CA2261769A1 - Catio3 interfacial template structure on superconductor - Google Patents

Catio3 interfacial template structure on superconductor

Info

Publication number
CA2261769A1
CA2261769A1 CA002261769A CA2261769A CA2261769A1 CA 2261769 A1 CA2261769 A1 CA 2261769A1 CA 002261769 A CA002261769 A CA 002261769A CA 2261769 A CA2261769 A CA 2261769A CA 2261769 A1 CA2261769 A1 CA 2261769A1
Authority
CA
Canada
Prior art keywords
perovskite
film
material surface
semiconductor
template
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CA002261769A
Other languages
French (fr)
Other versions
CA2261769C (en
Inventor
Rodney Allen Mckee
Frederick Joseph Walker
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Tennessee Research Foundation
Lockheed Martin Energy Research Corp
Original Assignee
Lockheed Martin Energy Research Corporation
Rodney Allen Mckee
Frederick Joseph Walker
The University Of Tennessee Research Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lockheed Martin Energy Research Corporation, Rodney Allen Mckee, Frederick Joseph Walker, The University Of Tennessee Research Corporation filed Critical Lockheed Martin Energy Research Corporation
Publication of CA2261769A1 publication Critical patent/CA2261769A1/en
Application granted granted Critical
Publication of CA2261769C publication Critical patent/CA2261769C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

A structure including a film of a desired perovskite which overlies and is fully commensurate with the material surface of a semiconductor-based substrate and an associated process for constructing the structure involves the build up of an interfacial template film of perovskite between the material surface and the desired perovskite film. The orientation of the perovskite of the template is rotated 45° with the respect to the orientation of the underlying material surface and thereby effects a transition in the lattice structure from the foc (of the semiconductor-based material) to the simple cubic lattice structure of perovskite while the fully commensurate periodicity between the perovskite template film and the underlying material surface is maintained. The film-growth techniques of the invention can be used to fabricate solid state electrical components wherein a perovskite film (84) is built up upon a semiconductor based material (72) and the perovskite film is adapted to exhibit ferroelectric, piezoelectric, pyroelectric, electro-optic or large dielectric properties during use of the component. This process can be used to form FFETs with semiconducting substrate (72), a transistor (70), a source and drain (78, 80), gate electrode (82) and a gate dielectric (83). The perovskite (84) is part of the gate electrode.
CA002261769A 1996-08-05 1997-07-31 Catio3 interfacial template structure on superconductor Expired - Fee Related CA2261769C (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US692,343 1996-08-05
US08/692,343 US5830270A (en) 1996-08-05 1996-08-05 CaTiO3 Interfacial template structure on semiconductor-based material and the growth of electroceramic thin-films in the perovskite class
PCT/US1997/013527 WO1998005807A1 (en) 1996-08-05 1997-07-31 CaTiO3 INTERFACIAL TEMPLATE STRUCTURE ON SUPERCONDUCTOR

Publications (2)

Publication Number Publication Date
CA2261769A1 true CA2261769A1 (en) 1998-02-12
CA2261769C CA2261769C (en) 2005-09-06

Family

ID=24780189

Family Applications (1)

Application Number Title Priority Date Filing Date
CA002261769A Expired - Fee Related CA2261769C (en) 1996-08-05 1997-07-31 Catio3 interfacial template structure on superconductor

Country Status (7)

Country Link
US (1) US5830270A (en)
EP (1) EP0950132A4 (en)
JP (1) JP2000517280A (en)
KR (1) KR100493881B1 (en)
AU (1) AU3903497A (en)
CA (1) CA2261769C (en)
WO (1) WO1998005807A1 (en)

Families Citing this family (92)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5993541A (en) * 1996-07-31 1999-11-30 Geo Centers Inc Process for nucleation of ceramics and product thereof
US6093242A (en) * 1996-08-05 2000-07-25 Ut-Battelle, Llc Anisotropy-based crystalline oxide-on-semiconductor material
US6080235A (en) * 1997-06-03 2000-06-27 Ut-Battelle, Llc Geometric shape control of thin film ferroelectrics and resulting structures
FR2753567B1 (en) * 1996-09-19 1998-11-13 Alsthom Cge Alcatel METHOD FOR DEPOSITING A FERROMAGNETIC FILM ON A WAVEGUIDE, AND A MAGNETO-OPTICAL COMPONENT COMPRISING A THIN FERROMAGNETIC FILM DEPOSITED ACCORDING TO THE METHOD
US6069368A (en) * 1997-12-15 2000-05-30 Texas Instruments Incorporated Method for growing high-quality crystalline Si quantum wells for RTD structures
US6262462B1 (en) * 1998-06-22 2001-07-17 Motorola, Inc. Enhanced dielectric constant gate insulator
WO2000006812A1 (en) * 1998-07-30 2000-02-10 Ut-Battelle, Llc Control of crystal anisotropy for perovskite oxides on semiconductor-based substrates
US6103008A (en) * 1998-07-30 2000-08-15 Ut-Battelle, Llc Silicon-integrated thin-film structure for electro-optic applications
US6248459B1 (en) 1999-03-22 2001-06-19 Motorola, Inc. Semiconductor structure having a crystalline alkaline earth metal oxide interface with silicon
US6241821B1 (en) 1999-03-22 2001-06-05 Motorola, Inc. Method for fabricating a semiconductor structure having a crystalline alkaline earth metal oxide interface with silicon
US6652989B2 (en) 1999-04-06 2003-11-25 Ut-Battelle, Llc Structure and method for controlling band offset and alignment at a crystalline oxide-on-semiconductor interface
US6143072A (en) * 1999-04-06 2000-11-07 Ut-Battelle, Llc Generic process for preparing a crystalline oxide upon a group IV semiconductor substrate
US6605151B1 (en) 1999-11-29 2003-08-12 Northwestern University Oxide thin films and composites and related methods of deposition
US6479173B1 (en) 1999-12-17 2002-11-12 Motorola, Inc. Semiconductor structure having a crystalline alkaline earth metal silicon nitride/oxide interface with silicon
US6291319B1 (en) 1999-12-17 2001-09-18 Motorola, Inc. Method for fabricating a semiconductor structure having a stable crystalline interface with silicon
US6392257B1 (en) 2000-02-10 2002-05-21 Motorola Inc. Semiconductor structure, semiconductor device, communicating device, integrated circuit, and process for fabricating the same
US6693033B2 (en) 2000-02-10 2004-02-17 Motorola, Inc. Method of removing an amorphous oxide from a monocrystalline surface
US6680126B1 (en) * 2000-04-27 2004-01-20 Applied Thin Films, Inc. Highly anisotropic ceramic thermal barrier coating materials and related composites
US6620723B1 (en) 2000-06-27 2003-09-16 Applied Materials, Inc. Formation of boride barrier layers using chemisorption techniques
WO2002001648A1 (en) * 2000-06-28 2002-01-03 Motorola, Inc. Semiconductor structure, device, circuit, and process
US7101795B1 (en) 2000-06-28 2006-09-05 Applied Materials, Inc. Method and apparatus for depositing refractory metal layers employing sequential deposition techniques to form a nucleation layer
US6551929B1 (en) 2000-06-28 2003-04-22 Applied Materials, Inc. Bifurcated deposition process for depositing refractory metal layers employing atomic layer deposition and chemical vapor deposition techniques
US7964505B2 (en) 2005-01-19 2011-06-21 Applied Materials, Inc. Atomic layer deposition of tungsten materials
US7732327B2 (en) 2000-06-28 2010-06-08 Applied Materials, Inc. Vapor deposition of tungsten materials
US7405158B2 (en) 2000-06-28 2008-07-29 Applied Materials, Inc. Methods for depositing tungsten layers employing atomic layer deposition techniques
US6501973B1 (en) 2000-06-30 2002-12-31 Motorola, Inc. Apparatus and method for measuring selected physical condition of an animate subject
US6427066B1 (en) 2000-06-30 2002-07-30 Motorola, Inc. Apparatus and method for effecting communications among a plurality of remote stations
US6477285B1 (en) 2000-06-30 2002-11-05 Motorola, Inc. Integrated circuits with optical signal propagation
US6410941B1 (en) 2000-06-30 2002-06-25 Motorola, Inc. Reconfigurable systems using hybrid integrated circuits with optical ports
JP2004505444A (en) * 2000-07-24 2004-02-19 モトローラ・インコーポレイテッド Thin film metal oxide structure and method of manufacturing the same
US6555946B1 (en) 2000-07-24 2003-04-29 Motorola, Inc. Acoustic wave device and process for forming the same
KR100370504B1 (en) * 2000-08-03 2003-01-30 한국화학연구원 Epitaxial growth of a high quality magnesium oxide film using a cubic silicon carbide buffer layer on a silicon (100) substrate
US6518609B1 (en) * 2000-08-31 2003-02-11 University Of Maryland Niobium or vanadium substituted strontium titanate barrier intermediate a silicon underlayer and a functional metal oxide film
US6224669B1 (en) 2000-09-14 2001-05-01 Motorola, Inc. Method for fabricating a semiconductor structure having a crystalline alkaline earth metal oxide interface with silicon
US6638838B1 (en) * 2000-10-02 2003-10-28 Motorola, Inc. Semiconductor structure including a partially annealed layer and method of forming the same
US6501121B1 (en) 2000-11-15 2002-12-31 Motorola, Inc. Semiconductor structure
AU2002228719A1 (en) * 2000-11-16 2002-05-27 Motorola, Inc. Single crystalline oxide on a semiconductor substrate
US20030001207A1 (en) * 2000-11-22 2003-01-02 Motorola, Inc. Structure and method for fabricating semiconductor structures and devices utilizing the formation of a compliant subtrate for materials used to form the same
US6583034B2 (en) 2000-11-22 2003-06-24 Motorola, Inc. Semiconductor structure including a compliant substrate having a graded monocrystalline layer and methods for fabricating the structure and semiconductor devices including the structure
US6563118B2 (en) 2000-12-08 2003-05-13 Motorola, Inc. Pyroelectric device on a monocrystalline semiconductor substrate and process for fabricating same
US6765178B2 (en) 2000-12-29 2004-07-20 Applied Materials, Inc. Chamber for uniform substrate heating
US6825447B2 (en) 2000-12-29 2004-11-30 Applied Materials, Inc. Apparatus and method for uniform substrate heating and contaminate collection
US6951804B2 (en) 2001-02-02 2005-10-04 Applied Materials, Inc. Formation of a tantalum-nitride layer
US6673646B2 (en) 2001-02-28 2004-01-06 Motorola, Inc. Growth of compound semiconductor structures on patterned oxide films and process for fabricating same
US6660126B2 (en) 2001-03-02 2003-12-09 Applied Materials, Inc. Lid assembly for a processing system to facilitate sequential deposition techniques
US6878206B2 (en) 2001-07-16 2005-04-12 Applied Materials, Inc. Lid assembly for a processing system to facilitate sequential deposition techniques
US6734020B2 (en) 2001-03-07 2004-05-11 Applied Materials, Inc. Valve control system for atomic layer deposition chamber
US7046719B2 (en) 2001-03-08 2006-05-16 Motorola, Inc. Soft handoff between cellular systems employing different encoding rates
US20020140013A1 (en) * 2001-04-02 2002-10-03 Motorola, Inc. Structure and method for fabricating semiconductor structures and devices utilizing a stable template
US20020153524A1 (en) * 2001-04-19 2002-10-24 Motorola Inc. Structure and method for fabricating semiconductor structures and devices utilizing perovskite stacks
US20020158245A1 (en) * 2001-04-26 2002-10-31 Motorola, Inc. Structure and method for fabricating semiconductor structures and devices utilizing binary metal oxide layers
US20020167005A1 (en) * 2001-05-11 2002-11-14 Motorola, Inc Semiconductor structure including low-leakage, high crystalline dielectric materials and methods of forming same
US20020195057A1 (en) * 2001-06-21 2002-12-26 Motorola, Inc. Apparatus for fabricating semiconductor structures and method of forming the same
US6709989B2 (en) 2001-06-21 2004-03-23 Motorola, Inc. Method for fabricating a semiconductor structure including a metal oxide interface with silicon
US6933566B2 (en) * 2001-07-05 2005-08-23 International Business Machines Corporation Method of forming lattice-matched structure on silicon and structure formed thereby
US6852575B2 (en) * 2001-07-05 2005-02-08 International Business Machines Corporation Method of forming lattice-matched structure on silicon and structure formed thereby
US6992321B2 (en) * 2001-07-13 2006-01-31 Motorola, Inc. Structure and method for fabricating semiconductor structures and devices utilizing piezoelectric materials
US7211144B2 (en) 2001-07-13 2007-05-01 Applied Materials, Inc. Pulsed nucleation deposition of tungsten layers
US6646293B2 (en) 2001-07-18 2003-11-11 Motorola, Inc. Structure for fabricating high electron mobility transistors utilizing the formation of complaint substrates
US6693298B2 (en) 2001-07-20 2004-02-17 Motorola, Inc. Structure and method for fabricating epitaxial semiconductor on insulator (SOI) structures and devices utilizing the formation of a compliant substrate for materials used to form same
US6498358B1 (en) 2001-07-20 2002-12-24 Motorola, Inc. Structure and method for fabricating an electro-optic system having an electrochromic diffraction grating
US6472694B1 (en) 2001-07-23 2002-10-29 Motorola, Inc. Microprocessor structure having a compound semiconductor layer
US6585424B2 (en) 2001-07-25 2003-07-01 Motorola, Inc. Structure and method for fabricating an electro-rheological lens
US6667196B2 (en) 2001-07-25 2003-12-23 Motorola, Inc. Method for real-time monitoring and controlling perovskite oxide film growth and semiconductor structure formed using the method
US6594414B2 (en) 2001-07-25 2003-07-15 Motorola, Inc. Structure and method of fabrication for an optical switch
US6462360B1 (en) 2001-08-06 2002-10-08 Motorola, Inc. Integrated gallium arsenide communications systems
US6639249B2 (en) 2001-08-06 2003-10-28 Motorola, Inc. Structure and method for fabrication for a solid-state lighting device
US6589856B2 (en) 2001-08-06 2003-07-08 Motorola, Inc. Method and apparatus for controlling anti-phase domains in semiconductor structures and devices
US6673667B2 (en) 2001-08-15 2004-01-06 Motorola, Inc. Method for manufacturing a substantially integral monolithic apparatus including a plurality of semiconductor materials
US6916398B2 (en) 2001-10-26 2005-07-12 Applied Materials, Inc. Gas delivery apparatus and method for atomic layer deposition
WO2003038878A2 (en) * 2001-10-26 2003-05-08 Motorola Inc. Method for fabricating semiconductor structures
US6729824B2 (en) 2001-12-14 2004-05-04 Applied Materials, Inc. Dual robot processing system
US6620670B2 (en) 2002-01-18 2003-09-16 Applied Materials, Inc. Process conditions and precursors for atomic layer deposition (ALD) of AL2O3
US6911391B2 (en) 2002-01-26 2005-06-28 Applied Materials, Inc. Integration of titanium and titanium nitride layers
US6998014B2 (en) 2002-01-26 2006-02-14 Applied Materials, Inc. Apparatus and method for plasma assisted deposition
US6827978B2 (en) 2002-02-11 2004-12-07 Applied Materials, Inc. Deposition of tungsten films
US6833161B2 (en) 2002-02-26 2004-12-21 Applied Materials, Inc. Cyclical deposition of tungsten nitride for metal oxide gate electrode
US6720027B2 (en) 2002-04-08 2004-04-13 Applied Materials, Inc. Cyclical deposition of a variable content titanium silicon nitride layer
US6869838B2 (en) 2002-04-09 2005-03-22 Applied Materials, Inc. Deposition of passivation layers for active matrix liquid crystal display (AMLCD) applications
US6875271B2 (en) 2002-04-09 2005-04-05 Applied Materials, Inc. Simultaneous cyclical deposition in different processing regions
US7279432B2 (en) 2002-04-16 2007-10-09 Applied Materials, Inc. System and method for forming an integrated barrier layer
US6821563B2 (en) 2002-10-02 2004-11-23 Applied Materials, Inc. Gas distribution system for cyclical layer deposition
US7005302B2 (en) * 2004-04-07 2006-02-28 Advanced Micro Devices, Inc. Semiconductor on insulator substrate and devices formed therefrom
US20060288928A1 (en) * 2005-06-10 2006-12-28 Chang-Beom Eom Perovskite-based thin film structures on miscut semiconductor substrates
US7364989B2 (en) * 2005-07-01 2008-04-29 Sharp Laboratories Of America, Inc. Strain control of epitaxial oxide films using virtual substrates
US7718516B2 (en) * 2006-03-23 2010-05-18 The University Of Hong Kong Method for epitaxial growth of (110)-oriented SrTiO3 thin films on silicon without template
US7892964B2 (en) * 2007-02-14 2011-02-22 Micron Technology, Inc. Vapor deposition methods for forming a metal-containing layer on a substrate
CN101651150B (en) * 2008-08-12 2012-04-18 中国科学院物理研究所 Full oxide heterostructure field effect transistor
US8389300B2 (en) 2010-04-02 2013-03-05 Centre National De La Recherche Scientifique Controlling ferroelectricity in dielectric films by process induced uniaxial strain
US8778767B2 (en) * 2010-11-18 2014-07-15 Taiwan Semiconductor Manufacturing Company, Ltd. Integrated circuits and fabrication methods thereof
DE102015108865A1 (en) * 2015-06-03 2016-12-08 Universität Rostock Moldings containing piezoactive calcium titanium oxide, a process for their preparation and excitation and use of piezoactive calcium titanium oxide as a piezoelectric molded body or component of piezoelectric molded bodies
US20180151301A1 (en) * 2016-11-25 2018-05-31 The Boeing Company Epitaxial perovskite materials for optoelectronics

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1313335C (en) * 1987-08-24 1993-02-02 Keizo Harada Process for preparing a thin film of superconducting compound oxide
US5225031A (en) * 1991-04-10 1993-07-06 Martin Marietta Energy Systems, Inc. Process for depositing an oxide epitaxially onto a silicon substrate and structures prepared with the process
DE69117503T2 (en) * 1991-07-19 1996-09-19 Ibm Improved superconducting field effect transistor with inverse MISFET structure and method for its production
JP3026869B2 (en) * 1991-10-31 2000-03-27 ローム株式会社 Manufacturing method of semiconductor nonvolatile memory device
JP3130353B2 (en) * 1991-12-20 2001-01-31 ローム株式会社 Method of manufacturing device using ferroelectric film
JP3251625B2 (en) * 1992-02-24 2002-01-28 ローム株式会社 Field effect transistor
US5432015A (en) * 1992-05-08 1995-07-11 Westaim Technologies, Inc. Electroluminescent laminate with thick film dielectric
JPH06151872A (en) * 1992-11-09 1994-05-31 Mitsubishi Kasei Corp Fet device
US5323023A (en) * 1992-12-02 1994-06-21 Xerox Corporation Epitaxial magnesium oxide as a buffer layer on (111) tetrahedral semiconductors
FI92897C (en) * 1993-07-20 1995-01-10 Planar International Oy Ltd Process for producing a layer structure for electroluminescence components
US5330931A (en) * 1993-09-22 1994-07-19 Northern Telecom Limited Method of making a capacitor for an integrated circuit

Also Published As

Publication number Publication date
WO1998005807A1 (en) 1998-02-12
WO1998005807A8 (en) 2001-06-21
JP2000517280A (en) 2000-12-26
EP0950132A1 (en) 1999-10-20
KR20000029832A (en) 2000-05-25
EP0950132A4 (en) 2002-03-20
US5830270A (en) 1998-11-03
KR100493881B1 (en) 2005-06-10
AU3903497A (en) 1998-02-25
CA2261769C (en) 2005-09-06

Similar Documents

Publication Publication Date Title
CA2261769A1 (en) Catio3 interfacial template structure on superconductor
Robertson Band structures and band offsets of high K dielectrics on Si
US6812509B2 (en) Organic ferroelectric memory cells
EP1172858A4 (en) Semiconductor device
CA2151063A1 (en) C-Axis Perovskite Thin Films Grown on Silicon Dioxide
EP0342796A3 (en) Thin-film transistor
KR940006213A (en) High dielectric constant oxide structure containing Pb / Bi using perovskite containing no Pb / Bi as a buffer layer and a method of manufacturing the same
EP0597124A4 (en) Semiconductor nonvolatile storage device, semiconductor device, and its manufacture method.
TW329037B (en) Semiconductor memory device
KR970054168A (en) Semiconductor device and manufacturing method
EP1253627A3 (en) Semiconductordevice having a ferroelectric capacitor and fabrication process thereof
KR970013383A (en) Forming method of ferroelectric thin film and manufacturing method of capacitor structure of semiconductor device
EP1115156A4 (en) Ferroelectric memory device and method of manufacturing the same
WO2005043246A3 (en) Patterned ceramic films and method for producing the same
MY109375A (en) Superconducting field-effect transistors with inverted misfet structure and method for making the same.
CA2238857A1 (en) Ferroelectric material, method of manufacturing the same, semiconductor memory, and method of manufacturing the same
KR970077329A (en) Ferroelectric film and its formation method
US5686745A (en) Three-terminal non-volatile ferroelectric/superconductor thin film field effect transistor
CA2051778A1 (en) Method for manufacturing superconducting device having a reduced thickness of oxide superconducting layer and superconducting device manufactured thereby
KR890002908A (en) Superconducting Thin Film Manufacturing Method
Tani et al. Formation of c-axis-oriented Bi4Ti3O12 films with extremely flat surface by spin-coating
KR930011275A (en) Thin film transistor structure
Shiosaki et al. Growth and characterization of ferroelectric thin films by the photo-CVD process
Lee et al. Ferroelectric La-Sr-Co-O/Pb-La-Zr-Ti-O/La-Sr-Co-O heterostructures on silicon
KR970060505A (en) Semiconductor device and manufacturing method

Legal Events

Date Code Title Description
EEER Examination request
MKLA Lapsed