2) sodium salt of 4,4'-hexafluoroisopropylidenyl bisphenol, ammonium carbonate, and sodium sulfide; and (b) a second layer comprising a dissimilar polymeric material wherein said first and said second layers are bonded to one another.\
CA002325714A 1998-04-09 1998-08-25 Multi-layer compositions comprising a fluoropolymer Abandoned CA2325714A1 (en)